Effect fracture resistance on retardation of crack growth

Effect fracture resistance on retardation of crack growth Purpose – The prediction of fatigue crack growth behaviour is an important part of damage tolerance analyses. Recently, the author’s work has focused on evaluating the FASTRAN retardation model. This model is implemented in the AFGROW code, which allows different retardation models to be compared. The primary advantage of the model is that all input parameters, including those for an initial plane-strain state and its transition to a plane-stress-state, are objectively measured using standard middle-crack-tension M(T) specimens. The purpose of this paper is to evaluate the ability of the FASTRAN model to predict correct retardation effects due to high loading peaks that occur during variable amplitude loading in sequences representative of an aircraft service. Design/methodology/approach – This paper addresses pre-setting of the fracture toughness K R (based on J -integral J Q according to ASTM1820) in the FASTRAN retardation model. A set of experiments were performed using specimens made from a 7475-T7351 aluminium alloy plate. Loading sequences with peaks ordered in ascending-descending blocks were used. The effect of truncating and clipping selected load levels on crack propagation behaviour was evaluated using both experimental data and numerical analyses. The findings were supported by the results of a fractographic analysis. Findings – Fatigue crack propagation data defined using M(T) specimens made from Al 7475-T7351 alloy indicate the difficulty of evaluating the following two events simultaneously: fatigue crack increments after application of loads with maximum amplitudes that exceeded J Q and subcritical crack increments caused by loads at high stress intensity factors. An effect of overloading peaks with a maximum that exceeds J Q should be assessed using a special analysis beyond the scope of the FASTRAN retardation model. Originality/value – Measurements of fatigue crack growth on specimens made from 7475 T7351 aluminium alloy were carried out. The results indicated that simultaneously evaluating fatigue crack increments after application of the load amplitude above J Q and subcritical increments caused by the loads at high stress intensity factors is difficult. Experiments demonstrated that if the fatigue crack reaches a specific length, the maximal amplitude load induces considerable crack growth retardation. http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png International Journal of Structural Integrity Emerald Publishing

Effect fracture resistance on retardation of crack growth

Download PDF
12 pages

Loading next page...
 
/lp/emerald-publishing/effect-fracture-resistance-on-retardation-of-crack-growth-JX0a3Abewp

References (8)

Publisher
Emerald Publishing
Copyright
Copyright © Emerald Group Publishing Limited
ISSN
1757-9864
DOI
10.1108/IJSI-10-2014-0053
Publisher site
See Article on Publisher Site

Abstract

Purpose – The prediction of fatigue crack growth behaviour is an important part of damage tolerance analyses. Recently, the author’s work has focused on evaluating the FASTRAN retardation model. This model is implemented in the AFGROW code, which allows different retardation models to be compared. The primary advantage of the model is that all input parameters, including those for an initial plane-strain state and its transition to a plane-stress-state, are objectively measured using standard middle-crack-tension M(T) specimens. The purpose of this paper is to evaluate the ability of the FASTRAN model to predict correct retardation effects due to high loading peaks that occur during variable amplitude loading in sequences representative of an aircraft service. Design/methodology/approach – This paper addresses pre-setting of the fracture toughness K R (based on J -integral J Q according to ASTM1820) in the FASTRAN retardation model. A set of experiments were performed using specimens made from a 7475-T7351 aluminium alloy plate. Loading sequences with peaks ordered in ascending-descending blocks were used. The effect of truncating and clipping selected load levels on crack propagation behaviour was evaluated using both experimental data and numerical analyses. The findings were supported by the results of a fractographic analysis. Findings – Fatigue crack propagation data defined using M(T) specimens made from Al 7475-T7351 alloy indicate the difficulty of evaluating the following two events simultaneously: fatigue crack increments after application of loads with maximum amplitudes that exceeded J Q and subcritical crack increments caused by loads at high stress intensity factors. An effect of overloading peaks with a maximum that exceeds J Q should be assessed using a special analysis beyond the scope of the FASTRAN retardation model. Originality/value – Measurements of fatigue crack growth on specimens made from 7475 T7351 aluminium alloy were carried out. The results indicated that simultaneously evaluating fatigue crack increments after application of the load amplitude above J Q and subcritical increments caused by the loads at high stress intensity factors is difficult. Experiments demonstrated that if the fatigue crack reaches a specific length, the maximal amplitude load induces considerable crack growth retardation.