Experimental investigation into the adherence of novel coating of auto-catalyst on cordierite supports
Abstract
<jats:sec>
<jats:title content-type="abstract-subheading">Purpose</jats:title>
<jats:p>A structural and textural characterization study has been performed to investigate the adherence of zeolite-based catalyst washcoated onto honey-comb-type cordierite monoliths. The supports were characterized by the scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS), X-ray diffraction (XRD) and Brunauer–Emmett–Teller (BET) techniques.</jats:p>
</jats:sec>
<jats:sec>
<jats:title content-type="abstract-subheading">Design/methodology/approach</jats:title>
<jats:p>SEM/EDS provided quantitative estimate of the washcoated monolith as the elemental composition of catalyst coating. The XRD pattern deduced that the zeolite-based catalysts were successfully mounted on the cordierite support, showing the characteristic peaks of zeolites (Zeolite Socony Mobil–5; ZSM-5) at Braggs angles of 7.88°, 8.76°, 23.04°, 23.88° and 24.36°, whereas the characteristic peak of cordierite is seen at a Braggs angle of 10.44°.</jats:p>
</jats:sec>
<jats:sec>
<jats:title content-type="abstract-subheading">Findings</jats:title>
<jats:p>The BET results proved that a monolayer of zeolite may serve the need for surface area and porosity. This was evident in the increase of surface area of washcoated support as against the bare support. The obtained isotherms were of Type IV, illustrating the presence of mesopores. The adsorption and desorption isotherm branches coincided over the interval 0 < P/P0 < 0.50 and 0 < P/P0 < 0.45, showing N<jats:sub>2</jats:sub> reversible adsorption for the two samples, respectively.</jats:p>
</jats:sec>
<jats:sec>
<jats:title content-type="abstract-subheading">Originality/value</jats:title>
<jats:p>It was concluded that the composite materials which are ZSM-5 (Si/Al = 25) and precursors of the transition salts of copper, zinc and ceria powders were deposited on the catalyst supports, establishing the success of the coating procedure relative to the adherence of the catalyst compositions on the ceramic support.</jats:p>
</jats:sec>