Dense nanostructured Ti was sintered from mechanically activated Ti and TiH2 powders by pulsed-current activated heating under a pressure of 80 Mpa. TiH2 powder was decomposed to Ti during sintering. The hardness of the Ti increased, and the average grain size of the Ti decreased, with increasing milling time.