High temperature oxidation behaviour of nickel aluminide coated mild steel

High temperature oxidation behaviour of nickel aluminide coated mild steel Nickel aluminide coatings on mild steel have been prepared by pack cementation process. The high temperature oxidation behaviour of the coatings have been studied at 750, 800 and 850 in flowing air. The influence of different rare earth oxide addition on the oxidation rates of nickel aluminide coating on mild steel has also been investigated. The kinetic of the oxidation of nickel aluminide coating on mild steel, with or without addition of RE2O3 proceeds by a diffusion controlled mechanism as revealed by the parabolic nature of weight gain Vs time plots. At higher temperatures the oxidation rates of the nickel aluminide coatings are lowered down markedly irrespective of rare earth oxide concentration. The oxidation rates are significantly affected by the morphology of the oxide scales, in cases where the structure of oxide scales is not seriously disrupted due to decarburization, the oxidation rates are significantly reduced. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Anti-Corrosion Methods and Materials Emerald Publishing

High temperature oxidation behaviour of nickel aluminide coated mild steel

Loading next page...
 
/lp/emerald-publishing/high-temperature-oxidation-behaviour-of-nickel-aluminide-coated-mild-k0dRCYFh06
Publisher
Emerald Publishing
Copyright
Copyright © Emerald Group Publishing Limited
ISSN
0003-5599
DOI
10.1108/eb007297
Publisher site
See Article on Publisher Site

Abstract

Nickel aluminide coatings on mild steel have been prepared by pack cementation process. The high temperature oxidation behaviour of the coatings have been studied at 750, 800 and 850 in flowing air. The influence of different rare earth oxide addition on the oxidation rates of nickel aluminide coating on mild steel has also been investigated. The kinetic of the oxidation of nickel aluminide coating on mild steel, with or without addition of RE2O3 proceeds by a diffusion controlled mechanism as revealed by the parabolic nature of weight gain Vs time plots. At higher temperatures the oxidation rates of the nickel aluminide coatings are lowered down markedly irrespective of rare earth oxide concentration. The oxidation rates are significantly affected by the morphology of the oxide scales, in cases where the structure of oxide scales is not seriously disrupted due to decarburization, the oxidation rates are significantly reduced.

Journal

Anti-Corrosion Methods and MaterialsEmerald Publishing

Published: Jul 1, 1991