In-situ, non-destructive acoustic characterization of solid state electrolyte cells

In-situ, non-destructive acoustic characterization of solid state electrolyte cells Solid-state electrolytes such as cubic Li6.25Al0.25La3Zr2O12 (LLZO) can enable solid-state batteries, metallic lithium anodes and higher voltage cathodes. However, the stability of cubic LLZO is affected by current density. In beta alumina solid electrolyte, microstructural failure was caused by Na dendrite penetration, and was shown to be a function of the fracture toughness, KIC. The relationship between dendrite penetration and KIC indicates electronic failure is related to creation of microstructural damage, and the microstructural damage may be used as an indicator of imminent electronic failure. To monitor microstructural damage during cycling, we developed a non-invasive, in-situ cell monitoring apparatus to help to correlate mechanical stability with Li-ion current density in LLZO. A pulse-echo transducer was integrated into all solid-state Li-LLZO-Li cells. The capability enables the characterization of microscopic inhomogeneities through the careful measurement of changes to the elastic moduli. The elastic moduli and fracture toughness have been previously reported for dense (>99%) specimens, but monitoring of the relative change in moduli during cycling has not been explored. In this study, an acoustic monitoring method is presented to monitor LLZO specimens during cycling. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Journal of Power Sources Elsevier

In-situ, non-destructive acoustic characterization of solid state electrolyte cells

Loading next page...
 
/lp/elsevier/in-situ-non-destructive-acoustic-characterization-of-solid-state-THassFzG4a
Publisher
Elsevier
Copyright
Copyright © 2016 Elsevier B.V.
ISSN
0378-7753
D.O.I.
10.1016/j.jpowsour.2016.05.062
Publisher site
See Article on Publisher Site

Abstract

Solid-state electrolytes such as cubic Li6.25Al0.25La3Zr2O12 (LLZO) can enable solid-state batteries, metallic lithium anodes and higher voltage cathodes. However, the stability of cubic LLZO is affected by current density. In beta alumina solid electrolyte, microstructural failure was caused by Na dendrite penetration, and was shown to be a function of the fracture toughness, KIC. The relationship between dendrite penetration and KIC indicates electronic failure is related to creation of microstructural damage, and the microstructural damage may be used as an indicator of imminent electronic failure. To monitor microstructural damage during cycling, we developed a non-invasive, in-situ cell monitoring apparatus to help to correlate mechanical stability with Li-ion current density in LLZO. A pulse-echo transducer was integrated into all solid-state Li-LLZO-Li cells. The capability enables the characterization of microscopic inhomogeneities through the careful measurement of changes to the elastic moduli. The elastic moduli and fracture toughness have been previously reported for dense (>99%) specimens, but monitoring of the relative change in moduli during cycling has not been explored. In this study, an acoustic monitoring method is presented to monitor LLZO specimens during cycling.

Journal

Journal of Power SourcesElsevier

Published: Aug 30, 2016

References

You’re reading a free preview. Subscribe to read the entire article.


DeepDyve is your
personal research library

It’s your single place to instantly
discover and read the research
that matters to you.

Enjoy affordable access to
over 12 million articles from more than
10,000 peer-reviewed journals.

All for just $49/month

Explore the DeepDyve Library

Unlimited reading

Read as many articles as you need. Full articles with original layout, charts and figures. Read online, from anywhere.

Stay up to date

Keep up with your field with Personalized Recommendations and Follow Journals to get automatic updates.

Organize your research

It’s easy to organize your research with our built-in tools.

Your journals are on DeepDyve

Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.

All the latest content is available, no embargo periods.

See the journals in your area

DeepDyve Freelancer

DeepDyve Pro

Price
FREE
$49/month

$360/year
Save searches from
Google Scholar,
PubMed
Create lists to
organize your research
Export lists, citations
Read DeepDyve articles
Abstract access only
Unlimited access to over
18 million full-text articles
Print
20 pages/month
PDF Discount
20% off