Enhanced Absorption in InP Nanodisk Arrays on Ultra-Thin-Film Silicon for Solar Cell Applications
Enhanced Absorption in InP Nanodisk Arrays on Ultra-Thin-Film Silicon for Solar Cell Applications
Kjellberg, Mikko;Ravishankar, Ajith Padyana;Anand, Srinivasan
hv photonics Article Enhanced Absorption in InP Nanodisk Arrays on Ultra-Thin-Film Silicon for Solar Cell Applications Mikko Kjellberg *, Ajith Padyana Ravishankar and Srinivasan Anand Department of Applied Physics, School of Engineering Sciences, KTH Royal Institute of Technology, Albanova University Center, SE 10691 Stockholm, Sweden; email@example.com (A.P.R.); firstname.lastname@example.org (S.A.) * Correspondence: email@example.com Abstract: The photovoltaic (PV) market today is dominated by silicon (Si)-based solar cells, which, however, can be improved in performance and cost by developing technologies that use less material. We propose an indium phosphide (InP) nanoresonator array on silicon ultra-thin ﬁlm with a combined thickness of 0.5 μm to 2 μm as a solution to minimize cost and maximize power efﬁciency. This paper focuses on simultaneously achieving broadband antireﬂection and enhanced absorption in thin-ﬁlm Si with integrated InP nanodisk arrays. Electromagnetic simulations are used to design and optimize the reﬂectance and absorption of the proposed design. By varying the height and radius of the InP nanodisks on the Si substrate, together with the array pitch, a weighted reﬂectance minimum, with respect to the AM1.5 solar spectrum, of 2.9% is obtained in the wavelength range of 400 nm to 1100 nm. The antireﬂective properties are found to be a combination of a Mie-resonance-induced strong forward-scattering into the structure and an effective index-matching to the Si substrate. In terms of absorption, even up to 2 μm from the Si surface the InP nanodisk/Si structure consistently shows superior performance compared to plain Si as well as a Si nanodisk/Si structure. At a depth of 500 nm from the surface of the substrate, the absorption values were found to be 47.5% for the InP nanodisk/Si structure compared to only 18.2% for a plain Si substrate. This shows that direct bandgap InP nanoresonator arrays on thin-ﬁlm Si solar cells can be a novel design to enhance the absorption efﬁciency of the cell. Citation: Kjellberg, M.; Ravishankar, A.P.; Anand, S. Enhanced Absorption Keywords: thin-ﬁlm solar cell; InP; antireﬂection; Mie resonators; absorption; nanodisks in InP Nanodisk Arrays on Ultra-Thin-Film Silicon for Solar Cell Applications. Photonics 2022, 9, 157. https://doi.org/10.3390/photonics 1. Introduction Solar cell production is dominated today by silicon (Si)-based technology, mainly Received: 8 February 2022 due to its high efﬁciency and mature production methods as well as the abundance and Accepted: 3 March 2022 non-toxicity of Si. However, Si solar cells require thick active layers, typically in excess Published: 5 March 2022 of a few 100 μm due to inefﬁcient absorption of light in Si compared to 1 μm to 2 μm in- direct bandgap materials such as gallium arsenide (GaAs) or indium phosphide (InP) . Publisher’s Note: MDPI stays neutral Although III-V (e.g., InP, GaAs) solar cells are highly efﬁcient, they are expensive. Most with regard to jurisdictional claims in commonly encountered low-cost thin-ﬁlm solar cells use materials such as amorphous published maps and institutional afﬁl- iations. silicon (a-Si), Indium Phosphide (InP), Cadmium Telluride (CdTe), and Copper Indium Gal- lium Selenide (CIGS). The thickness of these cells ranges from a few to tens of micrometers compared to a typical thickness of 200 μm to 500 μm of a c-Si solar cell. In recent years, great effort has been made to improve the efﬁciency of thin-ﬁlm solar cell technology and efﬁ- Copyright: © 2022 by the authors. ciencies of 24.2% (InP) 23.4%, (CIGS), 22.1% (CdTe) and 14.0% (a-Si) have been measured in Licensee MDPI, Basel, Switzerland. laboratory settings. However, with an efﬁciency of 26.1% c-Si is still leading the race [2–4]. This article is an open access article Progress on thin ﬁlm (a few microns) c-Si solar cell technology has been challenging [5,6]. distributed under the terms and Efﬁciencies of 21.5% for 50 μm thick cells , 13.7% for 10 μm thick cells ,11% for 2 μm conditions of the Creative Commons thick “micro-crystalline” Si , and 8% in 1 μm thick nanostructured crystalline Si  Attribution (CC BY) license (https:// have been reported. To enhance the absorption properties of Si-based solar cells two options creativecommons.org/licenses/by/ are usually considered: lowering reﬂection losses from the cell surface to maximize the light 4.0/). Photonics 2022, 9, 157. https://doi.org/10.3390/photonics9030157 https://www.mdpi.com/journal/photonics Photonics 2022, 9, 157 2 of 11 entering the cell and by improving the light trapping in the material. Different antireﬂective surfaces have been realized using coatings [11,12] and texturization [13,14] of the solar cell. The optical properties of subwavelength nanostructures as light scatterers and as resonators are relevant for antireﬂective surface design. Noble metal particles and structures have shown promise in this area due to excitation of localized plasmon resonances that can lead to a suppression of reﬂection and broadband absorption [15–18]. These metallic particles suffer from inherent ohmic losses at optical frequencies and are as such unsuitable for low loss applications. An approach is to instead use optical resonance phenomena in dielectric nanostructures. Both electric and magnetic dipole and higher-order multipole Mie reso- nances can be excited by light in high-index dielectric particles, allowing for applications such as antireﬂection, light trapping, and color ﬁlters [19–23]. Recent work on enhancing the absorption or carrier collection in a single InP layer or nanostructure InP solar cell technology has shown promise for efﬁcient InP solar cell applications [24–26]. However, these studies have concentrated on InP as a freestanding absorbing material. Meanwhile combining thin ﬁlm InP with a Si substrate as a solar cell has been proposed as early as 1986 . Using a wider bandgap semiconductor material on top of a lower bandgap Si ﬁlm to widen the absorption spectra, the efﬁciency of the solar cell can be increased. Direct integration of several relevant III–Vs (e.g., InP, GaAs etc.) on Si by heteroepitaxy remains a major challenge due to the large lattice mismatch between III-V materials and Si [28–31]. On the other hand, low-temperature wafer bonding is not subjected to lattice matching conditions and several integrated devices have been demonstrated [32,33]. However, this approach often involves removing the entire III-V substrate after bonding and the electronic quality of the III-V/Si interface must be improved for device applications that require in- timate contact at the interface [32,33]. Dielectric mediated bonding using silicon dioxide or benzocyclobutene (BCB) is not suitable for solar cells as they do not facilitate carrier transfer through the III-V/Si interface. Oxide-free bonding has been shown to result in high tensile bonding strengths with suitable electrical characteristics [34,35]. InP has a direct gap energy of 1.34 eV that matches the optimal energy gap of single-junction solar cells . Furthermore, the type-II energy band alignment (and offsets) of InP/Si together with ap- propriate doping makes InP a well-suited candidate for III-V/Si thin-ﬁlm solar cells. Even though GaAs thin-ﬁlm solar cells today show higher efﬁciency than their InP counterparts, both InP and GaAs have similar theoretical maximum efﬁciencies . However, compared to GaAs, InP has signiﬁcantly lower surface recombination velocities [37,38]. To minimize nonradiative recombination losses arising from fabrication surface imperfections of the nanodisks and nonideal bonding to the Si layer, InP is determined as the better candidate for this application. InP/InGaAs multilayer dry etching together with selective wet etching of sacriﬁcial layers can facilitate the production of freestanding InP nanodisks arrays. For bonding InP nanodisk arrays to Si, transfer printing techniques can be used . By choos- ing InP as the material for the nanodisk array, both absorption and antireﬂection properties of the solar cell can be enhanced simultaneously with no need for added antireﬂection coatings. With InP exhibiting absorption in the visible wavelength range, the InP nanodisk array can act not only as an antireﬂective surface but also as a minority carrier generating structure. Adding a transparent conductive front electrode enables active charge extraction from the InP nanodisk array as well as from the bulk Si. In this paper, optical properties of InP nanodisks on an ultra-thin-ﬁlm Si layer of 0.5 μm to 2 μm thicknesses are examined, mainly antireﬂection and scattering, to enhance light absorption within the solar cell. This work is done through numerical simulations of reﬂectance, absorption, and electric ﬁeld distributions, enabling multipole decomposition of the induced electric current density. Optimization of the InP nanodisk array on Si for minimizing reﬂection of incident light and thus maximizing absorption in the structure is done by varying array parameters such as pitch, height and radius. Photonics 2022, 9, 157 3 of 11 2. Materials and Methods 2.1. InP/Si Heterojunction To afﬁrm the suitability of using InP structures on Si for solar cells, the band diagram of the InP/Si heterojunction was calculated using the Lumerical’s CHARGE solver . Figure 1a shows the band diagram of InP/Si has a type-II band alignment. This is suitable for carrier collection in a solar cell, with n-type InP and p-type Si . The conduction band and valence band offsets between undoped InP and Si are calculated to be 0.4 eV and 0.6 eV respectively. Figure 1. (a) Energy band diagram of a InP/Si heterojunction showing the type-II band alignment. Energy levels of the conduction band (Ec), valence band (Ev) and Fermi level (Ef) are depicted by the blue, orange and green lines, respectively. (b) Real and imaginary parts of the refractive indices of InP and Si used in the simulations. 2.2. Simulation All simulations to calculate the reﬂectance, scattering, and absorption properties of the structures were performed using Lumerical 2022 R1 ﬁnite-difference time-domain (FDTD) software . For the simulations on periodic arrays of nanodisks, the boundary conditions were set to periodic in the x and y-directions and to perfectly matching layer (PML) in the z-direction. A plane wave oriented in the negative z-direction was used as a source. Data were collected using 2D frequency-domain ﬁeld and power (FDPD) monitors. A 3D FDPD monitor, along with an index monitor, was used to collect the electrical ﬁeld distributions and refractive indices inside the nanodisk. The electric ﬁeld and refractive index data are then used to evaluate multipole contributions to the total reﬂectance/scattering from the structures. Refractive index data for both InP and Si shown in Figure 1b were taken from the Lumerical database. 2.3. Multipolar Decomposition Scattering of electromagnetic waves from a particle can be described using induced multipolar moments inside the particle. The contribution of the ﬁrst four multipoles to the total scattering cross-section is given by: e m p Q Q total m C = C + C + C + C sca sca sca sca sca k m = j p j + + 6pe E j j a inc (1) 0 13 kQ 1 ab @ A5 kQ + å ab 120 c ab where a, b = x, y, z, p and m are the electric magnetic dipole moments respectively, Q a a ab and Q the electric and magnetic quadrupole moments, respectively. These multipole ab Photonics 2022, 9, 157 4 of 11 moments are evaluated from the simulated data of the electric ﬁelds inside the particle . The forward and backscattering cross sections are deﬁned as [43,44]: jE (j = 0, q = 0)j far s = lim 4pr fw r!¥ jE j inc (2) e m k ik ik d y e m = p + Q Q xz yz 2 c 6 2c 4pe E j j inc and jE (j = 0, q = p)j far s = lim 4pr bw r!¥ jE j inc (3) e m k ik ik d y e m = p + Q Q xz yz c 6 2c 4pe E j j inc where k is the wavenumber and e is the permittivity of the medium surrounding the particle. The backward to forward-scattering ratio (BFR) can be deﬁned as: bw BFR = (4) fw 3. Results 3.1. Optimizing InP Structures on Si for Antireﬂection The antireﬂective layer consists of a hexagonal lattice of InP nanodisks placed on Si. The structure is schematically shown in Figure 2a. The light is vertically incident on the structure with forward-scattering deﬁned into the substrate and backward scattering into air. The effect of size and pitch/period of the array of InP nanodisks on the reﬂectance from the substrate was studied using FDTD simulations. The height (h), radius (r), and the distance between nearest neighbors, i.e., pitch ( p), were used as the varying parameters of the nanodisk array. A wavelength range of 400 nm to 1100 nm was chosen taking into account absorption in both Si and InP. A hexagonal array of nanodisks was used as the basis for the simulations as it can be reproducible in a real-world setting using colloidal lithography and dry etching techniques [45,46]. This also allows for the highest possible packing fraction of nanodisks in a 2D arrangement. However other lattices and nanostructure shapes can also be considered. A wide range parameter sweep consisting of seven heights from 100 nm to 700 nm, 10 pitches from 100 nm to 800 nm and 10 radii from 50 nm to 400 nm, amounting to 700 individual simulations were run to ﬁnd reﬂectance minima. The simulated reﬂectances are weighted with the solar spectrum as: lmax R(l)S(l)dl min R = (5) w R lmax S(l)dl min where R is the weighted reﬂectance, R(l) is the unweighted reﬂectance and S(l) is the AM1.5 solar spectrum. As seen in Figure 2b, the InP nanodisk array parameters pitch: 260 nm, radius: 90 nm and height: 100 nm result in a reﬂectance minimum of 3.1%. The nanodisk array parameters acquired from this wide range sweep were then used as a starting point for a more detailed sweep to ﬁnd the lowest reﬂectance. A minimum weighted reﬂectance of 2.9% resulted from using parameters: height 120 nm, pitch 250 nm and radius80 nm, shown in Figure 2c. For reference the weighted reﬂectance for bulk Si in the same wavelength range is 35.3%. The unweighted reﬂectance of the optimized structures as a function of wavelength is shown in Figure 2d. The structures show broadband antireﬂective properties between 400 nm to 1100 nm. Photonics 2022, 9, 157 5 of 11 Figure 2. Optimization of weighted reﬂectance of InP nanodisks on a Si substrate. (a) Schematic of the structure with relevant array parameters pitch, height, and radius. The incident light is depicted in yellow. A rough optimization shown in (b) and the ﬁnal optimized reﬂectance and nanodisk array parameters shown in (c). All parameters were varied in the sweeps but only the results from the optimized heights are shown. (d) Reﬂectance of the optimized InP nanodisk/Si structure. To understand how the reﬂectance is affected by the change in the radius and the separation of nanodisks, simulations varying these parameters close to the optimized ones were performed. With the height and pitch of the array held constant at 120 nm and 250 nm respectively, the radius was varied from 50 nm to 120 nm. Similarly, the pitch was varied from 170 nm to 600 nm while the array height was kept constant at 120 nm and radius at 82 nm. The results are depicted in Figure 3. Two distinct areas of minimal reﬂectance can be observed in these maps. When the radius is varied, an almost wavelength-independent area of reﬂectance minima can be seen in Figure 3a,b, depicted as A1. This can be accredited to a backward scattering reduction induced by a Mie type resonance in the nanodisks. Another area of minimal reﬂection is depicted as A2 in Figure 3a,b. The reﬂectance minimum red-shifts almost linearly with disk radius (Figure 3a) while it blue-shifts with the period (Figure 3b). As both increasing the radius and decreasing the pitch increase the surface ﬁll factor of the InP nanodisks, this is an indication of index-matching by an effective index layer, consisting of both the indices of the nanodisks and the surrounding air gap, to the Si substrate. Photonics 2022, 9, 157 6 of 11 Figure 3. Reﬂectance of InP nanodisks on a Si substrate as a function of radius (a), pitch (b) and wavelength. A1 shows an area of minimal reﬂectance due to Mie type resonances in the structures and A2 minimal reﬂectance due to the effective refractive index impedance matching. 3.2. Multipole Decomposition of the Optimized Structures To gain further insight on how the Mie resonances affect the antireﬂective properties of the nanodisk array on Si, a multipole decomposition of the induced electric current densities in the structures was studied. To study the resonance contribution to the antireﬂective properties of the nanodisk array placed on a Si substrate, the radius of the nanodisks as well as the array pitch was varied. The multipole decomposition method described in Section 2.3 was used to calculate a backward to forward-scattering ratio with the results presented in Figure 4. In these simulations the static parameters for height, pitch, and radius were chosen as the values for the optimized nanodisk array shown in Figure 2c. The sweep parameters for both pitch and radius were chosen to cover the A1 areas seen in Figure 3a,b. For the nanodisk array, with a pitch of 250 nm and nanodisk height of 120 nm, as the nanodisk radius is varied from 60 nm to 90 nm the BFR shifts slightly towards higher wavelengths and at the same time lowered slightly. Similarly for an array with a nanodisk radius of 80 nm and height of 120 nm, as the pitch of the nanodisks is varied from 200 nm to 350 nm the BFR minima position remains stationary close to 500 nm. By comparing the effects of varying radius and pitch in Figure 4 to the results from reﬂectance radius and pitch sweeps presented in Figure 3, similar effects can be observed. In both cases, we observe a reﬂectance minimum that is almost unaffected by the varying radius and pitch of the nanodisks. The BFR is under 0.6 for the whole wavelength span which indicates that most of the light is scattered towards the Si substrate. This strengthens the assumption that the antireﬂective properties of the nanodisk array indeed are composed of both effects arising from Mie resonances and an effective index-matching of the InP nanodisk array to the Si substrate. Figure 4. The effect on BFR of radius (a) and pitch (b) of the nanodisk array. Suppressed backward scattering can be observed at 550 nm in both (a,b). Variations in radius and pitch show a small effect on the BFR minima position. Photonics 2022, 9, 157 7 of 11 3.3. Thin-Film Effect With the incoming light at vertical incidence, the InP nanodisk/air interface can be modeled as a thin-ﬁlm coating with an effective refractive index n . The n is a volume- e f f e f f weighted average of the refractive indices of the nanodisk material and the surrounding medium and depends on the ﬁll factor of the array. Using Equation (6) the n of a thin e f f ﬁlm equivalent to the nanodisk array can be calculated. n = n f + n (1 f ) (6) e f f s i Here, n is the refractive index of the nanodisk, n the refractive index of the surround- s i ing medium, in our case air (n = 1) and f the ﬁll factor for a hexagonal array of disks given by 2pr f = (7) 3 p where r is the radius of the nanodisk and p is the pitch of the array. A sweep of a 120 nm thick ﬁlm with a varying effective index caused by a variance in the pitch, from 170 nm to 600 nm and radius from 50 nm to 120 nm, of an InP nanodisk array on a Si surface was performed. The results presented in Figure 5 show that the wavelength positions of the reﬂectance minima shift almost linearly when the radius and pitch are changed, similar to the trend observed in Figure 3. These results further strengthen the hypothesis that part of the reﬂectance suppression is caused by an index-matching between the nanodisk array and the substrate. Figure 5. The effect of varying radius (a) and pitch (b) of the reﬂectance of a hexagonal InP array on a Si substrate with a InP nanodisk height of 120 nm. 3.4. Absorption Enhancement in Thin-Film Si Solar Cells by Nanodisk Arrays To optimize the efﬁciency of a Si thin-ﬁlm solar cell it is important that most of the optical power is absorbed in the structure. Therefore, we investigate the absorption in the Si substrate of the InP nanodisk/Si structure at depths above 2 μm. We compare the simulated absorption of the optimized InP nanodisk/Si structure to a plain Si substrate, a Si nanodisk array on a Si substrate with the same parameters as the InP nanodisk array, and a thin-ﬁlm of InP on a Si substrate with a thickness equal to the nanodisk height. The surface of the Si substrate is deﬁned to be at depth 0 and the absorption is measured at 0, 500, 1000, and 2000 nm as shown in Figure 6. Photonics 2022, 9, 157 8 of 11 Figure 6. Absorption simulation setup for nanodisk and thin-ﬁlm structures. The investigated nanodisk arrays and InP thin ﬁlm are depicted in red on top of a bulk Si substrate (black). Absorption of all structures is measured in the Si substrate at depths of 0, 500, 1000 and 2000 nm. The results from the absorption simulations presented in Table 1 show that the opti- mized InP nanodisk/Si structure has the highest absorption at all depths compared to the other structures. At the surface of the Si substrate, the InP nanodisks have absorbed 30.8% of the incoming light compared to 30.5% in the InP thin ﬁlm, even though the InP nanodisk structure has a material ﬁll factor of 40% compared to the thin ﬁlm. This can partly be explained through Mie-resonance enhanced absorption in the InP nanodisks and partly by the antireﬂective properties of the InP nanodisk array, allowing for more light to enter the material. In comparison, a plain 120 nm thick Si slab has an absorption of only 6.9%. At 500 nm into the Si substrate, the InP nanodisk/Si structure has absorbed 47.5% of the in- coming optical power, of which 16.7% is absorbed in Si. At the same depth, the Si nanodisks on Si have a total absorption of 33.5% and the Si below has absorbed 25.2% of the light. The plain Si has absorbed 18.2% at this depth. The higher absorption in the Si nanodisk/Si structure compared to that of the Si slab is mainly due to the antireﬂective properties of the Si nanodisk array. With the parameters used the weighed reﬂectance was 4.9% for the Si nanodisk arrays. At 1 μm the 55% absorption in the InP nanodisk/Si structure is more than 10% higher than in the Si nanodisk/Si structure. Interestingly, at this depth, the Si nanodisk array on Si outperforms the InP thin-ﬁlm/Si structures with absorptions of 44.7% and 40.2% respectively. This can again be explained by the antireﬂective properties of the Si nanodisk array. By reducing the reﬂectance, the Si nanodisk array allows for a higher percentage of transmitted optical power into the Si substrate, leading to higher absorption. The InP nanodisk/Si structure has 7% higher absorption than Si nanodisk/Si at a depth of 2 μm. At depths of 5 μm to 10 μm the difference diminishes as the amount of power absorbed in the Si substrate is predominately a result of the antireﬂective properties of the arrays. The calculated ideal short circuit current density, assuming that every absorbed photon excite an electron-hole pair and all the generated carriers contribute with no recombination losses, 2 2 show an increase from 5.9 mA cm for plain Si to 16.4 mA cm for the InP nanodisk/Si structure at a depth of 500 nm in the Si substrate. Table 1. Absorption in % at different depths in the Si substrate with different structures as top layer. Nanodisk array parameters for all different setups are: radius 80 nm, pitch 250 nm (hexagonal array) and height 120 nm. Absorption Depth [nm] Plain Si InP Thin Film/Si Si Nanodisks/Si Optimized InP Nanodisks/Si 0 0% 30.5% 8.3% 30.8% 500 18.2% 36.9% 33.5% 47.5% 1000 25.9% 40.2% 44.7% 55.0% 2000 34.6% 44.7% 56.7% 63.6% 4. Conclusions In this paper, the potential advantages of using InP nanodisk arrays as both an an- tireﬂective coating and absorption enhancers in a thin-ﬁlm Si solar cell have been studied. Photonics 2022, 9, 157 9 of 11 The antireﬂective and absorption properties of InP nanodisk arrays on a Si substrate have been examined using FDTD simulations and multipole decomposition has been used to study the effect of Mie resonances on the scattering properties of the arrays. A reﬂectance minimum of 2.9% was found for a hexagonal InP nanodisk array on a Si substrate with parameters: height 120 nm, pitch 250 nm and radius 80 nm. Further analysis of the effect of radius and pitch on the reﬂectance of the optimized arrays showed two distinctive areas in the broadband reﬂectance minima. The origin of the antireﬂection was shown to arise from the collective effects of an impedance matching of the nanodisk array to the Si substrate and suppression of backward scattering due to Mie resonances in the InP nanodisks. The absorption properties of InP nanodisks were compared to Si nanodisks with the same structural parameters placed on top of a Si thin ﬁlm. The InP nanodisk-covered Si ﬁlm had a substantially higher absorption at all depths up to 2 μm compared to the Si nanodisk/Si structure. By enhancing the absorption near the surface of the thin-ﬁlm Si solar cell the diffusion path length of created carriers to the depletion region can be reduced thus enhancing carrier collection of the cell. The higher absorption also allows for thinner Si ﬁlms as most of the optical power is absorbed close to the surface of the cell. The ideal short circuit current density of the InP nanodisk/Si structure was also observed to be signiﬁcantly higher compared to that of a plain Si structure. With imperfections in the InP nanodisk surfaces arising from etching processes combined with the uncertain quality of bonding to the Si substrate, recombination losses in the structures are not yet fully clear and will require further study. Although other parameters such as ﬁll factor and external quantum efﬁciency are important for solar cell performance comparisons, they are not in the scope of this paper. Future work is planned for complete device simulations of the InP nanodisk/Si solar cell. The obtained results from this study are promising for thin-ﬁlm InP/Si solar cell applications. Author Contributions: Conceptualization, A.P.R. and S.A.; methodology, M.K. and A.P.R.; Code for multipole decomposition: A.P.R. and M.K.; The manuscript was written by M.K. with feedback from A.P.R. and S.A., and the results were jointly interpreted. All authors have read and agreed to the published version of the manuscript. Funding: This research was funded by the Swedish Research Council—Vetenskapsrådet, grant number 2019-05321, and by the Swedish Energy Agency—Energimyndigheten, grant number 49227-1. Institutional Review Board Statement: Not applicable. Informed Consent Statement: Not applicable. Data Availability Statement: The data presented in this study are available on request from the corresponding author. Conﬂicts of Interest: The authors declare no conﬂict of interest. References 1. Bohren, C.F.; Huffman, D.R. Absorption and Scattering of Light by Small Particles; Wiley Science Series; Wiley: New York, NY, USA, 1983. [CrossRef] 2. National Renewable Energy Laboratory, U.S. Department of Energy. Best Research-Cell Efﬁciency Chart. Available online: https://www.nrel.gov/pv/cell-efﬁciency.html (accessed on 2 July 2020). 3. Nayak, P.K.; Mahesh, S.; Snaith, H.J.; Cahen, D. Photovoltaic solar cell technologies: Analysing the state of the art. Nat. Rev. Mater. 2019, 4, 269–285. [CrossRef] 4. Green, M.A.; Dunlop, E.D.; Hohl-Ebinger, J.; Yoshita, M.; Kopidakis, N.; Ho-Baillie, A.W. Solar cell efﬁciency tables (Version 55). Prog. Photovolt. Res. Appl. 2020, 28, 3–15. [CrossRef] 5. Dross, F.; Baert, K.; Bearda, T.; Deckers, J.; Depauw, V.; El Daif, O.; Gordon, I.; Gougam, A.; Govaerts, J.; Granata, S.; et al. Crystalline thin-foil silicon solar cells: Where crystalline quality meets thin-ﬁlm processing. Prog. Photovolt. Res. Appl. 2012, 20, 770–784. [CrossRef] 6. Meillaud, F.; Boccard, M.; Bugnon, G.; Despeisse, M.; Hänni, S.; Haug, F.J.; Persoz, J.; Schüttauf, J.W.; Stuckelberger, M.; Ballif, C. Recent advances and remaining challenges in thin-ﬁlm silicon photovoltaic technology. Mater. Today 2015, 18, 378–384. [CrossRef] 7. Wang, A.; Zhao, J.; Wenham, S.R.; Green, M.A. 21.5% Efﬁcient thin silicon solar cell. Prog. Photovolt. Res. Appl. 1996, 4, 55–58. [CrossRef] Photonics 2022, 9, 157 10 of 11 8. Jeong, S.; McGehee, M.D.; Cui, Y. All-back-contact ultra-thin silicon nanocone solar cells with 13.7% power conversion efﬁciency. Nat. Commun. 2013, 4, 2950. [CrossRef] 9. Hänni, S.; Bugnon, G.; Parascandolo, G.; Boccard, M.; Escarré, J.; Despeisse, M.; Meillaud, F.; Ballif, C. High-efﬁciency microcrystalline silicon single-junction solar cells. Prog. Photovolt. Res. Appl. 2013, 21, 821–826. [CrossRef] 10. Depauw, V.; Trompoukis, C.; Massiot, I.; Chen, W.; Dmitriev, A.; Cabarrocas, P.R.i.; Gordon, I.; Poortmans, J. Sunlight-thin nanophotonic monocrystalline silicon solar cells. Nano Futures 2017, 1, 021001. [CrossRef] 11. Lee, S.H.; Lee, I.; Yi, J. Silicon nitride ﬁlms prepared by high-density plasma chemical vapor deposition for solar cell applications. Surf. Coat. Technol. 2022, 153, 67–71. [CrossRef] 12. Zhao, J.; Green, M. Optimized antireﬂection coatings for high-efﬁciency silicon solar cells. IEEE Trans. Electron Devices 1991, 38, 1925–1934. [CrossRef] 13. Macdonald, D.H.; Cuevas, A.; Kerr, M.J.; Samundsett, C.; Ruby, D.; Winderbaum, S.; Leo, A. Texturing industrial multicrystalline silicon solar cells. Sol. Energy 2004, 76, 277–283. [CrossRef] 14. Winderbaum, S.; Reinhold, O.; Yun, F. Reactive ion etching (RIE) as a method for texturing polycrystalline silicon solar cells. Sol. Energy Mater. Sol. Cells 1997, 46, 239–248. [CrossRef] 15. Atwater, H.A.; Polman, A. Plasmonics for improved photovoltaic devices. Nat. Mater. 2010, 9, 205–213. [CrossRef] [PubMed] 16. Baryshnikova, K.V.; Petrov, M.I.; Babicheva, V.E.; Belov, P.A. Plasmonic and silicon spherical nanoparticle antireﬂective coatings. Sci. Rep. 2016, 6, 22136. [CrossRef] [PubMed] 17. Deng, Y.; Cao, G.; Yang, H.; Zhou, X.; Wu, Y. Dynamic Control of Double Plasmon-Induced Transparencies in Aperture-Coupled Waveguide-Cavity System. Plasmonics 2018, 13, 345–352. [CrossRef] 18. Zheng, Z.; Zheng, Y.; Luo, Y.; Yi, Z.; Zhang, J.; Liu, Z.; Yang, W.; Yu, Y.; Wu, X.; Wu, P. A switchable terahertz device combining ultra-wideband absorption and ultra-wideband complete reﬂection. Phys. Chem. Chem. Phys. 2022, 24, 2527–2533. [CrossRef] 19. van Lare, C.; Lenzmann, F.; Verschuuren, M.A.; Polman, A. Dielectric Scattering Patterns for Efﬁcient Light Trapping in Thin-Film Solar Cells. Nano Lett. 2015, 15, 4846–4852. [CrossRef] 20. Daqiqeh Rezaei, S.; Dong, Z.; You En Chan, J.; Trisno, J.; Ng, R.J.H.; Ruan, Q.; Qiu, C.W.; Mortensen, N.A.; Yang, J.K. Nanophotonic Structural Colors. ACS Photonics 2021, 8, 18–33. [CrossRef] 21. Yang, W.; Xiao, S.; Song, Q.; Liu, Y.; Wu, Y.; Wang, S.; Yu, J.; Han, J.; Tsai, D.P. All-dielectric metasurface for high-performance structural color. Nat. Commun. 2020, 11, 1864. [CrossRef] 22. Cai, J.; Qi, L. Recent advances in antireﬂective surfaces based on nanostructure arrays. Mater. Horizons 2014, 2, 37–53. [CrossRef] 23. Peter Amalathas, A.; Alkaisi, M.M. Nanostructures for Light Trapping in Thin Film Solar Cells. Micromachines 2019, 10, 619. [CrossRef] [PubMed] 24. Adibzadeh, F.; Olyaee, S. Plasmonic Enhanced InP Nanowire Array Solar Cell through Optoelectronic Modeling. Photonics 2021, 8, 90. [CrossRef] 25. Raj, V.; Rougieux, F.; Fu, L.; Tan, H.H.; Jagadish, C. Design of Ultrathin InP Solar Cell Using Carrier Selective Contacts. IEEE J. Photovolt. 2020, 10, 1657–1666. [CrossRef] 26. Yin, X.; Battaglia, C.; Lin, Y.; Chen, K.; Hettick, M.; Zheng, M.; Chen, C.Y.; Kiriya, D.; Javey, A. 19.2% Efﬁcient InP Heterojunction Solar Cell with Electron-Selective TiO Contact. ACS Photonics 2014, 1, 1245–1250. [CrossRef] [PubMed] 27. Yamaguchi, M.; Yamamoto, A.; Uchida, N.; Uemura, C. A new approach for thin ﬁlm InP solar cells. Sol. Cells 1986, 19, 85–96. [CrossRef] 28. Kroemer, H.; Liu, T.Y.; Petroff, P.M. GaAs on Si and related systems: Problems and prospects. J. Cryst. Growth 1989, 95, 96–102. [CrossRef] 29. Sugo, M.; Takanashi, Y.; Al-jassim, M.M.; Yamaguchi, M. Heteroepitaxial growth and characterization of InP on Si substrates. J. Appl. Phys. 1990, 68, 540–547. [CrossRef] 30. Shimizu, Y.; Okada, Y. Growth of high-quality GaAs/Si ﬁlms for use in solar cell applications. J. Cryst. Growth 2004, 265, 99–106. [CrossRef] 31. Lourdudoss, S. Heteroepitaxy and selective area heteroepitaxy for silicon photonics. Curr. Opin. Solid State Mater. Sci. 2012, 16, 91–99. [CrossRef] 32. Tanabe, K.; Watanabe, K.; Arakawa, Y. III-V/Si hybrid photonic devices by direct fusion bonding. Sci. Rep. 2012, 2, 349. [CrossRef] 33. Roelkens, G.; Liu, L.; Liang, D.; Jones, R.; Fang, A.; Koch, B.; Bowers, J. III-V/silicon photonics for on-chip and intra-chip optical interconnects. Laser Photonics Rev. 2010, 4, 751–779. [CrossRef] 34. Pantzas, K.; Itawi, A.; Sagnes, I.; Patriarche, G.; Le Bourhis, E.; Lupu, A.; Benisty, H.; Talneau, A. Oxide-Free Bonding of III-V-Based Material on Silicon and Nano-Structuration of the Hybrid Waveguide for Advanced Optical Functions. Photonics 2015, 2, 1054–1064. [CrossRef] 35. Pasquariello, D.; Camacho, M.; Hjort, K.; Dózsa, L.; Szentpáli, B. Evaluation of InP-to-silicon heterobonding. Mater. Sci. Eng. B 2001, 80, 134–137. [CrossRef] 36. Rühle, S. Tabulated values of the Shockley–Queisser limit for single junction solar cells. Sol. Energy 2016, 130, 139–147. [CrossRef] 37. Hoffman, C.A.; Gerritsen, H.J.; Nurmikko, A.V. Study of surface recombination in GaAs and InP by picosecond optical techniques. J. Appl. Phys. 1980, 51, 1603–1604. [CrossRef] 38. Nolte, D.D. Surface recombination, free-carrier saturation, and dangling bonds in InP and GaAs. Solid-State Electron. 1990, 33, 295–298. [CrossRef] Photonics 2022, 9, 157 11 of 11 39. Naureen, S.; Shahid, N.; Dev, A.; Anand, S. Generation of substrate-free III–V nanodisks from user-deﬁned multilayer nanopillar arrays for integration on Si. Nanotechnology 2013, 24, 225301. [CrossRef] 40. Lumerical FDTD Solutions. Available online: https://www.lumerical.com/ (accessed on 13 September 2020). 41. Sze, S.M.; Ng, K.K. p-n Junctions. In Physics of Semiconductor Devices; John Wiley & Sons, Ltd.: Hoboken, NJ, USA, 2006; pp. 124–129. [CrossRef] 42. Alaee, R.; Rockstuhl, C.; Fernandez-Corbaton, I. An electromagnetic multipole expansion beyond the long-wavelength approxi- mation. Opt. Commun. 2018, 407, 17–21. [CrossRef] 43. Alaee, R.; Filter, R.; Lehr, D.; Lederer, F.; Rockstuhl, C. A generalized Kerker condition for highly directive nanoantennas. Opt. Lett. 2015, 40, 2645–2648. [CrossRef] 44. Pors, A.; Andersen, S.K.H.; Bozhevolnyi, S.I. Unidirectional scattering by nanoparticles near substrates: Generalized Kerker conditions. Opt. Express 2015, 23, 28808–28828. [CrossRef] 45. Naureen, S.; Sanatinia, R.; Shahid, N.; Anand, S. High Optical Quality InP-Based Nanopillars Fabricated by a Top-Down Approach. Nano Lett. 2011, 11, 4805–4811. [CrossRef] [PubMed] 46. Zhang, C.; Cvetanovic, S.; Pearce, J.M. Fabricating ordered 2-D nano-structured arrays using nanosphere lithography. MethodsX 2017, 4, 229–242. [CrossRef] [PubMed]
Multidisciplinary Digital Publishing Institute
Enhanced Absorption in InP Nanodisk Arrays on Ultra-Thin-Film Silicon for Solar Cell Applications
Ravishankar, Ajith Padyana
, Volume 9 (3) –
Mar 5, 2022