The influence of morphology on the (hydrolytic degradation of as-polymerized and hot-drawn poly(L-lactide))
The influence of morphology on the (hydrolytic degradation of as-polymerized and hot-drawn...
Joziasse, C. A. P.; Grijpma, D. W.; Bergsma, J. E.; Cordewener, F. W.; Bos, R. R. M.; Pennings, A. J.
1998-11-27 00:00:00
The influence of morpho-logy on the hydrolytic degradation behavior of poly(L-lactide) has been studied. High molecular weight and highly crystalline as-polymerized poly(L-lactide) was obtained in high yields through melt polymerization. Poly(L-lactide) fiber with a draw ratio of 5.6 was obtained by hot-drawing solution-spun fiber.
http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.pngColloid Polymer ScienceSpringer Journalshttp://www.deepdyve.com/lp/springer-journals/the-influence-of-morphology-on-the-hydrolytic-degradation-of-as-GQ5MxCGgpv
The influence of morphology on the (hydrolytic degradation of as-polymerized and hot-drawn poly(L-lactide))
Chemistry; Polymer Sciences; Soft and Granular Matter, Complex Fluids and Microfluidics; Characterization and Evaluation of Materials; Physical Chemistry; Food Science; Nanotechnology and Microengineering
The influence of morpho-logy on the hydrolytic degradation behavior of poly(L-lactide) has been studied. High molecular weight and highly crystalline as-polymerized poly(L-lactide) was obtained in high yields through melt polymerization. Poly(L-lactide) fiber with a draw ratio of 5.6 was obtained by hot-drawing solution-spun fiber.