Access the full text.
Sign up today, get DeepDyve free for 14 days.
Loading next page...
/lp/sage/effect-of-high-alumina-iron-ore-of-gibbsite-type-on-sintering-wPiD2pJApR
References (13)
-
Phase diagrams', 58; 1995, Dü sseldorf -
Liming Lu, R. Holmes, J. Manuel (2007)
Effects of Alumina on Sintering Performance of Hematite Iron OresIsij International, 47
-
C. Loo, W. Leung (2003)
Factors Influencing the Bonding Phase Structure of Iron Ore SintersIsij International, 43
-
K. Higuchi, M. Naito, Nakano Masanori, Y. Takamoto (2004)
Optimization of Chemical Composition and Microstructure of Iron Ore Sinter for Low-temperature Drip of Molten Iron with High PermeabilityIsij International, 44
-
E. Kasai, F. Saito (1996)
Note Differential Thermal Analysis of Assimilation and Melt-formation Phenomena in the Sintering Process of Iron OresIsij International, 36
-
K. MacKenzie, J. Temuujin, K. Okada (1999)
Thermal decomposition of mechanically activated gibbsiteThermochimica Acta, 327
-
Sarah Kiyanrad, Julia Lougovaya, A. Sarri, Kai Trampedach (1897)
Metall -
N. Webster, M. Pownceby, I. Madsen, J. Kimpton (2012)
Silico-ferrite of Calcium and Aluminum (SFCA) Iron Ore Sinter Bonding Phases: New Insights into Their Formation During Heating and CoolingMetallurgical and Materials Transactions B, 43
-
(1999)
Thermochim -
Neil Genzlinger (2006)
A. and QNew York Times Book Review
-
(2001)
Ceram -
W. Marsden (2012)
I and J -
O. Castelein, B. Soulestin, J. Bonnet, P. Blanchart (2001)
The influence of heating rate on the thermal behaviour and mullite formation from a kaolin raw materialCeramics International, 27
- Publisher
- SAGE
- Copyright
- © 2015 Institute of Materials, Minerals and Mining
- ISSN
- 0301-9233
- eISSN
- 1743-2812
- DOI
- 10.1179/1743281214y.0000000195
- Publisher site
- See Article on Publisher Site
Abstract
The fundamental properties and utilisation feasibility in the sintering production of a newly developed commercial iron ore resource were studied at laboratory scale in the present work. The new iron ore contained medium iron content and high of alumina of gibbsite type. The ore is a typical limonite, which could help to reduce the production cost of hot metal. The assimilation and fluidity properties of the new kind of high alumina iron ore were investigated, comparing with other kinds of limonite and magnetite iron ores. The effect of addition of the iron ore on sintering process was also performed in a sintering pot, and the properties of the sinter samples were then examined. The results showed that the melt formation and fluidity properties of the high alumina iron ore were not good, and it had adverse effect on sinter quality. The yield and strength of the sinter samples gradually decreased with the increasing of high alumina iron ore blending ratio from 7 to 27·3 wt-%. The reducibility first increased then decreased, and the low temperature reduction degradation characteristics changed in an opposite trend correspondingly. The softening–melting property of the sinter samples also deteriorated in the experiment and might have a negative influence on the blast furnace operation.
Journal
Ironmaking & Steelmaking – SAGE
Published: Jan 1, 2015
Keywords: Iron ore; Al2O3; Gibbsite; Sintering; Metallurgical properties