Access the full text.
Sign up today, get DeepDyve free for 14 days.
Loading next page...
/lp/multidisciplinary-digital-publishing-institute/experimental-devices-to-investigate-the-long-term-stability-of-phase-qgT21Y1c26
- Publisher
- Multidisciplinary Digital Publishing Institute
- Copyright
- © 1996-2020 MDPI (Basel, Switzerland) unless otherwise stated Disclaimer The statements, opinions and data contained in the journals are solely those of the individual authors and contributors and not of the publisher and the editor(s). MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. Terms and Conditions Privacy Policy
- ISSN
- 2076-3417
- DOI
- 10.3390/app10227968
- Publisher site
- See Article on Publisher Site
Abstract
applied sciences Article Experimental Devices to Investigate the Long-Term Stability of Phase Change Materials under Application Conditions 1 , 1 2 3 Christoph Rathgeber *, Stefan Hiebler , Rocío Bayón , Luisa F. Cabeza , 3 4 4 5 Gabriel Zsembinszki , Gerald Englmair , Mark Dannemand , Gonzalo Diarce , 6 6 7 7 Oliver Fellmann , Rebecca Ravotti , Dominic Groulx , Ali C. Kheirabadi , 8 9 9 10 , 11 Stefan Gschwander , Stephan Höhlein , Andreas König-Haagen , Noé Beaupere and Laurent Zalewski Bavarian Center for Applied Energy Research (ZAE Bayern), Walther-Meißner-Str. 6, 85748 Garching, Germany; stefan.hiebler@zae-bayern.de Thermal Storage and Solar Fuels Unit, CIEMAT-PSA, Av. Complutense 40, 28040 Madrid, Spain; rocio.bayon@ciemat.es GREiA Research Group, Universitat de Lleida, Pere de Cabrera s/n, 25001 Lleida, Spain; luisaf.cabeza@udl.cat (L.F.C.); gabriel.zsembinszki@udl.cat (G.Z.) Department of Civil Engineering, Technical University of Denmark (DTU), Brovej, Building 118, 2800 Kongens Lyngby, Denmark; gereng@byg.dtu.dk (G.E.); markd@byg.dtu.dk (M.D.) Faculty of Engineering of Bilbao, University of the Basque Country (UPV/EHU), Rafael Moreno Pitxitxi 2, 48012 Bilbao, Spain; gonzalo.diarce@ehu.eus Institute of Mechanical Engineering and Energy Technology IME, Lucerne University of Applied Sciences and Arts (HSLU), Technikumstrasse 21, 6048 Horw, Switzerland; oliver.fellmann@hslu.ch (O.F.); rebecca.ravotti@hslu.ch (R.R.) Lab of Applied Multiphase Thermal Engineering (LAMTE), Dalhousie University, 5269 Morris St., Halifax, NS B3H 4R2, Canada; dominic.groulx@dal.ca (D.G.); Dominic.Groulx@Dal.Ca (A.C.K.) Fraunhofer Institute for Solar Energy Systems ISE, Heidenhofstr. 2, 79110 Freiburg, Germany; stefan.gschwander@ise.fraunhofer.de Chair of Engineering Thermodynamics and Transport Processes (LTTT), Center of Energy Technology (ZET), University of Bayreuth, Universitätsstraße 30, 95447 Bayreuth, Germany; Stephan.Hoehlein@uni-bayreuth.de (S.H.); Andreas.koenig-haagen@uni-bayreuth.de (A.K.-H.) Laboratoire de Génie Civil et géo-Environnement (LGCgE), ULR 4515, Univercity Artois, F-62400 Béthune, France; noe.beaupere@cea.fr (N.B.); laurent.zalewski@univ-artois.fr (L.Z.) CEA/LITEN/DTNM/SA3D/LMCM, CEA Grenoble, Université Grenoble Alpes, 38000 Grenoble, France * Correspondence: christoph.rathgeber@zae-bayern.de; Tel.: +49-893-294-4288 Received: 1 September 2020; Accepted: 29 October 2020; Published: 10 November 2020 Abstract: An important prerequisite to select a reliable phase change material (PCM) for thermal energy storage applications is to test it under application conditions. In the case of solid–liquid PCM, a large amount of thermal energy can be stored and released in a small temperature range around the solid–liquid phase transition. Therefore, to test the long-term stability of solid–liquid PCM, they are subjected to melting and solidification processes taking into account the conditions of the intended application. In this work, 18 experimental devices to investigate the long-term stability of PCM are presented. The experiments can be divided into thermal cycling stability tests, tests on PCM with stable supercooling, and tests on the stability of phase change slurries (PCS). In addition to these experiments, appropriate methods to investigate a possible degradation of the PCM are introduced. Considering the diversity of the investigated devices and the wide range of experimental parameters, further work toward a standardization of PCM stability testing is recommended. Appl. Sci. 2020, 10, 7968; doi:10.3390/app10227968 www.mdpi.com/journal/applsci Appl. Sci. 2020, 10, 7968 2 of 30 Keywords: phase change materials (PCM); latent heat storage; degradation; thermal cycling stability; stable supercooling 1. Introduction Phase change materials (PCM) can store large amounts of thermal energy in a small temperature range around their phase change temperature. Therefore, latent heat storage systems based on PCM can provide high thermal energy storage densities [1–4]. An important prerequisite to select a reliable phase change material (PCM) for thermal energy storage applications is to investigate its stability under application conditions. Since appropriate testing devices are not commercially available, lots of di erent self-built devices exist in various research institutions. Many of these institutions are currently participating in IEA ES Annex 33/SHC Task 58 “Material and Component Development for Compact Thermal Energy Storage”, which is a joint working group of the “Energy Storage” (ES) and the “Solar Heating and Cooling” (SHC) Technology Collaboration Programmes (TCP) of the International Energy Agency (IEA) [5]. The main goal of this working group is to support an application-oriented development of innovative and compact thermal energy storage materials including PCM and thermochemical materials (TCM). Therefore, the participants have proposed sharing their experience regarding PCM stability testing. In total, 18 mostly self-built devices from 10 institutions are presented in this survey. The experiments performed can be divided in three types: type A: thermal cycling stability tests; type B: tests on PCM with stable supercooling, and type C: tests on the stability of phase change slurries (PCS). In the case of solid–liquid PCM, heat is stored and released under repeated melting and solidification processes, which are also referred as thermal cycles. To assess the suitability of a PCM for a thermal storage application, testing the variation of its thermal properties under repeated thermal cycling (type A tests) taking application conditions into account is crucial [6–8]. Relevant experimental conditions are the temperature interval, heating and cooling rates, contact to atmosphere, contact to container, heat exchanger material, etc. To study thermal cycling stability, the PCM under investigation is typically subjected to a temperature–time profile, as shown in Figure 1. Figure 1. Idealized temperature–time curves of a thermal cycling stability experiment of a solid–liquid phase change material (PCM); PCM temperature (red dashed line); and heat transfer medium temperature (black solid line). Appl. Sci. 2020, 10, 7968 3 of 30 Two temperature levels, one above (T ) and one below (T ) the melting temperature (T ), high low m are applied alternately for a defined number of cycles. Certain periods of time are necessary to obtain a complete phase change from solid to liquid and vice versa. In between these two temperature levels, transition steps are carried out, either using temperature ramps with controlled temperature gradients, allowing natural cooling, or by heating and cooling as fast as possible. The curves plotted in Figure 1 are idealized. In reality (e.g., as shown in Figure 20), both the temperature–time profile of the heat transfer medium (solid black line) and the temperature response of the PCM under investigation (dashed red line) will not change suddenly between isothermal segments and transition segments. In addition, in many experiments, supercooling of the PCM will occur at least to a small extent. Among the thermal properties to be checked after (or during) thermal cycling, the enthalpy–temperature curves upon melting and solidification are particularly relevant. In this context, a material can be regarded as stable after a certain number of thermal cycles if melting temperature and melting enthalpy variations remain within specific tolerance values. For example, according to the “RAL Quality Association PCM” [9] testing regulations, a decrease of the melting enthalpy by less than 10% and a melting temperature variation of 1 K can be tolerated after a certain number of cycles. PCM are classified in cycling categories according to the number of cycles performed without damage: from A category (10,000 cycles) to F category (50 cycles). However, the testing regulations of the “RAL Quality Association PCM” neither indicate details on the appropriate design of stability testing devices nor give recommendations on suitable experimental techniques to study the stability of relevant properties after thermal cycling (except calorimetric techniques to measure enthalpy–temperature curves). In addition, apart from defining di erent cycling categories, nothing is said about the long-term stability of PCM under application conditions. So far, other testing regulations dedicated to the thermal cycling stability of PCM have not been proposed. A concept for medium and long-term thermal energy storage is to utilize the ability of certain PCM to be stored as a liquid in the supercooled state. As investigated by Englmair et al. [10] and Desgrosseilliers [11], the application of sodium acetate trihydrate (SAT) in closed containers permits the use of its sensible heat capacity after melting while preserving its heat of fusion at room temperature in a state of stable supercooling. The result is a thermal energy storage capacity that can be used on demand by the controlled initialization of crystallization. This storage concept has been demonstrated for a solar heating system [12,13] and showed potential for compact thermal energy storage systems in buildings [14]. Recently, Duquesne et al. reported Xylitol [15] and Puupponen et al. reported micro-structured polyol-polystyrene composites [16] as further promising materials with stable supercooling properties. To investigate the stability of PCM with stable supercooling (type B tests), dedicated test procedures are required. In addition to temperature–time profiles of regular thermal cycling tests, both the degree and duration of supercooling are parameters of interest. Phase change slurries (PCS) are fluids composed of PCM and a carrier fluid [1]. A PCS is stable if the emulsified or encapsulated PCM droplets do not degrade during operation, e.g., due to an agglomeration of droplets or a PCM leakage in the case of capsules. Among others, the stability of PCS depends on the investigated sample and particle size and the applied flow rate. Stability testing of PCS is carried out with self-built experimental devices (type C tests) that provide application-oriented charging and discharging conditions. While existing studies reported on stability tests of a certain PCM tested with a certain device for a given number of thermal cycles (as e.g., in the review articles of Ferrer et al. [6] and Rathod and Banerjee [17]), this work focuses on the experimental devices and testing procedures that are being used to perform PCM stability tests under application conditions. The aims of this work are as follows: first, to give an overview of the variety of experimental devices that are being used to investigate the long-term stability of PCM; second, to compare the specifications and test conditions of these devices, and to identify di erences or similarities of the applied methods; third, to increase awareness that PCM stability studies need to take application conditions into account in order to investigate possible degradation phenomena in a realistic manner; Appl. Sci. 2020, 10, 7968 4 of 30 and fourth, to initiate a discussion of whether there is a need to define or develop standardized stability test devices and procedures. Following the comparison of investigated validation test devices of types A to C (Section 2), appropriate experimental methods to detect a possible degradation of the PCM are introduced (Section 3). 2. Comparison of Experimental Devices 2.1. Summary of Technical Specifications This article is based on a survey comparing the experimental conditions and procedures of 18 testing devices from 10 di erent institutions. The device names used are formed according to the abbreviations of the respective institute designations. The technical specifications and the experimental conditions of these devices are summarized in Table 1. Devices are divided into thermal cycling stability tests (type A), tests on PCM utilizing stable supercooling (type B), and tests on the stability of PCS and encapsulated PCM (type C). The experimental devices for thermal cycling stability tests (type A) are typically used to test common PCM such as salt hydrates, parans, and other organic materials (e.g., fatty acids and esters). Further information about the investigated materials and their measured stability as well as further specifications of the devices can be found in the quoted references. Appl. Sci. 2020, 10, 7968 5 of 30 Table 1. Specifications of testing devices (device types A–C explained in Section 2.1). Explanations of columns: typical size (range) of the investigated sample; temperature range of measurements DT; heating and cooling rates between isothermal segments; typical number of melting–solidification cycles per day; atmosphere the PCM sample is in contact with; abbreviations used for stability tests: T(t) = comparison of temperature–time curves of di erent cycles, m(t) = sample cycles mass monitoring after certain number of cycles or time, vis. = visually, Dh = comparison of the thermal energy content in repeated storage cycles, T(t) = cycles solid. temperature profile during material solidification, Dp = pressure loss of cooling heat exchanger, = viscosity measurement, further abbreviations in nomenclature; HX material of sample container. Device Name Heating, Cooling Sample Size T/ C Cycles Per Day Atmosphere Stability Tests Sample Container Ref. (Type) Rate/Kmin CIEMAT I (A) 60–100 mL RT –350 1–20 1 air T(t) , DSC, m(t) glass, ceramic [18,19] cycles CIEMAT II (A) 10 mL RT–500 1–20, natural 1 air T(t) , DSC, m(t) ceramic [18,19] cycles T(t) , DSC, m(t) CIEMAT III (A) 60 mL RT–500 1–20, natural 1 air, N , Ar ceramic [20] 2 cycles EHU (A) 5 g 45–200 variable variable air, N , Ar DSC, vis., XRD, FTIR glass, metal - 1 100 mL, 3 25 T(t) , DSC, vis. HSLU (A) 40–180 10; 0.5 10 air glass - cycles mL, 5 8 mL ISE capsules (A) <22 L 10–80 1; 1 10 air DSC, m(t), RLM polystyrene [21] ISE Peltier (A) 10–100 mL 30–200 variable <24 air DSC, vis. stainless steel LAMTE (A) 3–6 mL 5–125 13; 7 <140 air DSC glass, plastic [22–25] T(t) , Dh , cycles cycles LGCgE (A) 270 mL 5–80 0.05–0.3 2–3 air, vacuum PMMA [26] T(t) solid. LTTT (A) 10–100 ml 20–180 variable variable air T(t) , DSC glass, metal, plastic [27] cycles UDL-GREiA I (A) 18 0.5 mL 4–99 50; 50 100 air DSC, FT-IR, TGA polypropylene [4,28] UDL-GREiA II (A) 154 L 20–400 1; natural 1 air DSC, FT-IR, TGA stainless steel [29–38] aluminum, stainless UDL-GREiA III (A) 8 L 10–80 0.5; 1 2 air DSC, FT-IR, TGA [39] steel ZAE (A) 60 ml 30–220 1 2 air T(t) , DSC, vis. glass, stainless steel [7] cycles DTU full-scale (B) 100–200 L 20–90 1; 0.5 air T(t) , Dh metal, plastic [40–42] 0.2 (0.4 ) cycles cycles T(t) , Dh , cycles cycles DTU heat loss (B) 200 g 20–90 1; natural air glass jar, metal lid [43] 0.25 (0.5 ) T(t) solid. DTU multiple (B) 10 30 L 8–93 0.15; 3–4 0.25 air T(t) , Dh stainless steel [44] cycles cycles 4 4 5 ISE PCS (C) 3.5 L 10–80 140; 100 1300 - DSC, Dp , PSA, stainless steel [45] HX 1 2 3 4 1 5 RT = room temperature, without supercooling of SAT, max. bath volume, at 200 lh , PCS in contact with water. Appl. Sci. 2020, 10, 7968 6 of 30 2.2. Descriptions of Testing Devices In this section, the experimental setups, operating principles, and testing procedures of the self-built stability testing devices are presented. Devices are grouped and listed in the same order as in Table 1. 2.2.1. Type A—Thermal Cycling Stability Tests CIEMAT I The experimental device “CIEMAT I” is an oven that allows performing thermal tests under controlled heating and cooling rates with stand-by periods at constant temperatures up to 350 C. Pictures of this device are shown in Figure 2. Thermal cycles can be performed between two temperature levels with transitions via linear ramps with rates from 1 to 20 Kmin . These ramps can be combined with stand-by periods up to a maximum test time of 24 h. Figure 2. Setup outside (a) and oven inside (b) of the device “CIEMAT I”. The temperature inside the oven is accurately controlled thanks to a fan located on one side, which provides forced ventilation (Figure 2b). Various samples with di erent sizes can be tested simultaneously under static ambient air. During the experiments, the temperature of both sample(s) and oven are monitored with calibrated T-type thermocouples. CIEMAT II The “CIEMAT II” device consists of a vertical oven with a cylindrical ceramic cavity as shown in Figure 3. This oven can perform thermal cycles up to 500 C at controlled heating rates (between 1 and 20 Kmin ) with stand-by periods at constant temperature. To cool down the sample, the heating system automatically switches o so that only natural cooling can be achieved. This device also allows performing thermal tests at constant temperature for indefinite periods of time. Moreover, it can be installed inside an extraction hood so that PCM thermal degradation tests under air can be carried out either at constant heating rate or constant temperature. As shown in Figure 3b, only one sample can be tested at a time remaining under atmospheric air. During the experiments, the sample temperature is monitored with calibrated T-type or J-type thermocouples. Typically, one thermal cycle per day is carried out. Appl. Sci. 2020, 10, 7968 7 of 30 Figure 3. Setup outside (a) and oven inside (b) of the device “CIEMAT II”. CIEMAT III “CIEMAT III” is a thermal cycling device shown in Figure 4. It consists of a vessel enclosed inside a furnace that allows performing cycles under controlled heating (between 1 and 20 Kmin ) up to 500 C and natural cooling (Figure 4a) with stand-by periods in between. This device also allows performing thermal tests at constant temperature for indefinite periods of time. The testing vessel is a metallic cavity closed by two flanges where only one sample can be introduced. In the upper covering flange, a J-type thermocouple is installed to record the sample temperature during the experiments, and the lower flange has two connecting pipes for gas inlet and outlet, respectively (Figure 4b). Each gas pipe is connected to a valve that allows gas entrance and exit and keeps the pressure in the device at a user-defined pressure range. The gas facility is prepared for using Ar or N , but other gases such as air might also be used. Figure 4. Setup outside and furnace (a) and setup inside (b) of the device “CIEMAT III”. EHU The testing device “EHU” is comprised of a thermostatic bath and airtight tubes. The samples are inserted inside the tubes, and these are immersed into the thermostatic bath, which uses silicone oil as a heat transfer fluid. The tubes are made of glass and include a nylon screwed cap with an O-ring sealing that ensures tightness. They can handle pressures up to 10 bar. The usual sample size is approximately 5 g, although tubes with variable dimensions can be employed (Figure 5). Appl. Sci. 2020, 10, 7968 8 of 30 Figure 5. Pictures of stability testing device “EHU”; thermostatic bath (a), glass tube and cap (b), thermally cycled samples (c). The arrangement and configuration are flexible and adapted to the investigated PCM and the kind of degradation expected. The temperature program usually comprises consecutive heating and cooling cycles if physical phase separation is expected. When the material under study might undergo thermal decomposition, then the program normally consists of submitting di erent samples to a constant temperature. The samples are extracted after di erent periods of time and analyzed. Several complementary techniques are used. Variations on the thermal behavior (storage capacity, melting temperatures, and others) are evaluated by di erential scanning calorimetry (DSC). Visual control is kept by periodic imaging. Additional information is obtained by X-Ray di raction, Fourier transform infrared spectroscopy (FT-IR), and liquid chromatography. During the experiment, the temperature of the thermostatic bath is measured. The temperature inside of the samples can be also recorded by introducing a thermocouple inside a “sacrificed” sample. Normally, the PCM is in contact with air. However, other gases (e.g., N or Ar) can be introduced by the use of a controlled atmosphere chamber (a globe box). HSLU The setup used at Lucerne University of Applied Sciences and Arts (HSLU) is based on the commercial device Easymax 102 (METTLER TOLEDO AG., CH), which is used as a cycling device and synthesis station (Figure 6). The Easymax is operated between 30 and 180 C. Two heating chambers with various adapters allow the measurement with one to five vessels (1 100 mL, 3 25 mL, 5 8 mL) per chamber (Figure 7a). Magnetic or mechanical stirring can be applied. Easymax 102 contains one temperature sensor per chamber. Therefore, an external logging device to record the temperature of the other vessels is used. Di erent heating and cooling rates can be applied, either using a fixed rate or by controlled heating so that a temperature di erence between the sample temperature (T ) and the temperature of the jacket (T ) is not exceeded. If more than one vessel per chamber is measured, only heating by rate is possible (Figure 8). During the experiments, the jacket temperature T and the reaction temperature T are measured. With the addition of a reaction calorimetry unit (Figure 7b), the phase change enthalpy, heat transfer coecient, and specific heat can be determined as well. Typically, ten thermal cycles per day are carried out. Appl. Sci. 2020, 10, 7968 9 of 30 Figure 6. Picture of stability testing device “HSLU”. Figure 7. Sample containers of the stability testing device “HSLU” (a), reaction calorimetry unit (b). Figure 8. Typical temperature profiles of the stability testing device “HSLU” (fixed heating and cooling rate (a), constant temperature di erence upon heating and fixed cooling rate (b)); jacket temperature T , and reaction temperature T . r Appl. Sci. 2020, 10, 7968 10 of 30 ISE Capsules The test facility “ISE capsules” consists of an open bath in which the encapsulated PCM samples are immersed. Circulating tap water is applied as a heat transfer fluid. The flow rate can be adjusted manually by means of a pump with a downstream restriction. The bath temperature is controlled by a thermostat that supplies heat to the test circuit by a heat exchanger. Temperature sensors at the flow and return line of the bath and a volume flow sensor allow the thermal balancing of the heat stored in the PCM macro-capsules. The schematic of the setup is shown in Figure 9. Figure 9. Schematic of stability testing device “ISE capsules”. The typical temperature profile is comprised of temperature steps (1 Kmin heating and cooling rate), which are repeated cyclically. The set temperatures depend on the PCM under investigation and are usually set 5 K below and above the melting temperature of the PCM. Typically, ten thermal cycles per day are carried out. ISE Peltier This is a flexible Peltier test rig for cycling in the temperature range 30 to 200 C. Up to 16 Peltier modules with a maximum heating and cooling power of 30 W each and a surface of 65 65 mm can be flexibly combined in the x and z directions. Each Peltier module has two Peltier elements: one on the bottom and one on top. The upper Peltier elements are single point fixed to compensate for non-parallel surfaces. The contact pressure of the upper Peltier element can be controlled by pressurized air. A picture of the Peltier test rig is shown in Figure 10. Figure 10. Peltier test rig. Up to eight individual temperature controllers are used to control the temperature of samples. Peltier elements can be individually attached to each controller. Temperature profiles are composed of basic segments. Basic segments are the sudden temperature change, ramp, or isotherms. Heating and cooling rates can be defined individually. Sample crucibles are designed as needed. In line stability check is not foreseen. External stability check via DSC, optical inspection, or others is necessary. Measured data are the temperatures of the PCM (middle or surface) and the temperature of the Peltier surface. Up to 24 thermal cycles per day are carried out. Appl. Sci. 2020, 10, 7968 11 of 30 LAMTE The cycling device “LAMTE” is used to simultaneously cycle up to eight samples within a similar range of phase transition temperatures. The temperature is adjusted using two cartridge heaters embedded in an aluminum block as heat sources and four thermoelectric coolers for cooling of the system. Typically, a heating rate of approximately 13 Kmin and a cooling rate of approximately 7 Kmin are applied. Pictures of the device are given in Figure 11. Figure 11. (a) Schematic diagram showing the various components of the thermal cycler general assembly, (b) photograph of the actual experimental setup, and (c) photograph of the housing unit with the heating and cooling elements and vials containing PCM (reproduced with permission from [22], Elsevier, 2016). The maximum sample volume is 7.4 mL. Typically, only half the volume is used to allow for any expansion. The PCM is inserted in a dram vial made of borosilicate glass with a 15–425 threaded PTFE/silicone liner cap; the vial is inserted in the aluminum block where thermal grease is applied between the aluminum and the PCM vial to reduce thermal resistance to conduction. During the experiments, the temperature–time curve of the aluminum block is measured using a negative coecient (NTC) thermistor. A typical temperature-time profile is shown in Figure 12. A numerical study of the system was done to determine the temperature, and phase, history of a PCM inside the dram vial during both the melting and solidification phase of the cycle, therefore ensuring complete melting and solidification of the PCM during each cycle [23]. Up to 140 thermal cycles per day are carried out. Appl. Sci. 2020, 10, 7968 12 of 30 Figure 12. Typical temperature–time profile of stability testing device “LAMTE”. LGCgE The Fluxmetric bench (Figure 13a) is a thermal cycling device used to impose temperature ramps on both larger sides of a parallelepipedal poly(methyl methacrylate) (PMMA) sample containing PCM (Figure 13b). Temperature ramps are applied thanks to the exchanger plates, each of which is connected to a refrigerated/heating circulator controlled by a computer. Typically, a heating rate of approximately 1 1 0.05 Kmin and a cooling rate of approximately 0.3 Kmin are applied. Two to three thermal cycles per day are carried out. The four smaller faces of the sample are insulated so as to minimize lateral heat losses (Figure 13b). In its current configuration, the container is filled with 270 mL of PCM. This configuration allows limiting convective flow when the PCM is in a liquid state. A heat flux meter incorporating a T-type thermocouple is placed on each side of the PMMA sample in order to calculate the energy balance at each heat cycle and to identify the melting and solidification temperatures. Between each temperature ramp, an isothermal step is imposed to return to an equilibrium (isothermal state and heat flux = 0) (Figure 14). For each fusion, the latent heat is estimated by subtracting the sensible energy stored (stored by PMMA and PCM) from the total stored energy measured by heat flux meters. For example, multiple heating and cooling ramps have been imposed on SAT to study its aging by following the variation in the amount of latent heat involved in each melting transition [26]. At each cooling ramp, the temperature of the stochastic solidification (or degree of supercooling) can be identified. For each cooling ramp, by observing the peak of heat flux at the moment of crystallization, the degree of supercooling can be estimated (Figure 14). In Figure 14, part of a thermal cycling experiment on SAT is shown beginning with the crystallization of cycle 32 (“Crist. 32”) up to cycle 35. Cycle 34 consist of melting (Melt. 34), cooling down without crystallization (“Sensible heat loss”) followed by the crystallization of the supercooled liquid (“Crist. 34”). Appl. Sci. 2020, 10, 7968 13 of 30 Figure 13. Fluxmetric bench “LGCgE” (a), parallelepipedal poly (methyl methacrylate) (PMMA) sample containing PCM with the lateral heat fluxmeters before installation in the insulation (b). Figure 14. Ramps of temperature and heat fluxes measurements during thermal cycling of sodium acetate trihydrate (SAT). LTTT The thermal cycling device “LTTT” is comprised of a thermostatic bath (water or thermal oil) with a 4-channel PT100 data logger (expandable). Pictures of the device are shown in Figure 15. As temperature profile, one temperature level above and one the below phase-change temperature with a rapid change between the temperature levels or with defined heating/cooling rates are applied. Up to 16 samples can be cycled simultaneously in test tubes (made of glass, metal, or plastic), which are sealed with a rubber plug and immersed in the thermostatic bath. During the experiments, temperature–time curves of the samples are measured. After a certain number of cycles, DSC measurements are performed, and the temperature curves of the samples are analyzed. Appl. Sci. 2020, 10, 7968 14 of 30 Figure 15. View of the stability testing device “LTTT” (a) and detailed view of the arrangement of the sample holders (b). UDL-GREiA I (This Equipment Is Shared with the University of Barcelona, DIOPMA Research Group) The GeneQ BIOER TC-18/H(b) thermal cycler allows performing thermal cycles from room temperature up to 100 C to investigate the stability of PCM samples over time. Typically, 50 Kmin is applied as the heating and cooling rate. Up to 100 thermal cycles per day are carried out. The thermal cycler allows placing 18 samples at the same time in 0.5 mL Eppendorf tubes. The Eppendorf tube must not be filled completely, as only the lower part will be subjected to heating and cooling cycles. It is recommended to fill 2/3 of the Eppendorf tube. Depending on the aim of the study, di erent temperature profiles can be applied. A picture of the stability testing device “GREiA I” is shown in Figure 16. Figure 16. Picture of stability testing device “UDL-GREiA I”. Appl. Sci. 2020, 10, 7968 15 of 30 UDL-GREiA II The pilot plant at the University of Lleida was built to accurately test di erent thermal energy storage (TES) systems working with latent or sensible heat storage materials. This facility is composed of a 24 kW electrical boiler to heat up the heat transfer fluid (HTF) (acting as energy source during the charging process), di erent storage tanks containing PCM, and a 20 kW air heat exchanger to cool down the HTF (acting as energy consumption). Typically, one thermal cycle per day is carried out. A picture and schematic of the pilot plant test facility are shown in Figure 17. Figure 17. (a) Picture and (b) scheme of stability testing device “UDL-GREiA II” (reproduced with permission from [46], University of Lleida, 2017). The letters in the figure (a) correspond to: (a) electrical heater, (b) air–heat transfer fluid (HTF) heat exchanger, (c) hot tank, (d) cold tank, (e) plate heat exchanger HTF–molten salt, (f) HTF loop, (g) molten salt, (h) acquisition and recording system, (i) latent thermal energy storage system, and (j) sensible thermal energy storage system. A data acquisition system consisting of temperature, pressure, and flow rate sensors as well as di erent data loggers and a personal computer were integrated in the facility to measure the HTF flows, HTF pressures, and HTF and PCM temperatures in the boiler and storage tank, respectively. Depending on the aim of the study, di erent temperature profiles are applied. In this regard, during experimental tests that are carried out to assess the performance of components such as PCM tanks under di erent charging and discharging conditions, thermal cycling testing of the PCM can also be realized as far as the required number of thermal cycles and the temperature profile are known. Then, the degradation of PCM after di erent cycles can be evaluated at a pilot-plant scale, or small samples of the PCM can be extracted and analyzed in the lab using established techniques, such as DSC, FT-IR spectroscopy, or thermogravimetric analysis (TGA). UDL-GREiA III This experimental setup of the GREiA lab at the University of Lleida was built to test the behavior of di erent types of heat exchangers and thermal energy storage tanks. Both charging and discharging of the thermal energy storage modules can be performed by means of two separate circuits: one cooling circuit connected to a variable capacity condensing unit, and one heating circuit connected to a thermal bath. There is the possibility of connecting the heating bath to a water storage tank to increase the thermal inertia and to provide a more stable water temperature to the heat exchangers. A picture and schematic of the test facility are shown in Figure 18. Appl. Sci. 2020, 10, 7968 16 of 30 Figure 18. Picture (a) and scheme (b) of test facility “UDL-GREiA III”. During the experiments, PCM and HTF temperatures, PCM pressure, and HTF flow rate are measured. Depending on the aim of the study, di erent temperature profiles can be applied. Due to the relatively small size of this setup, dedicated thermal cycling tests of PCM can be performed to study the degradation of the PCM after di erent numbers of melting–solidification cycles at lab scale. Typically, two thermal cycles per day are carried out. ZAE The thermal cycling test rig at ZAE Bayern can be applied to thermally cycle PCM under successive melting and crystallization processes and to visually detect the variation in appearance of the material, e.g., a phase separation. The test rig includes three sample containers to simultaneously investigate three PCM with similar melting temperatures [7]. A picture of the installation is given in Figure 19. Figure 19. Pictures of stability testing device “ZAE”. Appl. Sci. 2020, 10, 7968 17 of 30 To thermally cycle PCM, two di erent temperature levels for melting/freezing and transitions via linear ramps are applied (typically 1 Kmin heating and cooling rate). During the experiments, temperature–time curves of three temperature sensors within each of the three samples and three temperature sensors in the heat exchanger close to the sample containers are recorded. Figure 20 depicts the temperature–time data of one full thermal cycle. Figure 20. Temperature–time curves measured with the stability testing device “ZAE”. Usually, two thermal cycles per day are carried out. In the assessment of the cycling stability, special attention is paid to the visual detection of a possible phase separation. Figure 21 shows a thermally cycled sample at a temperature above the original melting point. Figure 21. Visual observation of phase separation of a solid–liquid PCM in the device “ZAE”. The visual observation indicates that at least three di erent phases are present: a liquid and two solid phases, one at the bottom and one at the top of the sample container. If no phase separation is observed, after a certain number of cycles, a small liquid amount of sample material is taken and measured via DSC to check for potential variations of the melting enthalpy and temperature. Performing thermal cycling stability tests under application-relevant conditions and observing potential phase separation visually has shown to provide a reliable assessment of the long-term thermal cycling stability of PCM, e.g., of PCM based on salt-water mixtures. Summary of Type A Tests Summarizing the experimental devices to investigate the thermal cycling stability of PCM, a large variety in terms of applied test conditions can be observed. Investigated sample sizes range from Appl. Sci. 2020, 10, 7968 18 of 30 0.5 mL to 154 l. Heating and cooling rates vary from 0.05 to 50 Kmin and, as a consequence, the typical number of thermal cycles that are carried out per day varies from 1 up to 140. Di erent sample container materials are being used: metals, glass, ceramic, and plastics. The atmosphere the PCM sample is in contact with is in most cases air. Two devices allow the use of inert gases (N , Ar) instead of air; one device is capable of applying vacuum. In principle, a device that is used for thermal cycling tests can also be used to apply a constant temperature to the sample under investigation. For example, this applies to the devices CIEMAT I, CIEMAT II, and CIEMAT III. Overall, the observed variety in terms of applied experimental test conditions can be a consequence of strongly di ering applications for which the stability tests have been performed and/or an indication for a lack of standardization regarding PCM thermal cycling stability testing. 2.2.2. Type B—Tests on Supercooled PCM In the case of PCM with stable supercooling, the investigation of long-term stability consists mainly in determining the reliability of the state of supercooling over a certain period of time under various experimental conditions (size of the sample container or storage tank, maximum charging temperature, minimum discharging temperature, etc.). The desired stability of a supercooled PCM storage unit is achieved if no spontaneous crystallization occurs during the discharge phase of the storage unit or during the holding time of the long-term storage phase. Since PCM storage systems based on stably supercooling PCM are usually operated as long-term storage systems, the number of thermal cycles to be investigated is comparatively low. DTU Full-Scale “DTU full-scale” is a full-scale heat storage prototype testing installation [40–42]. The stability of the supercooled PCM in contact with the container material is investigated. The setup is shown in Figure 22. Figure 22. Testing device “DTU full scale”: PCM heat storage test facility at DTU (a), schematic of charge and discharge loop (b). A typical temperature profile applied to study the supercooling of SAT consists in the following steps (Figure 23): charging from approximately 20 to 90 C, cooling down to ambient temperature (approximately 20 C), initialization of crystallization, and discharge to ambient temperature (approximately 20 C). Appl. Sci. 2020, 10, 7968 19 of 30 Figure 23. Temperature profile of a test cycle with supercooling of PCM (device “DTU full scale”). During the experiments, the following data are measured: temperatures (inlet, outlet) and volume flow rate of the heat transfer fluid, ambient temperature, and heat storage surface temperature. DTU Heat Loss Method With “DTU heat loss method”, determination of the heat content of (supercooled) PCM at a large sample size (approximately 200 g) is performed [43]. Pictures of the testing device are shown in Figure 24. Figure 24. (a) Glass jar with lid, (b) the well-insulated box, (c) locations of temperature sensors (“DTU heat loss method”). In the case of supercooled SAT, a typical temperature profile consists in heating up the sample in the oven from approximately 20 to 90 C followed by cooling down to ambient temperature at approximately 20 C. Then, the crystallization of supercooled SAT is initiated inside an insulated chamber by means of a seed crystal, and the temperature–time curve during the temperature rises due to the crystallization enthalpy, and the succeeding cooling down to ambient temperature is measured. Figure 25 depicts the temperature development of a SAT sample, where the heat content was evaluated as the thermal energy dispersed to the ambience (green area). Appl. Sci. 2020, 10, 7968 20 of 30 Figure 25. Exemplary cooling process of PCM samples in the device “DTU heat loss method”. DTU Multiple Storage The device “DTU multiple storage” consists of multiple (10) identical heat storage units [47] which are subjected to repeated heating and cooling cycles with various temperature levels and durations [44]. SAT has been investigated as PCM utilizing supercooling. The focus of the investigations is the e ect of di erent temperature levels and duration of charge on the supercooling stability of SAT. Illustrations of the testing device are given in Figure 26. Figure 26. Testing device “DTU multiple storage”: PCM heat storage test facility at DTU (a), schematic of charge and discharge loop (b). Regarding application conditions, discharge is conducted with cold water at 10 C. As the focus of investigations is the supercooling behavior of SAT, a typical temperature profile consists of the following steps: charging in periods of 8 to 16 h from 10 to 90 C, cooling down to 10 to 30 C, 72 h observation period (looking for spontaneous crystallization of the supercooled SAT), intentional initialization of solidification and discharge (at 10 to 30 C). During the experiments, the following data are measured: temperatures (inlet, outlet) and volume flow rate of the heat transfer fluid, ambient temperature, and heat storage surface temperature. Summary of Type B Tests In this study, the experimental setups to investigate the stability of PCM with stable supercooling are dedicated to the properties of SAT. Due to the melting temperature of SAT at 58 C and its significant supercooling, the experimental devices in this section are being operated within the temperature range Appl. Sci. 2020, 10, 7968 21 of 30 of approximately 10 to 90 C. As the three experimental devices in this section have been designed by the same research group, it is not surprising that they cover di erent parts of stability investigations on supercooled SAT. The “DTU heat loss method” was applied to identify promising SAT composites by screening samples of up to 200 g with a variety of additive concentrations. The “DTU full scale” setup was used to test prototype stores of up to 200 l storage volume with previously identified promising SAT composites in combination with container and heat exchangers, which are designed to enable stable supercooling. The test setup “DTU multiple storage” was designed to perform long-term stability tests. The operation of up to 10 storage prototype units with 30 l storage volume with typical application conditions (under variation of charging temperature, charging duration, and supercooling periods) is used to elucidate the reliability of developed heat stores. 2.2.3. Type C—Tests on Phase Change Slurries (PCS) ISE PCS The device “ISE PCS” (Figure 27) is a phase change slurry cycling test rig to determine the stability of PCS while cycling through a hydraulic system in which the dispersed PCM is exposed to repeated phase transitions and shear stress caused by a pump and other hydraulic components. It consists of three hydraulic circuits: the PCS test circuit, a heating circuit, and a cooling circuit; the last two are connected to thermostats (Figure 28). The heat flux in these two circuits is recorded by measuring the volume flows and the temperature di erence over the heat exchangers. In the PCS circuit, the volume flow and the temperatures over the heat exchangers are measured as well, so it is possible to monitor the heat flux into and out of the PCS. Additionally, the pressure di erence over the cooling heat exchanger on the PCS side is recorded. Samples of PCS for analysis can be taken while the test facility is in operation. To cycle PCS, the following temperature profile is typically applied: constant temperature at the output of the heating and cooling heat exchanger in the secondary circuit with temperature levels depending on the phase transition temperature range of the dispersed PCM. The cycle rate is determined by the volume of PCS filled into the secondary circuit and the volume flow applied. At 200 lh volume flow, approximately 1300 cycles per day are carried out. During the experiments, the following data are measured: temperatures at the inlets and outlets of both heat exchangers in the primary and secondary circuits; volume flows in all three circuits; and pressure loss in the secondary circuit of the cooling heat exchanger. The detection of degradation is done on five di erent parameters: (a) heat flux into and out of the PCS, (b) pressure drop over the cooling heat exchanger, (c) particle size distribution, (d) enthalpy determination via DSC, and (e) viscosity measurement of samples taken. Figure 27. Picture of stability testing device “ISE PCS”. Appl. Sci. 2020, 10, 7968 22 of 30 Figure 28. Schematic of stability testing device “ISE PCS”. Summary of Type C Tests For this survey, one device for the investigation of the stability of PCS has been considered. Comparing the PCS test rig with the other stability testing devices of type A and type B, it can be observed that the PCS test rig applies the highest heating and cooling rates and the highest number of thermal cycles that are carried out per day to its samples. Such a fast melting and solidification of the sample is possible because PCS consist of PCM in comparably small volumes (emulsified or encapsulated) leading to a large heat transfer area and a relatively fast phase change between solid and liquid. Due to the special properties of PCS, the methods for investigating possible degradation processes also di er from those used for PCM and PCM with stable supercooling. 3. Experimental Techniques to Check a Possible Degradation of PCM In this section, appropriate methods to check for a possible degradation of the PCM after testing under application conditions are introduced. These methods include an analysis of temperature–time curves (Sections 3.1 and 3.2), calorimetric measurements and measurements of thermal energy content (Sections 3.3, 3.5 and 3.6), mass change studies (Sections 3.4 and 3.5), structural investigations (Section 3.7, Section 3.8, Section 3.9, Section 3.10) and tests dedicated to PCS (Section 3.11, Section 3.12, Section 3.13). The abbreviations of the methods used in Table 1 are indicated in parentheses in each subsection title. Information on the uncertainties of standard measuring instruments (e.g., DSC) is discussed in the respective publications on these measuring methods. Uncertainties of special methods that are not based on standard measurements (e.g., Sections 3.1, 3.2, 3.6 and 3.7) have to be determined in each individual case and cannot be discussed adequately in the context of this paper. 3.1. Comparison of Temperature–Time Curves of Di erent Cycles (“T(t) ”) cycles The shape of temperature–time curves upon melting and solidification of a PCM indicate the temperature range of solid–liquid phase change. In addition, the degree of supercooling can be determined by evaluating the temperature–time curves upon cooling. The idea of comparing temperature–time curves of di erent cycles performed during a thermal cycling test measurement is based on the assumption that a possible degradation of the PCM will have an influence on its thermal properties and, hence, will a ect the shape of temperature–time curves during the phase change. In the case of stability tests on PCM utilizing stable supercooling (type B), temperature–time curves indicate if and when unwanted crystallization occurs. Appl. Sci. 2020, 10, 7968 23 of 30 3.2. Temperature Profile During Material Solidification (“T(t) ”) solid Knowing the heat loss coecient of a vessel containing supercooled PCM in temperature equilibrium with the ambience, the heat content can be evaluated as the thermal energy dispersed to the ambience. This method was applied for stability tests on PCM utilizing stable supercooling (type B). If the heat content measured in successive storage cycles is reduced, degradation of the PCM may have occurred. A change in the plateau temperature during solidification can also indicate a degradation of the PCM. 3.3. Di erential Scanning Calorimetry (“DSC”) Di erential scanning calorimetry (DSC) is a widely used technique to measure the melting temperature and melting enthalpy of PCM. With DSC measurements, enthalpy–temperature curves upon heating and cooling can be determined [48]. Due to the relatively small sample size (in the order of 5 to 20 mg), the degree of supercooling observed in DSC is increased compared with the behavior of PCM in larger quantities [49,50]. Therefore, the analysis of DSC heating curves is more favorable in the context of PCM stability testing: DSC measurements are applied to check if the melting temperature and enthalpy (or the enthalpy–temperature curves) after the testing under application conditions (e.g., thermal cycling tests) are the same as before the test. 3.4. Sample Mass Monitoring after Certain Number of Cycles or Time (“m(t)”) A clear indication that a certain PCM undergoes some kind of degradation is the decrease of mass with time when it is either cycled or kept at constant temperature above the melting point [51]. Mass decrease can be due to vaporization and, hence, to material loss but also to the formation of volatile species due to the occurrence of chemical reactions so that the PCM composition changes. If mass loss is due to chemical reactions leading to volatile species, not only PCM thermal properties are expected to change but dangerous compounds can be evolved [8]. Note that if PCM is reacting with the surrounding gases (mainly water vapor or oxygen), its mass could increase as well. Therefore, if mass variation is observed for a PCM, the material cannot be implemented in any storage system unless measures are taken for avoiding such behavior (encapsulation, inert environment under pressure, etc.). Ensuring that PCM mass does not change over time under application conditions is a key issue for its validation. Simple experimental procedures such sample weighting after a certain number of cycles or time interval [51] can be designed for detecting the occurrence of possible PCM volatilization and/or degradation. 3.5. Thermogravimetric Analysis (“TGA”) Another way to study PCM mass variation and possible degradation reactions is performing thermogravimetric analysis (TGA). TGA results can be compared with the results of sample mass monitoring to obtain more information about PCM stability. TGA is a technique that monitors the weight of a sample within a furnace to study the mass changes within a temperature range. This technique is suitable for di erent thermal analysis, such as decomposition temperature, oxidation, or loss of volatiles. A material sample of a few mg is placed inside the TGA apparatus usually exposed to air or nitrogen atmosphere, which is able to heat it at a controlled rate or maintain it at a defined temperature. The mass of the sample is recorded and can be plotted against temperature or time by means of a thermogravimetric curve (thermogram). In the case of PCM, TGA can be used to determine its maximum working temperature, usually defined as the temperature at which the sample loosed 1.5 wt % of its initial mass or after the dehydration process, and also the final degradation temperature, which can be extracted from the thermogram. Moreover, if TGA measurements are performed at various heating rates, degradation kinetics could be obtained as well and hence an estimation of the PCM lifetime [52]. Appl. Sci. 2020, 10, 7968 24 of 30 3.6. Comparison of the Thermal Energy Content in Repeated Storage Cycles (“Dh ”) cycles The thermal energy content of investigated samples determined for repeated storage cycles indicates cyclic material stability for applied test conditions (sample size, temperatures, cooling and heating rates). Observations can be analyzed regarding the initial storage cycle and/or in comparison with di erent material compositions (e.g., for the identification of the optimal amount of additives). Furthermore, the dependency of cyclic stability on the degree and the duration of PCM supercooling (type B) can be investigated. The thermal energy content of prototype storages including PCM, heat transfer fluid, and container material determined under typical application conditions is used to check the reliability of the investigated storage. 3.7. Visually (“vis.”) In the case of solid–liquid PCM, a visual observation of possible phase separation is a useful and simple measure to detect a degradation of a PCM during experimental testing. The presence of solid material at a temperature where the PCM should be completely molten is a clear indication of phase separation. Thereby, a visual control of phase separation can be favorable compared to measured temperature–time curves. If the temperature sensor is not in thermal contact with the precipitated solid, the measured temperature–time curves may not be a ected by the phase separation. Practically, a visual check of degradation can be carried out by taking pictures at given time intervals or temperature steps followed by an analysis of pictures from di erent thermal cycles. In addition, simply looking at the sample after the experimental investigations is a reliable measure to visually check degradation. In the case of degradation tests performed on organic PCM at elevated temperatures, a visual check also includes a possible change in the PCM color. For example, a browning of sugar alcohols indicates a thermal degradation of the sample [53]. 3.8. X-ray Powder Di raction (“XRD”) X-ray powder di raction (XRD) is mainly employed for the phase identification of a crystalline material, which can be used to perform compound identification. Therefore, the material is finely ground, homogenized, and the average bulk composition is determined. Based on these features, XRD can be easily applied to determine changes in the crystalline structure or the formation of new materials of a solid PCM due to a degradation process. XRD measurements are presented as a di ractogram, where the X-ray intensity is plotted as a function of the scanning angle. The typical aspect of a di ractogram consists of a horizontal baseline alternated with sharp peaks denoted as di ractions. These di ractions are used to identify the compounds present in the sample. If, e.g., due to a degradation on thermal cycling, new solid compounds appear in the solid PCM, they can be identified when comparing the di ractogram of the original sample with that of the degraded sample. Mass concentrations as low as 2% with respect to the sample mass can be detected. A potential phase separation can also be investigated by extracting aliquots from di erent locations of the PCM sample submitted to thermal cycling and comparing their phase/compound compositions by XRD. Some XRD devices can perform measurements under di erent temperatures, giving the possibility to study the variations of the structure of the solid PCM upon heating or cooling. 3.9. Fourier Transform Infrared Spectroscopy (FT-IR) Fourier transform infrared (FT-IR) spectroscopy is an analytical technique based on the vibrations of a molecule that is irradiated with infrared radiation at a specific wavelength range due to selective absorption of infrared radiation by the sample material. Since the wavelengths that are absorbed by the sample material are characteristic of its molecular structure, this technique allows identifying molecular components and structures of organic and inorganic materials. Appl. Sci. 2020, 10, 7968 25 of 30 FT-IR with attenuated total reflectance (ATR) allows analyzing the PCM chemical degradation caused by thermal cycling. The use of ATR has the advantage that the sample does not require any previous specific preparation to obtain the spectra. When the material is oxidized or degraded as a result of thermal cycling, a total or partial disappearance of the characteristic peaks and/or the appearance of new peaks are observed in the spectra. 3.10. Reflected Light Microscopy (RLM) In the case of the “ISE capsules” test rig, reflected light microscopy (RLM) is used for repeated optical inspections of PCM macrocapsules. With RLM, possible damage of the capsules walls can be detected that would lead to leakage of the PCM out of the capsules. 3.11. Pressure Loss of Cooling Heat Exchanger (Dp ) HX Measuring the pressure loss of a cooling heat exchanger is a method that is appropriate for the stability testing of PCS. An unstable PCS (e.g., damaged microcapsules) releases PCM material, which crystallizes at the heat exchanger surface when cooling below the crystallization temperature. PCM crystallizing at the heat exchanger surface increases the pressure drop over the heat exchanger. Therefore, this technique is a proper inline detection for a possible degradation of a PCS. 3.12. Particle Size Analysis (PSA) PCS show a change in particle size distribution when they degrade. Particle size measurement can be done inline or with separate devices (e.g., laser di ractometer). Using separate devices, samples have to be taken while the material is in a degradation process (e.g., conveyed in a hydraulic loop). 3.13. Viscosity Measurement () Viscosity measurements can be used to detect the degradation of PCS. A change in particle size is usually connected to a change in viscosity. However, even if there is no change in particle size, a reduction of the PCM fraction can occur due to separation in hydraulic systems. Such a separation leads to lower viscosity. 4. Conclusions The present survey is based on 18 experimental devices to investigate the long-term stability of solid–liquid PCM. The experiments are divided into thermal cycling stability tests, tests on PCM with stable supercooling, and tests on the stability of phase change slurries (PCS). Comparing the technical specifications and the applied test conditions, a large variety can be observed among the mostly self-built test rigs. Most of the devices are being used to perform thermal cycling stability tests. Depending on the type of PCM to be investigated and the intended application, di erent testing conditions are chosen, such as temperature range of investigation, heating and cooling rates to perform thermal cycles, sample container materials, and the atmosphere that the PCM sample is in contact with. Sample sizes in the order of few milliliters allow for the quick screening of properties, whereas samples of several hundred milliliters and more allow evaluating the material’s behavior without the enhanced supercooling typically observed in measurements on small samples. The chosen speed of PCM cycling depends on several boundary conditions, such as the sample size under investigation. Typically, the larger the sample, the slower the cycling. Relatively slow cycling of larger samples is often done in order to study the thermal cycling behavior of PCM under application conditions with few cycles per day to be carried out. So far, there is no consensus on how to accelerate stability tests of PCM reasonably. While several test rigs are designed to investigate di erent types of PCM for di erent applications, tests on PCM with stable supercooling are dedicated—but not limited—to SAT. Applied temperatures Appl. Sci. 2020, 10, 7968 26 of 30 (charging, discharging, and ambient) as well as the degree and the duration of supercooling should be in accordance to the conditions of the aimed application. In addition to the solid–liquid phase transition, tests on PCS investigate the mechanical stability of capsules or emulsions during pumping the PCS. Overall, the comparison of experimental devices can be an encouragement to discuss and develop uniform standards of PCM stability testing. The fact that many further devices are being used in other research groups strengthens this. A possible goal for future work in this context could be to propose a guideline for long-term stability investigations or to further develop existing testing regulations, e.g., the regulations from the “RAL Quality Association PCM”. Investigating the stability of PCM under application conditions requires, first, knowledge about the application and, second, a method to translate the application requirements into experimental testing conditions. Thereby, the second step influences the technical design of testing devices and applied testing procedures. It is especially this “translation” that is nowadays being done in a highly non-standardized manner. Further work toward a standardization of PCM stability testing is recommended. Author Contributions: Conceptualization, C.R., S.H. (Stefan Hiebler), R.B., L.F.C., G.Z., G.E., M.D., G.D., O.F., R.R., D.G., S.G., S.H. (Stephan Höhlein), A.K.-H. and L.Z.; Funding acquisition, C.R., S.H. (Stefan Hiebler), R.B., L.F.C., G.Z., G.E., M.D., G.D., O.F., R.R., D.G., S.G., S.H. (Stephan Höhlein), A.K.-H. and L.Z.; Investigation, C.R., S.H. (Stefan Hiebler), R.B., L.F.C., G.Z., G.E., M.D., G.D., O.F., R.R., D.G., A.C.K., S.G., S.H. (Stephan Höhlein), A.K.-H., N.B. and L.Z.; Methodology, C.R., S.H. (Stefan Hiebler), R.B., L.F.C., G.Z., G.E., M.D., G.D., O.F., R.R., D.G., S.G., S.H. (Stephan Höhlein), A.K.-H. and L.Z.; Writing—original draft, C.R.; Writing—review and editing, C.R., S.H. (Stefan Hiebler), R.B., L.F.C., G.Z., G.E., M.D., G.D., O.F., R.R., D.G., S.G., S.H. (Stephan Höhlein), A.K.-H. and L.Z. All authors have read and agreed to the published version of the manuscript. Funding: This survey has been carried out within the framework of IEA ES Annex 33/SHC Task 58 “Material and Component Development for Compact Thermal Energy Storage”, a joint working group of the “Energy Storage” (ES) and the “Solar Heating and Cooling” (SHC) Technology Collaboration Programmes of the International Energy Agency (IEA). The responsibility for the content of this publication is with the authors. The work of ZAE Bayern is part of the project properPCM and was supported by the German Federal Ministry of Economic A airs and Energy under the project code 03ET1342A. The work of CIEMAT is part of two projects: ACES2030 (S2018/EM-4319) which is supported by Comunidad de Madrid and European Structural Funds through and SFERA III (GA No 823802) which is supported by European Union’s Horizon H2020 Research and Innovation Programme. The work of DTU was supported by HM Heizkörper GmbH and the Danish Energy Agency through the EUDP program. The work of EHU is part of the project Sweet-TES (RTI2018-099557-B-C22), funded by the Spanish Ministry of Science, Innovation and Universities. The work of GREiA was partially funded by the Ministerio de Ciencia, Innovación y Universidades de España (RTI2018-093849-B-C31—MCIU/AEI/FEDER, UE) and by the Ministerio de Ciencia, Innovación y Universidades—Agencia Estatal de Investigación (AEI) (RED2018-102431-T). The authors would like to thank the Catalan Government for the quality accreditation given to their research group (GREiA 2017 SGR 1537). GREiA is certified agent TECNIO in the category of technology developers from the Government of Catalonia. This work is partially supported by ICREA under the ICREA Academia programme. The work of HSLU was partially funded by the Swiss Competence Centre for Energy Research on Heat and Electricity (SCCER HaE). The authors would like to thank the SCCER HaE as well as METTLER TOLEDO AG for the support given. The work of Fraunhofer ISE was part of the projects KOLAN (FKZ 03ESP357B) and KOKAP (FKZ 03ET1463A) which were administrated by the Projektträger Jülich (PtJ) and funded by the German Federal Ministry of Economic A airs and Energy. The work of LAMTE was supported by Intel Corporation, along with the Natural Sciences and Engineering Research Council of Canada (NSERC) and the Canada Foundation for Innovation. The work of LGCgE is partly funded by the French National Research Agency (ANR) under the project "Hybrid storage and heat exchanger device with PCM—EUROPA". Noé Beaupere’s PhD work was funded by the French Alternative Energies and Atomic Energy Commission (CEA) Grenoble. The work of LTTT is part of the project MALATrans and was funded by the German Federal Ministry for Economic A airs and Energy (BMWi) under the project code 03ESP227B. Conflicts of Interest: The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results. Appl. Sci. 2020, 10, 7968 27 of 30 Nomenclature DSC Di erential scanning calorimetry FT-IR Fourier transform infrared spectroscopy HTF Heat transfer fluid PCM Phase change material PCS Phase change slurry PMMA Poly (methyl methacrylate) PSA Particle size analysis RLM Reflected light microscope SAT Sodium acetate trihydrate TES Thermal energy storage TGA Thermogravimetric analysis TCM Thermochemical material XRD X-ray di raction spectroscopy h Specific enthalpy/Jg m Mass/kg Viscosity/Pas T Temperature/ C t Time/s References 1. Mehling, H.; Cabeza, L.F. Heat and Cold Storage with PCM; Springer: Berlin, Germany, 2008. 2. Zalba, B.; Marın, J.M.; Cabeza, L.F.; Mehling, H. Review on thermal energy storage with phase change: Materials, heat transfer analysis and applications. Appl. Therm. Eng. 2003, 23, 251–283. 3. Cabeza, L.F.; Castell, A.; Barreneche, C.D.; De Gracia, A.; Fernández, A.I. Materials used as PCM in thermal energy storage in buildings: A review. Renew. Sustain. Energy Rev. 2011, 15, 1675–1695. 4. Zsembinszki, G.; Fernández, A.G.; Cabeza, L.F. Selection of the Appropriate Phase Change Material for Two Innovative Compact Energy Storage Systems in Residential Buildings. Appl. Sci. 2020, 10, 2116. 5. IEA ES Annex 33/SHC Task 58 “Material and Component Development for Compact Thermal Energy Storage”. Available online: https://task58.iea-shc.org/ (accessed on 17 August 2020). 6. Ferrer, G.; Solé, A.; Barreneche, C.; Martorell, I.; Cabeza, L.F. Review on the methodology used in thermal stability characterization of phase change materials. Renew. Sustain. Energy Rev. 2015, 50, 665–685. 7. Rathgeber, C.; Grisval, A.; Schmit, H.; Hoock, P.; Hiebler, S. Concentration dependent melting enthalpy, crystallization velocity, and thermal cycling stability of pinacone hexahydrate. Thermochim. Acta 2018, 670, 142–147. 8. Bayón, R.; Rojas, E. Development of a new methodology for validating thermal storage media: Application to phase change materials. Int. J. Energy Res. 2019, 43, 6521–6541. 9. RAL Quality Association PCM. Quality and Testing Specifications for Phase Change Materials. 2018. Available online: http://www.pcm-ral.org/pcm/en/quality-testing-specifications-pcm/ (accessed on 17 August 2020). 10. Englmair, G.; Jiang, Y.; Dannemand, M.; Moser, C.; Schranzhofer, H.; Furbo, S.; Fan, J. Crystallization by local cooling of supercooled sodium acetate trihydrate composites for long-term heat storage. Energy Build. 2018, 180, 159–171. 11. Desgrosseilliers, L. Design and Evaluation of a Modular, Supercooling Phase Change Heat Storage Device for Indoor Heating. Ph.D. Thesis, Dalhousie University, Halifax, NS, Canada, 2016. Available online: https://dalspace.library.dal.ca/handle/10222/73309 (accessed on 17 August 2020). 12. Englmair, G.; Moser, C.; Furbo, S.; Dannemand, M.; Fan, J. Design and functionality of a segmented heat-storage prototype utilizing stable supercooling of sodium acetate trihydrate in a solar heating system. Appl. Energy 2018, 221, 522–534. Appl. Sci. 2020, 10, 7968 28 of 30 13. Englmair, G.; Kong, W.; Berg, J.B.; Furbo, S.; Fan, J. Demonstration of a solar combi-system utilizing stable supercooling of sodium acetate trihydrate for heat storage. Appl. Therm. Eng. 2020, 166, 114647. 14. Englmair, G.; Moser, C.; Schranzhofer, H.; Fan, J.; Furbo, S. A solar combi-system utilizing stable supercooling of sodium acetate trihydrate for heat storage: Numerical performance investigation. Appl. Energy 2019, 242, 1108–1120. 15. Duquesne, M.; Del Barrio, E.P.; Godin, A. Nucleation triggering of highly undercooled Xylitol using an air lift reactor for seasonal thermal energy storage. Appl. Sci. 2019, 9, 267. 16. Puupponen, S.; Mikkola, V.; Ala-Nissila, T.; Seppälä, A. Novel microstructured polyol-polystyrene composites for seasonal heat storage. Appl. Energy 2016, 172, 96–106. 17. Rathod, M.K.; Banerjee, J. Thermal stability of phase change materials used in latent heat energy storage systems: A review. Renew. Sustain. Energy Rev. 2013, 18, 246–258. 18. Bayón, R.; Biencinto, M.; Rojas, E.; Uranga, N. Study of hybrid dry cooling systems for STE plants based on latent storage. In Proceedings of the ISEC Conference, Graz, Austria, 3–5 October 2018. 19. Rodríguez-García, M.M.; Rojas, E.; Bayón, R. Test campaign and performance evaluation of a spiral latent storage module with Hitec as PCM. In Proceedings of the SWC 2017/SHC2017 Conference, Abu Dhabi, UAE, 29 October–2 November 2017. 20. Rodríguez-García, M.M.; Bayón, R.; Rojas, E. Stability of D-mannitol upon melting/freezing cycles under controlled inert atmosphere. Energy Procedia 2016, 91, 218–225. 21. Biedenbach, M.; Klünder, F.; Gschwander, S. Investigations on the stability of metallic cans for PCM macro-encapsulation. In Proceedings of the International Institute of Refrigeration (IIR), Birmingham, AL, USA, 2–5 September 2018. 22. Kahwaji, S.; Johnson, M.B.; Kheirabadi, A.C.; Groulx, D.; White, M.A. Stable, low-cost phase change material for building applications: The eutectic mixture of decanoic acid and tetradecanoic acid. Appl. Energy 2016, 168, 457–464. 23. Kheirabadi, A.C.; Groulx, D. Design of an automated thermal cycler for long-term phase change material phase transition stability studies. In Proceedings of the COMSOL Conference 2014, Boston, MA, USA, 8–10 October 2014. 24. Kahwaji, S.; Johnson, M.B.; Kheirabadi, A.C.; Groulx, D.; White, M.A. Fatty acids and related phase change materials for reliable thermal energy storage at moderate temperatures. Sol. Energy Mater. Sol. Cells 2017, 167, 109–120. 25. Kahwaji, S.; Johnson, M.B.; Kheirabadi, A.C.; Groulx, D.; White, M.A. A comprehensive study of properties of paran phase change materials for solar thermal energy storage and thermal management applications. Energy 2018, 162, 1169–1182. 26. Beaupere, N. Pilotage de la Libération de Chaleur et Etude du Vieillissement de Matériaux à Changement de Phase. Ph.D. Thesis, Université d’Artois/CEA Grenoble, Grenoble, France, 2019. 27. Orak, F.; König-Haagen, A.; Brüggemann, D. E ect of Nucleators on Heat Storage Properties of Salt Hydrates. In Proceedings of the 2017 11th International Renewable Energy Storage Conference (IRES 2017), Düsseldorf, Germany, 14–16 March 2017. 28. Navarro, L.; Solé, A.; Martín, M.; Barreneche, C.; Olivieri, L.; Tenorio, J.A.; Cabeza, L.F. Benchmarking of useful phase change materials for a building application. Energy Build. 2019, 182, 45–50. 29. Oró, E.; Gil, A.; Miró, L.; Peiró, G.; Álvarez, S.; Cabeza, L.F. Thermal energy storage implementation using phase change materials for solar cooling and refrigeration applications. Energy Procedia 2012, 30, 947–956. 30. Gil, A.; Oró, E.; Castell, A.; Cabeza, L.F. Experimental analysis of the e ectiveness of a high temperature thermal storage tank for solar cooling applications. Appl. Therm. Eng. 2013, 54, 521–527. 31. Gil, A.; Oró, E.; Miró, L.; Peiró, G.; Ruiz, A.; Salmerón, J.M.; Cabeza, L.F. Experimental analysis of hydroquinone used as phase change material (PCM) to be applied in solar cooling refrigeration. Int. J. Refrig. 2014, 39, 95–103. [CrossRef] 32. Peiró, G.; Gasia, J.; Miró, L.; Cabeza, L.F. Experimental evaluation at pilot plant scale of multiple PCMs (cascaded) vs. single PCM configuration for thermal energy storage. Renew. Energy 2015, 83, 729–736. [CrossRef] Appl. Sci. 2020, 10, 7968 29 of 30 33. Prieto, C.; Miró, L.; Peiró, G.; Oró, E.; Gil, A.; Cabeza, L.F. Temperature distribution and heat losses in molten salts tanks for CSP plants. Sol. Energy 2016, 135, 518–526. [CrossRef] 34. Peiró, G.; Gasia, J.; Miró, L.; Prieto, C.; Cabeza, L.F. Experimental analysis of charging and discharging processes, with parallel and counter flow arrangements, in a molten salts high temperature pilot plant scale setup. Appl. Energy 2016, 178, 394–403. [CrossRef] 35. Gasia, J.; de Gracia, A.; Peiró, G.; Arena, S.; Cau, G.; Cabeza, L.F. Use of partial load operating conditions for latent thermal energy storage management. Appl. Energy 2018, 216, 234–242. [CrossRef] 36. Peiró, G.; Prieto, C.; Gasia, J.; Jové, A.; Miró, L.; Cabeza, L.F. Two-tank molten salts thermal energy storage system for solar power plants at pilot plant scale: Lessons learnt and recommendations for its design, start-up and operation. Renew. Energy 2018, 121, 236–248. [CrossRef] 37. Gil, A.; Peiró, G.; Oró, E.; Cabeza, L.F. Experimental analysis of the e ective thermal conductivity enhancement of PCM using finned tubes in high temperature bulk tanks. Appl. Therm. Eng. 2018, 142, 736–744. [CrossRef] 38. Gasia, J.; de Gracia, A.; Zsembinszki, G.; Cabeza, L.F. Influence of the storage period between charge and discharge in a latent heat thermal energy storage system working under partial load operating conditions. Appl. Energy 2019, 235, 1389–1399. [CrossRef] 39. Mselle, B.D.; Verez, D.; Zsembinszki, G.; Borri, E.; Cabeza, L.F. Performance Study of Direct Integration of Phase Change Material into an Innovative Evaporator of a Simple Vapour Compression System. Appl. Sci. 2020, 10, 4649. [CrossRef] 40. Dannemand, M.; Dragsted, J.; Fan, J.; Johansen, J.B.; Kong, W.; Furbo, S. Experimental investigations on prototype heat storage units utilizing stable supercooling of sodium acetate trihydrate mixtures. Appl. Energy 2016, 169, 72–80. [CrossRef] 41. Dannemand, M.; Johansen, J.B.; Kong, W.; Furbo, S. Experimental investigations on cylindrical latent heat storage units with sodium acetate trihydrate composites utilizing supercooling. Appl. Energy 2016, 177, 591–601. [CrossRef] 42. Englmair, G.; Furbo, S.; Dannemand, M.; Fan, J. Experimental investigation of a tank-in-tank heat storage unit utilizing stable supercooling of sodium acetate trihydrate. Appl. Therm. Eng. 2020, 167, 114709. [CrossRef] 43. Kong, W.; Dannemand, M.; Johansen, J.B.; Fan, J.; Dragsted, J.; Englmair, G.; Furbo, S. Experimental investigations on heat content of supercooled sodium acetate trihydrate by a simple heat loss method. Sol. Energy 2016, 139, 249–257. [CrossRef] 44. Dannemand, M.; Furbo, S. Supercooling stability of sodium acetate trihydrate composites in multiple heat storage units. Refrig. Sci. Technol. 2018, 227–231. [CrossRef] 45. Niedermaier, S.; Biedenbach, M.; Gschwander, S. Characterisation and enhancement of phase change slurries. Energy Procedia 2016, 99, 64–71. [CrossRef] 46. Peiró, G. High Temperature Thermal Energy Storage for Solar Cooling and Solar Thermal Power Plants Applications. Ph.D. Thesis, University of Lleida, Lleida, Spain, 2017. Available online: http://hdl.handle.net/ 10803/462071 (accessed on 17 August 2020). 47. Deng, J.; Furbo, S.; Kong, W.; Fan, J. Thermal performance assessment and improvement of a solar domestic hot water tank with PCM in the mantle. Energy Build. 2018, 172, 10–21. [CrossRef] 48. Gschwander, S.; Haussmann, T.; Hagelstein, G.; Barreneche, C.; Ferrer, G.; Cabeza, L.; Diarce, G.; Hohenauer, W.; Lager, D.; Rathgeber, C.; et al. Standardization of pcm characterization via DSC. Refrig. Sci. Technol. 2016, 70–75. [CrossRef] 49. Rathgeber, C.; Schmit, H.; Miró, L.; Cabeza, L.F.; Gutierrez, A.; Ushak, S.N.; Hiebler, S. Enthalpy-temperature plots to compare calorimetric measurements of phase change materials at di erent sample scales. J. Storage Mater. 2018, 15, 32–38. [CrossRef] 50. Rathgeber, C.; Miró, L.; Cabeza, L.F.; Hiebler, S. Measurement of enthalpy curves of phase change materials via DSC and T-History: When are both methods needed to estimate the behaviour of the bulk material in applications? Thermochim. Acta 2014, 596, 79–88. [CrossRef] 51. Bayón, R.; Rojas, R. Feasibility study of D-mannitol as phase change material for thermal storage. AIMS Energy 2017, 5, 404–424. [CrossRef] Appl. Sci. 2020, 10, 7968 30 of 30 52. Doyle, C.D. Estimating isothermal life from thermogravimetric data. J. Appl. Polym. Sci. 1962, 6, 639–642. [CrossRef] 53. Solé, A.; Neumann, H.; Niedermaier, S.; Martorell, I.; Schossig, P.; Cabeza, L.F. Stability of sugar alcohols as PCM for thermal energy storage. Sol. Energy Mater. Sol. Cells 2014, 126, 125–134. [CrossRef] Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional aliations. © 2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
Journal
Applied Sciences – Multidisciplinary Digital Publishing Institute
Published: Nov 10, 2020