In the present work we focus on the mechanisms involved in Ti2AlC MAX phase thin-film formation. The TiAl2 thin-film was deposited by magnetron sputtering on a SiC-4H  substrate. Samples were annealed at various temperatures (700–800°C) for various times and analysed by XRD and TEM. The epitaxial Ti2AlC phase was formed as follows: MAX//SiC and (11−20)MAX//(11–20)SiC which is in a good agreement with thermodynamic considerations. The presence of TiC structures at the interface indicates that the formation of this structure is necessary to obtain Ti2AlC. Moreover, the formation of a liquid AlSi alloy was highlighted due to the interdiffusion of Al and Si respectively from TiAl2 and SiC during TiC formation. Finally, we assume that, during the cooling, the AlSi alloy separates and Al diffuses to the surface of the TiAl2 layer leading to the formation of an Al-rich layer. The remaining Si reacts with Ti from TiAl2 to form a Ti5Si3 layer following this epitaxial relation: Ti2AlC//Ti5Si3 and (11–20)Ti2AlC//(3−210)Ti5Si3. These mechanisms lead to the stacking of four different layers. Between 700 and 800°C, the nature of the formation mechanism is not time-dependent. However, the kinetics of the reactions are both temperature and time dependent.
Materials & design – Elsevier
Published: Apr 15, 2018
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.
All for just $49/month
Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly
Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.
Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera