Thick Film Superconductors Based on Bi2O3 Modified YBaCuO and BiSrCaCuO Systems

Thick Film Superconductors Based on Bi2O3 Modified YBaCuO and BiSrCaCuO Systems A superconducting material with a composition Y1xBa2Cu3O732x x2 Bi2O3 x 01 and 02 was synthesised. The influence of Bi2O3 additions on sintering was studied. Preliminary investigations of the BiSrCaCuO system were also made. Thick film pastes, prepared from Y1xBixBa2Cu3O7 compositions, from the compound YBa2Cu3O7 with 10 wo addition of Bi2CuO4 and from two compositions in the BiSrCaCu0 system, were fired on Al2O3 and ZrO2 substrates. All thick film materials based on YBa2Cu3O7 compound were superconducting at temperatures above 77 K when fired on ZrO2 substrates, while only a material with the starting composition Y08Ba2Cu3O6.7 01 Bi2O3 reached zero resistivity above 77 K on Al2O3 substrates. Tc onset of samples based on the YBa2Cu3O7 compound was around 95 K, and of samples from the BiSrCaCuO system between 95 and 100 K. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Microelectronics International Emerald Publishing

Thick Film Superconductors Based on Bi2O3 Modified YBaCuO and BiSrCaCuO Systems

Loading next page...
 
/lp/emerald-publishing/thick-film-superconductors-based-on-bi2o3-modified-ybacuo-and-tSDZgNqTP7
Publisher
Emerald Publishing
Copyright
Copyright © Emerald Group Publishing Limited
ISSN
1356-5362
DOI
10.1108/eb044364
Publisher site
See Article on Publisher Site

Abstract

A superconducting material with a composition Y1xBa2Cu3O732x x2 Bi2O3 x 01 and 02 was synthesised. The influence of Bi2O3 additions on sintering was studied. Preliminary investigations of the BiSrCaCuO system were also made. Thick film pastes, prepared from Y1xBixBa2Cu3O7 compositions, from the compound YBa2Cu3O7 with 10 wo addition of Bi2CuO4 and from two compositions in the BiSrCaCu0 system, were fired on Al2O3 and ZrO2 substrates. All thick film materials based on YBa2Cu3O7 compound were superconducting at temperatures above 77 K when fired on ZrO2 substrates, while only a material with the starting composition Y08Ba2Cu3O6.7 01 Bi2O3 reached zero resistivity above 77 K on Al2O3 substrates. Tc onset of samples based on the YBa2Cu3O7 compound was around 95 K, and of samples from the BiSrCaCuO system between 95 and 100 K.

Journal

Microelectronics InternationalEmerald Publishing

Published: Feb 1, 1989