Polymeric Materials--Long Term Property Evaluations, UL 746 B. 3d
G. Talamini, G. Pezzin (1960)
Kinetic study on the reaction of polyvinyl chloride thermal dehydrochlorinationMacromolecular Chemistry and Physics, 39
(1997)
Polgrn &grad-Stab
In the temperature range studied, an excellent correlation between weight loss and impact failure was observed
Eran Tuval, A. Thurm, Z. Rigbi (1997)
The shelf life of rubber compoundsPolymer Degradation and Stability, 58
I. Mcneill (1989)
15 – Thermal DegradationComprehensive Polymer Science and Supplements, 15
(1987)
Instrumented I b a c t Testing of Plastic and Composite Materials
P. Budrugeac (1995)
Thermal lifetime evaluation of polymeric materials exhibiting a compensation effect and dependence of activation energy on the degree of conversionPolymer Degradation and Stability, 50
J. Flynn (1988)
Thermal analysis kinetics-problems, pitfalls and how to deal with themJournal of thermal analysis, 34
J. Tamblyn, G. Newland (1965)
Induction period in the aging of polypropyleneJournal of Applied Polymer Science, 9
J. Flynn (1995)
A critique of lifetime prediction of polymers by thermal analysisJournal of thermal analysis, 44
J. Danforth, J. Spiegel, J. Bloom (1982)
The Kinetics and Mechanism of the Thermal Dehydrochlorination of Poly(vinyl Chloride)Journal of Macromolecular Science, Part A, 17
(1987)
Kessler et a&
P. Budrugeac (1997)
On the pseudo compensation effect due to the complexity of the mechanism of thermal degradation of polymeric materialsPolymer Degradation and Stability, 58
(1989)
in Comprehensive Polymer Science, 6
An instrumented drop weight impact test was used to study the effect of thermal degradation on the impact properties of PVC compounds. The impact resistance of the aged compounds related well with their weight loss and hence, with thermal degradation. Each compound showed a specific weight loss percentage that correlated with a 50% loss in its impact properties (failure point), irrespective of the aging temperature. The results were also used to estimate a thermal index (TI) of each compound in a rapid and reliable way.
Journal of Vinyl & Additive Technology – Wiley
Published: Dec 1, 1999
Read and print from thousands of top scholarly journals.
Already have an account? Log in
Bookmark this article. You can see your Bookmarks on your DeepDyve Library.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Copy and paste the desired citation format or use the link below to download a file formatted for EndNote
Access the full text.
Sign up today, get DeepDyve free for 14 days.
All DeepDyve websites use cookies to improve your online experience. They were placed on your computer when you launched this website. You can change your cookie settings through your browser.