Preparation and characterization of ternary composite films of polyvinyl alcohol/sodium alginate/TiO2

Preparation and characterization of ternary composite films of polyvinyl alcohol/sodium... Nano-TiO2 with anionic surface active agent sodium dodecylsulfate (SDS) modified, the poly(vinyl alcohol)/sodium alginate/TiO2 composite films were prepared by method of solution blending representing. The structure of the films was analyzed by XRD and SEM. In addition, air permeability rate, swelling ratio, light transmittance, mechanical properties, and antibacterial properties were tested. The results showed that in compound membrane there was a strong force between poly(vinyl alcohol)/sodium alginate and TiO2 particles, indicating that there was good compatibility between the sodium alginate and the poly(vinyl alcohol). The mixed membranes were of good water resistance, tensile strength, and closure. When the titanium dioxide content increased appropriately, they had very good mechanical properties. In addition, the antibacterial properties of composite membrane gradually increased with the increase in the TiO2content. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Russian Journal of Applied Chemistry Springer Journals

Preparation and characterization of ternary composite films of polyvinyl alcohol/sodium alginate/TiO2

Loading next page...
1
 
/lp/springer_journal/preparation-and-characterization-of-ternary-composite-films-of-hxXeaTMpsY

References (14)

Publisher
Springer Journals
Copyright
Copyright © 2016 by Pleiades Publishing, Ltd.
Subject
Chemistry; Chemistry/Food Science, general; Industrial Chemistry/Chemical Engineering
ISSN
1070-4272
eISSN
1608-3296
DOI
10.1134/S10704272160020191
Publisher site
See Article on Publisher Site

Abstract

Nano-TiO2 with anionic surface active agent sodium dodecylsulfate (SDS) modified, the poly(vinyl alcohol)/sodium alginate/TiO2 composite films were prepared by method of solution blending representing. The structure of the films was analyzed by XRD and SEM. In addition, air permeability rate, swelling ratio, light transmittance, mechanical properties, and antibacterial properties were tested. The results showed that in compound membrane there was a strong force between poly(vinyl alcohol)/sodium alginate and TiO2 particles, indicating that there was good compatibility between the sodium alginate and the poly(vinyl alcohol). The mixed membranes were of good water resistance, tensile strength, and closure. When the titanium dioxide content increased appropriately, they had very good mechanical properties. In addition, the antibacterial properties of composite membrane gradually increased with the increase in the TiO2content.

Journal

Russian Journal of Applied ChemistrySpringer Journals

Published: May 22, 2016

There are no references for this article.