The polycrystalline sample of KMgPO4:Tb3+(KMPT) phosphor was successfully synthesized by using solid state method. The X-ray powder diffraction, photoluminescence (PL) emission and excitation spectra, thermoluminescence (TL) and optically stimulated luminescence (OSL) were thoroughly measured. The PL spectra of as-prepared KMPT phosphor showed characteristic blue-green emission, when excited by 226nm under UV excitation. The optimum PL intensity was observed at 0.01mol concentration of Tb3+ions and this phosphor used for remaining studies. The TL glow curve of KMPT phosphor consist two characterized peaks, which were deconvoluted and the kinetic parameters i.e. trap depth or activation energy, order of kinetic and frequency factor determined by using peak shape method. TL sensitivity of KMPT phosphors was found to be 10% than that of TL sensitivity of TLD-500 phosphor. The OSL sensitivity of KMPT was 0.92 times than OSL sensitivity of α-Al2O3:C phosphor. The OSL decay curve KMPT phosphor consist of three component having photoionization cross sections were found to be 0.26548×10−17, 0.220×10−17, 2.92×10−17 cm2. The KMPT phosphor showed linear dose response in range 100–6000mGy and fading of KMPT phosphor was found to be 31% in 15 days. The Minimum detectable dose (MDD) was found to be 0.39mGy with corresponding 3σ back ground. The phosphor shows good dosimetry properties such as sensitivity, dose response, MDD, Fading.
Journal of Luminescence – Elsevier
Published: Aug 1, 2016
It’s your single place to instantly
discover and read the research
that matters to you.
Enjoy affordable access to
over 12 million articles from more than
10,000 peer-reviewed journals.
All for just $49/month
Read as many articles as you need. Full articles with original layout, charts and figures. Read online, from anywhere.
Keep up with your field with Personalized Recommendations and Follow Journals to get automatic updates.
It’s easy to organize your research with our built-in tools.
Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.
All the latest content is available, no embargo periods.
“Hi guys, I cannot tell you how much I love this resource. Incredible. I really believe you've hit the nail on the head with this site in regards to solving the research-purchase issue.”Daniel C.
“Whoa! It’s like Spotify but for academic articles.”@Phil_Robichaud
“I must say, @deepdyve is a fabulous solution to the independent researcher's problem of #access to #information.”@deepthiw
“My last article couldn't be possible without the platform @deepdyve that makes journal papers cheaper.”@JoseServera