Access the full text.
Sign up today, get DeepDyve free for 14 days.
Jie Liu, Yaqing Lin, Tianxing Lu, Chenqiang Du, Wen Wang, Shirong Wang, Zhiyuan Tang, D. Qu, Xin-he Zhang (2015)
Characterization and electrochemical properties of Li2MoO4 modified Li4Ti5O12/C anode material for lithium-ion batteriesElectrochimica Acta, 170
D. Mikhailova, A. Voß, S. Oswald, A. Tsirlin, M. Schmidt, A. Senyshyn, J. Eckert, H. Ehrenberg (2015)
Lithium Insertion into Li2MoO4: Reversible Formation of (Li3Mo)O4 with a Disordered Rock-Salt StructureChemistry of Materials, 27
Hao Zhang, Xiuyu Wang, Q. Cheng, Xiaoping Ma, Mingxiu Li, Ping Zhang, Yonggui Zhao (2016)
Preparation of Li2MoO4 using aqueous solution method and microwave dielectric properties after sinteringJournal of Materials Science: Materials in Electronics, 27
J. Ni, Henghui Zhou, Jitao Chen, Xinxiang Zhang (2008)
Improved electrochemical performance of layered LiNi0.4Co0.2Mn0.4O2 via Li2ZrO3 coatingElectrochimica Acta, 53
T. Sasaki, K. Kiuchi (1981)
Electronic structures and X-ray photoelectron spectra of MoO2 and Li2 MoO4Chemical Physics Letters, 84
S. Komaba, N. Kumagai, Rumiko Kumagai, N. Kumagai, H. Yashiro (2002)
Molybdenum oxides synthesized by hydrothermal treatment of A2MoO4 (A=Li, Na, K) and electrochemical lithium intercalation into the oxidesSolid State Ionics, 152
He-Yang Wang, Bangkun Zou, Zhongfeng Tang, Z. Wen, Chun-hua Chen (2016)
Enhancing cyclability and rate performance of Li2MoO4 by carbon coatingMaterials Letters, 177
A. Barinova, R. Rastsvetaeva, Y. Nekrasov, D. Pushcharovskii (2001)
Crystal Structure of Li2MoO4Doklady Chemistry, 376
Xudong Liu, Yanming Zhao, Youzhong Dong, Qinghua Fan, Q. Kuang, Zhiyong Liang, Xinghao Lin, W. Han, Qidong Li, M. Wen (2015)
Synthesis of One Dimensional Li2MoO4 Nanostructures and Their Electrochemical Performance as Anode Materials for Lithium-ion BatteriesElectrochimica Acta, 174
M. Reddy, M. Kishore, V. Pralong, V. Caignaert, U. Varadaraju, B. Raveau (2007)
Electrochemical performance of VOMoO4 as negative electrode material for Li ion batteriesJournal of Power Sources, 168
Li-na Wang, Zhiguo Zhang, Kun Zhang (2007)
A simple, cheap soft synthesis routine for LiFePO4 using iron(III) raw materialJournal of Power Sources, 167
G. Du, K. Seng, Zaiping Guo, Jun Liu, Wenxian Li, Dianzeng Jia, C. Cook, Zongwen Liu, Huakun Liu (2011)
Graphene–V2O5·nH2O xerogel composite cathodes for lithium ion batteriesRSC Advances, 1
(1981)
Electrochim. Acta 53:3075
In this paper, submicron Li2MoO4 material was synthesized via rheological phase method. The structure, composition and morphology of the obtained powders were characterized by X-ray diffraction (XRD), X-ray photoelectron spectrometer (XPS) and scanning electron microscope (SEM), respectively. The key calcination temperature was 700 oC. The particle sizes were about from 100 to 300 nm. As anode material of lithium ion batteries, lithium storage performances of the as-prepared Li2MoO4 were evaluated at different current densities. The best capacity retention was 75.7% of the initial capacity (592.13 mAh g-1) after 50 cycles at 0.2 mA cm-2 in 0.1-2.5 V, and the resistance was about 123.5 Ω, indicating a potential prospect in the application of lithium ions batteries.
Ionics – Springer Journals
Published: Apr 10, 2017