The frequency and severity of scuffing in automotive engines has the potential to increase due to new low-viscosity lubricants for fuel efficiency and increased cylinder power output. This work is to understand the fundamental causes and events resulting in piston ring and liner scuffing. A TE-77 high frequency reciprocating tribometer was used with a synthetic PAO base oil (4cSt) to reciprocate a 52100 G5 barrel against a ground pearlitic Grade 250 grey cast iron.Samples were run-in at 50N and 10Hz prior to a temperature ramp to 150°C followed by a discreet load ramp to 1kN (0.49GPa). The tests were terminated when a sharp increase in the average friction force was observed indicating that scuffing had occurred. 3D optical profilometry showed that the scuffed cast iron surface consisted of smeared platelets and craters of 35μm depth. SEM and EDX analyses suggested adhesive transfer of cast iron material to the counter-surface was occurring by failure along lamellar graphite interfaces. Tests were repeated using instantaneous high-speed friction data and indicated that micro-scuffing initiated at a load of 620N. Focused ion beam cross-sections of the mildly scuffed surface confirmed the mechanism of sub-surface crack initiation occurring along lamellar graphite boundaries.
Wear – Elsevier
Published: May 1, 2015
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera