Dependence of the density of the Li1.3Al0.3Ti1.7(PO4)3 (LATP) ceramic on thermal treatment modes was studied. The conditions in which ceramic samples with density exceeding 90% are obtained were determined. It was found that the bulk ionic conductivity of LATP upon sintering at 1000°C for 2–6 h is (1.1–1.3) × 10–3 S cm–1 at 20°C, which corresponds to the maximum values for lithium-aluminum titanophosphate.
Russian Journal of Applied Chemistry – Springer Journals
Published: Jun 30, 2017