T. Zhang, X. Jiang, S. Li, X. Lu (1994)
A QUANTITATIVE ESTIMATION OF THE SYNERGY BETWEEN CORROSION AND ABRASIONCorrosion Science, 36
(1995)
G
V. Buchanan, D. McCartney, P. Shipway (2008)
A comparison of the abrasive wear behaviour of iron-chromium based hardfaced coatings deposited by SMAW and electric arc sprayingWear, 264
(1982)
Hardness [versus] Wear Resistance, Surf
T. Matsuo, C. Kiminami, W. Fo, C. Bolfarini (2005)
Sliding wear of spray-formed high-chromium white cast iron alloysWear, 259
(1996)
New Developments in Hardfacing Alloys, Weld
Ö. Doğan, G. Laird, J. Hawk (1995)
Abrasion resistance of the columnar zone in high Cr white cast ironsWear
S. Chatterjee, T. Pal (2003)
Wear behaviour of hardfacing deposits on cast ironWear, 255
B. Wang, M. Seitz (2001)
Comparison in erosion behavior of iron-base coatings sprayed by three different arc-spray processesWear, 250
(1994)
of the Synergy Between Corrosion and Abrasion, Corros
K. Katô (1992)
Micro-mechanisms of wear — wear modesWear, 153
(2005)
and C
L. Svensson, B. Gretoft, B. Ulander, H. Bhadeshia (1986)
Fe-Cr-C hardfacing alloys for high-temperature applicationsJournal of Materials Science, 21
K. Gahr, G. Eldis (1980)
Abrasive wear of white cast ironsWear, 64
T. Devine, B. Drummond (1981)
Use of Accelerated Intergranular Corrosion Tests and Pitting Corrosion Tests to Detect Sensitization and Susceptibility to Intergranular Stress Corrosion Cracking in High Temperature Water of Duplex 308 Stainless SteelCorrosion, 37
(1981)
The Cumulative Benefits of Surface Treatment of Rolls, Sugar Azucar
(1999)
Rollers and Abrasion Resistant Surface Coatings for Mill Rollers
M. Guo, C. Chiang, C. Tsao (2002)
Microstructure and wear behavior of spray-formed and conventionally cast rolls of 18Cr–2.5Mo–Fe alloyMaterials Science and Engineering A-structural Materials Properties Microstructure and Processing, 326
G. Reinhard, M. Radtke, U. Rammelt (1992)
On the role of the salts of weak acids in the chemical passivation of iron and steel in aqueous solutionsCorrosion Science, 33
N Maier (1981)
The Cumulative Benefits of Surface Treatment of RollsSugar Azucar, 76
(1992)
Fe - CrC Hardfacing Alloys for High - Temperature Applications
E. Rabinowicz, Free Download (1966)
Friction and Wear of Materials
(1979)
Development of New Flux-Cored Electrodes for Arcing of Sugar Mill Roller Shells, Proc
CP Cookson (1982)
Hardness [versus] Wear ResistanceSurf. J., 13
K. Kato (1997)
Abrasive wear of metalsTribology International, 30
(1985)
Quantitative Metallography, Metals Handbook, 9th ed., Vol 9, Metallography and Structures, American Society for Metals
(1991)
New Alternatives for the Reclamation and Coating of Mill Rolls
(1976)
Surfacing II: Weld Overlays That Resist Corrosion,Weld
F. Ferrer, H. Idrissi, H. Mazille, P. Fleischmann, P. Labeeuw (2000)
A study of abrasion–corrosion of AISI 304L austenitic stainless steel in saline solution using acoustic emission techniqueNdt & E International, 33
(2000)
and P
K. Gahr (1998)
Wear by hard particlesTribology International, 31
R. Menon (1996)
New developments in hardfacing alloysWelding Journal, 75
M. Pourbaix (1974)
Atlas of Electrochemical Equilibria in Aqueous Solutions
Abrasion-corrosion tests were conducted on two commonly Fe-Cr-C shielded metal arc welding (SMAW) hardfacings used in the sugar industry and an arc sprayed Fe-Cr-based coating. The tests were performed on a modified block-on-ring tester with the coatings sliding against compressed sugarcane fiber in the presence of abrasive slurry. The findings showed that, in the presence of sugarcane juice and sand slurry, the SMAW coatings had similar wear performance while the abrasive wear of the arc-sprayed coating was superior to the SMAW coatings. In the presence of a neutral solution, the material loss from the arc-sprayed coating was similar to that obtained in the sugarcane juice while the SMAW coatings showed a marked decrease; this demonstrated that the arc-sprayed coating was more desirable in an abrasive-corrosion environment. The study also showed that the resistance to material does not follow the expected trend, in which wear resistance increases with increasing hardness.
Journal of Materials Engineering and Performance – Springer Journals
Published: Mar 23, 2011
Read and print from thousands of top scholarly journals.
Already have an account? Log in
Bookmark this article. You can see your Bookmarks on your DeepDyve Library.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Copy and paste the desired citation format or use the link below to download a file formatted for EndNote
Access the full text.
Sign up today, get DeepDyve free for 14 days.
All DeepDyve websites use cookies to improve your online experience. They were placed on your computer when you launched this website. You can change your cookie settings through your browser.