Improved cold rolling workability of warm rolled Fe-6.5wt%Si electrical steel with columnar grains by annealing

Improved cold rolling workability of warm rolled Fe-6.5wt%Si electrical steel with columnar... The effects of annealing temperature (with the annealing time being constant at 1 h) on the microstructure, ordering, residual stress, mechanical properties, and subsequent cold rolling workability of Fe-6.5wt%Si electrical steel with columnar grains were investigated, where the steel was warm rolled at 500°C with a reduction of 95%. The results show that recrystallization began to occur in the sample annealed at 575°C and that full recrystallization occurred in the sample annealed at 625°C. When the annealing temperature was 500°C or greater, the extent of reordering in the sample was high, which reduced the room-temperature plasticity. However, annealing at temperatures below 300°C did not significantly reduce the residual tensile stress on the edge of the warm rolled samples. Considering the comprehensive effects of annealing temperature on the recrystallization, reordering, residual stress, and mechanical properties of the warm rolled Fe-6.5wt%Si electrical steel with columnar grains, the appropriate annealing temperature range is 300°C-400°C. Unlike the serious edge cracks that appeared in the sample after direct cold rolling, the annealed samples could be cold rolled to a total reduction of more than 71.4% without the formation of obvious edge cracks, and bright-surface Fe-6.5wt%Si electrical steel strips with a thickness less than 0.1 mm could be fabricated by cold rolling. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png International Journal of Minerals, Metallurgy, and Materials Springer Journals

Improved cold rolling workability of warm rolled Fe-6.5wt%Si electrical steel with columnar grains by annealing

Loading next page...
 
/lp/springer-journals/improved-cold-rolling-workability-of-warm-rolled-fe-6-5wt-si-sG8qR7Myp4

References (25)

Publisher
Springer Journals
Copyright
Copyright © 2015 by University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg
Subject
Material Science; Materials Science, general; Metallic Materials; Characterization and Evaluation of Materials; Ceramics, Glass, Composites, Natural Methods; Surfaces and Interfaces, Thin Films; Tribology, Corrosion and Coatings
ISSN
1674-4799
eISSN
1869-103X
DOI
10.1007/s12613-015-1182-z
Publisher site
See Article on Publisher Site

Abstract

The effects of annealing temperature (with the annealing time being constant at 1 h) on the microstructure, ordering, residual stress, mechanical properties, and subsequent cold rolling workability of Fe-6.5wt%Si electrical steel with columnar grains were investigated, where the steel was warm rolled at 500°C with a reduction of 95%. The results show that recrystallization began to occur in the sample annealed at 575°C and that full recrystallization occurred in the sample annealed at 625°C. When the annealing temperature was 500°C or greater, the extent of reordering in the sample was high, which reduced the room-temperature plasticity. However, annealing at temperatures below 300°C did not significantly reduce the residual tensile stress on the edge of the warm rolled samples. Considering the comprehensive effects of annealing temperature on the recrystallization, reordering, residual stress, and mechanical properties of the warm rolled Fe-6.5wt%Si electrical steel with columnar grains, the appropriate annealing temperature range is 300°C-400°C. Unlike the serious edge cracks that appeared in the sample after direct cold rolling, the annealed samples could be cold rolled to a total reduction of more than 71.4% without the formation of obvious edge cracks, and bright-surface Fe-6.5wt%Si electrical steel strips with a thickness less than 0.1 mm could be fabricated by cold rolling.