The effect of quasi-hydrostatic compression on the strength of ZrO2 + 3 mol.% Y2O3 ceramic specimens of two series was studied. The series 1 ceramic was a powder commercially available from TOSOH Co. (Japan), with a density of 6.1 g/cm3, and the series 2 ceramic was a powder with a density of 5.9 g/cm3 prepared under laboratory conditions at the IPM Research Institute (National Academy of Sciences, Ukraine). The pressure range was up to 1.2 GPa, and the pressure-transmitting medium was a coarse-grained corundum powder. In the series 1 specimens, the strength increases with pressure over the entire pressure range (from 670 MPa to 1098 MPa at 1.2 GPa); in the series 2 specimens, the strength increases only to a pressure of 0.8 GPa (from 695 MPa to 828 MPa) and then, with further increase in pressure drops sharply to nearly zero (30 MPa at 1.2 GPa). It was proposed that the observed effect might be associated with a martensite transformation in the zone of structural imperfections (discontinuities). On reaching a critical value determined by the strength of the matrix, the martensite transformation becomes a cause of failure of the material.
Refractories and Industrial Ceramics – Springer Journals
Published: Oct 13, 2004
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera