The main target of this paper is to investigate the effect of peak stress at the extremities of the adhesive layer of a bonded assembly subjected to dynamic shear impact. It is known, that under both static and dynamic loadings such joints endure at their extremities high level of stresses, an aspect known as edge effects. Double lap joint assembly was considered with unidirectional carbon–epoxy substrates and Araldite 2031 adhesive. To quantify this edge effect, a specific coefficient, named coefficient of stress concentration was defined: it is the ratio of the maximum shear stress to the average shear stress. This coefficient helps to calculate maximum strength of the joint since experimentally, only average shear stress could be measured. A numerical analysis at the midplane of the joint was carried out to investigate the effect of geometrical and material parameters on this stress concentration factor. It was found that this factor is constant with the time once the equilibrium is established. Moreover, this stress concentration coefficient decreases with higher Young's modulus of the adherents, lower Young's modulus of the adhesive, thicker and shorter adhesive layer. A unified parameter involving geometrical and mechanical parameters of the specimen was established to quantify this stress concentration factor.
International Journal of Adhesion and Adhesives – Elsevier
Published: Dec 1, 2015
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera