The microstructure of Ti-Co polycrystals with 1.6 and 3.2 at.% Co has been studied between 690 and 810 °C after long anneals (720-860 h) in the αTi+β(Ti,Co) two-phase area of the Ti-Co phase diagram. It has been observed that depending on the annealing temperature and GB energy, the αTi phase...
Thermal expansion and electrical resistivity of alloys based on Sn-Zn eutectic with 0.5, 1.0, 1.5, and 4.0 wt.% additions of In were studied. Thermal expansion measurements were performed using thermomechanical analysis tester over 223-373 K temperature range. Electrical resistivity measurements...
Thermal explosion reactions of Al-Ti-C system were studied. It was found that TiC and Al3Ti could be synthesized as final products in the Al-Ti-C system. A particular morphology variation of TiC occurred with an increase of TiC content. TiC presented a strip form as the content of TiC was 20...
Read and print from thousands of top scholarly journals.
Continue with Facebook
Sign up with Google
Log in with Microsoft
Already have an account? Log in
Bookmark this article. You can see your Bookmarks on your DeepDyve Library.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Sign Up Log In
To subscribe to email alerts, please log in first, or sign up for a DeepDyve account if you don’t already have one.
To get new article updates from a journal on your personalized homepage, please log in first, or sign up for a DeepDyve account if you don’t already have one.