Impact fatigue properties of unidirectional carbon fibre-reinforced polyetherimide (PEI) composites was evaluated by subjecting standard izod impact samples to low velocity impact loading at energy levels ranging 0.16–1.08 J by using Ceast Model Resil 25, a pendulum type instrumented impact...
Room temperature creep (RTC) at a crack tip and its influence on the fatigue crack growth behavior of a 304 stainless steel have been studied at room temperature. A time-dependent deformation has been observed at the crack tips under various stress intensity factors. The deformation increases...
A methodology to recover the non-ohmic properties of ZnO based varistors after degradation with long and short duration pulses was proposed in this work. The basic idea consists in submitt the degraded ceramics at different temperatures and oxygen flows. Thermal treatment at 900 °C for 2 h with...
Ceramic thermal barrier coatings (TBCs) are playing an increasingly critical role in advanced gas turbine engines due to their ability to sustain further increases in operating temperatures. However, these increases in temperature could raise considerable issues associated with increased...
The metallurgical study of Pb–2wt.%Sm and Pb–0.08wt.%Ca–2wt.%Sm has been performed from hardness measurements, DSC tests, TEM and SEM observations. It has been shown that the binary alloys do not hardened by microprecipitation of an intermetallic phase such as Pb 3 Sm: after 2 years, the...
The crystallization and subsequent melting behaviour of absorbed water in the model composites of polyamide 6 (PA6) and carbon fibre were investigated by differential scanning calorimetry (DSC) in comparison with those in neat PA6, using the small rectangular specimens exposed to water at 90 °C....
Single-phased spinel-related titanium-substituted Li 0.5 Fe 2.5 O 4 has been synthesized by sintering in air a mechanically pre-milled mixture of lithium carbonate, corundum-related iron (III) oxide and the rutile polymorph of titanium (IV) oxide at 700 °C (12 h). This temperature is ca....
Read and print from thousands of top scholarly journals.
Sign up with Facebook
Sign up with Google
Already have an account? Log in
Save this article to read later. You can see your Read Later on your DeepDyve homepage.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Sign Up Log In
To subscribe to email alerts, please log in first, or sign up for a DeepDyve account if you don’t already have one.
To get new article updates from a journal on your personalized homepage, please log in first, or sign up for a DeepDyve account if you don’t already have one.