Bauxite-based high-density ceramic binding suspensions (HDBS) are promising materials for producing high-quality refractories. Static unilateral pressing at 200 MPa of a system composed of electrocorundum (filler) and a bauxite HDBS led to greens with a porosity of 16–17% and subsequent low-temperature firing yielded refractories with a compressive strength of about 140 MPa. The phenomenon of filler grain break-up in the course of pressing was studied. This process markedly modifies the initial grain size and weight distribution.
Refractories and Industrial Ceramics – Springer Journals
Published: Nov 26, 2007
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera