AU - Yeung, King
AB - JOURNAL OF MATERIALS SCIENCE 39 (2 004) 5603 – 5605 L E T T E R S Preparation of composite carbon–zeolite membranes using a simple method XIONGFU ZHANG, TONGHUA WANG, HAIOU LIU Institute of Adsorption and Inorganic Membrane, School of Chemical Engineering, Dalian Univeristy of Technology, Dalian 116012, People’s Republic of China E-mail: xfzhang@dlut.edu.cn; membrane@chem.dlut.edu.cn KING LUN YEUNG Department of Chemical Engineering, The Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong, SAR, People’s Republic of China Zeolite thin films and composites supported on differ- pared at Dalian University of Technology have 9 mm ent materials have been widely used as highly selec- OD, 5 mm ID, 75 mm long, and a nominal pore size tive membrane separators, membrane reactors, chemi- of 0.3 µm. Prior to use, the tubes were rinsed with cal sensors, and microdevices [1–11]. In particular, ze- DDI water and then dried at 393 K for 10 hr. A thin olite membranes supported on polymers and ceramics layer of zeolite seeds was coated onto the inner surface as supports are universally studied. However, polymers of the tubes using a slip-casting technique in 1wt% are vulnerable to organic solvents and could not tolerate 
TI - Preparation of composite carbon-zeolite membranes using a simple method
JF - Journal of Materials Science
DO - 10.1023/B:JMSC.0000039299.76924.82
DA - 2004-10-14
UR - https://www.deepdyve.com/lp/springer-journals/preparation-of-composite-carbon-zeolite-membranes-using-a-simple-p7KN8ssXBX
SP - 5603
EP - 5605
VL - 39
IS - 17
DP - DeepDyve
ER -