To improve the bio-resistance of engineered wood composites products via gluing process, aqueous phenol formaldehyde (PF) resin was modified using nano CuO containing alkane surfactant and polyvinyl alcohol (PVA) 17-99. The modified PF system was analyzed by dynamic mechanical thermal analysis, and the mechanical properties of the bonded plywood panels including tensile strength, modulus of rupture (MOR), modulus of elasticity (MOE) and shear strength under five test conditions were also evaluated. The results indicated that the addition of nano CuO incorporating PVA 17-99 separated the gel point and vitrification point in the curve of tan δ, which is related to the delaying of moisture loss in modified PF resin during the curing process. The modification showed adverse effect on tensile strength but only a minimal influence on MOR and MOE. Additionally, PVA 17-99 reduced the water resistance of cured PF resins. However, with the test conditions of dipping in 100 °C water for 6 h, then drying for 20 h at 63 °C in air, followed by dipping in 100 °C water for 4 h, PVA consolidated the re-curing effect on the PF resin and compensated the strength loss from hydrolysis. Thus, the modified PF system not only guaranteed bio-resistance of glued wood composites via CuO, but also has the potential for developing self-curing wood composites being applied as structural construction materials.
European Journal of Wood and Wood Products – Springer Journals
Published: Jun 5, 2018
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera