The effect of the initial kind of A12O3 powder on the properties of corundum ceramics with a diminished sintering temperature is investigated. It is shown that A12O3 fabricated by calcinating industrial powder of aluminum hydroxide has the best prospects. This material with an addition of partially stabilized ZrO2 has been used for fabricating a ceramics with an ultimate strength in three point bending equal to 500±40 MPa and a density of 4.19 g/cm3. Additives containing MnO are shown to provide strong ceramics with a diminished sintering temperature.
Refractories and Industrial Ceramics – Springer Journals
Published: Nov 23, 2007
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera