The effect of delignification on the properties of cellulosic fiber material

The effect of delignification on the properties of cellulosic fiber material AbstractThe behavior of pressed poplar chemi-thermomechanical pulping (CTMP) without additive the focus of our study. Four CTMPs with decreasing lignin contents were prepared by the sodium chlorite/acetic acid method and the holocellulose, α-cellulose, pentosan and Klason lignin contents of the delignified CTMPs were determined. The surface composition, aggregation structure and microstructure of the delignified fibers were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM), and the mechanical properties of the fiber material were investigated by means of tensile and bending tests. As shown by XPS, the lignin content of the Pr-CTMP surface layer firstly increased and then decreased as the lignin content of CTMP decreased. With the delignification time increased from 0 to 240 min, the crystallinity index (CrI) of CTMP increased from 60.1% to 65.7%. The CrI of all CTMPs at different delignification degrees showed significant elevated values after hot-pressing. The fiber cell wall became thinner and the cells were flattened and thus elevated the contact area among fibers and, as a consequence, the density of material gradually increased at higher delignification degrees. The tensile strength increased by ca. 10%, when the lignin content decreased from 24.9% to 13.1%, and by ca. 53%, when the lignin content decreased from 13.1% to nearly zero. The bending strength increased with increasing delignification. When the removal rate of lignin increased from 47% to 54%, the bending strength increased from 101 to 122 MPa. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Holzforschung de Gruyter

The effect of delignification on the properties of cellulosic fiber material

Loading next page...
 
/lp/degruyter/the-effect-of-delignification-on-the-properties-of-cellulosic-fiber-SwW07xt1lS
Publisher
de Gruyter
Copyright
©2018 Walter de Gruyter GmbH, Berlin/Boston
ISSN
1437-434X
eISSN
1437-434X
D.O.I.
10.1515/hf-2017-0183
Publisher site
See Article on Publisher Site

Abstract

AbstractThe behavior of pressed poplar chemi-thermomechanical pulping (CTMP) without additive the focus of our study. Four CTMPs with decreasing lignin contents were prepared by the sodium chlorite/acetic acid method and the holocellulose, α-cellulose, pentosan and Klason lignin contents of the delignified CTMPs were determined. The surface composition, aggregation structure and microstructure of the delignified fibers were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM), and the mechanical properties of the fiber material were investigated by means of tensile and bending tests. As shown by XPS, the lignin content of the Pr-CTMP surface layer firstly increased and then decreased as the lignin content of CTMP decreased. With the delignification time increased from 0 to 240 min, the crystallinity index (CrI) of CTMP increased from 60.1% to 65.7%. The CrI of all CTMPs at different delignification degrees showed significant elevated values after hot-pressing. The fiber cell wall became thinner and the cells were flattened and thus elevated the contact area among fibers and, as a consequence, the density of material gradually increased at higher delignification degrees. The tensile strength increased by ca. 10%, when the lignin content decreased from 24.9% to 13.1%, and by ca. 53%, when the lignin content decreased from 13.1% to nearly zero. The bending strength increased with increasing delignification. When the removal rate of lignin increased from 47% to 54%, the bending strength increased from 101 to 122 MPa.

Journal

Holzforschungde Gruyter

Published: Jun 27, 2018

There are no references for this article.

You’re reading a free preview. Subscribe to read the entire article.


DeepDyve is your
personal research library

It’s your single place to instantly
discover and read the research
that matters to you.

Enjoy affordable access to
over 18 million articles from more than
15,000 peer-reviewed journals.

All for just $49/month

Explore the DeepDyve Library

Search

Query the DeepDyve database, plus search all of PubMed and Google Scholar seamlessly

Organize

Save any article or search result from DeepDyve, PubMed, and Google Scholar... all in one place.

Access

Get unlimited, online access to over 18 million full-text articles from more than 15,000 scientific journals.

Your journals are on DeepDyve

Read from thousands of the leading scholarly journals from SpringerNature, Elsevier, Wiley-Blackwell, Oxford University Press and more.

All the latest content is available, no embargo periods.

See the journals in your area

DeepDyve

Freelancer

DeepDyve

Pro

Price

FREE

$49/month
$360/year

Save searches from
Google Scholar,
PubMed

Create lists to
organize your research

Export lists, citations

Read DeepDyve articles

Abstract access only

Unlimited access to over
18 million full-text articles

Print

20 pages / month

PDF Discount

20% off