A transparent and highly porous thin-film photocatalyst was prepared using the dipcoating method with the thermal decomposition of titanium alkoxide complex. The photocatalyst film obtained was formed with aggregated nano-sized TiO2 single anatase crystals, and this film had a large surface area. Film thickness was 0.2–4.4 μm. A thick film (about 4.4 μm thickness) was also transparent. The average specific surface area of the film was ca. 70 m2/g. The crystalline phase of TiO2 was anatase alone for calcinations over 400°C. The photocatalytic ability of the films was almost equal to the same weight of P25 on coated glass plates. The films decomposed 100 ppm of toluene and p-xylene (using a 1-1 size batch-type photo-reactor).
Research on Chemical Intermediates – Springer Journals
Published: Jul 8, 2009
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera