Strength properties are considered for ZrO2 hot-pressed ceramic materials stabilized with 4 – 6 wt.% Y2O3 in relation to original powder preparation method: solid phase synthesis, high-temperature salt thermolysis, combined hydroxide precipitation followed by freezing, drying and calcining, and the sol-gel method. Ceramic material with the highest strength in bending (up to 1350 MPa) are prepared from ZrO2 – 5 wt.% Y2O3 powders, synthesized by coprecipitation of hydroxides followed by freezing.
Refractories and Industrial Ceramics – Springer Journals
Published: Dec 1, 2010
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
All the latest content is available, no embargo periods.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud