is computed and the criterion is used to predict debonding initiation at the fiber / matrix interface . The analysis shows that this failure is most likely to occur at the free surface, i.e. the region where ...
and closure. Damage models of matrix fragmentation, interface debonding, and fiber’s failure are considered in the micromechanical analysis of tensile response, and the matrix fragmentation closure, interface ...
This paper aims to predict fatigue life and fatigue limit of fiber -reinforced ceramic- matrix composites (CMCs) with different fiber preforms, i.e. unidirectional, cross-ply, 2D-, 2.5D- and 3D-woven ...
-dependent tensile stress–strain curves, matrix cracking, interface debonding, and fiber failure of four different unidirectional SiC/SiC minicomposites for different oxidation time are predicted ...
of random fiber distribution as observed in the microscopic image of an actual composite ply. For modeling the fiber / matrix interface failure behavior, cohesive zone module (cohesive surface/cohesive element ...
cracking, fiber / matrix interface debonding, and fiber failure is obtained for the fiber and the matrix axial stress and the fiber / matrix interface shear stress in the interface wear region, interface ...
Analysis (FEA) methodology to predict the room temperature transverse tensile failure behavior of a SiCf/SiC composite (Silicon Carbide Fiber /Silicon Carbide Matrix ) with Boron Nitride (BN) fiber coating ...
as well as experimental data. Lastly, we predicted the failure of laminates. Instead of using a unidirectional ply-based failure theory, starting with the fiber , matrix , and their interface will lead ...
, interface debonding model, fiber strength degradation model and fiber failure model, has been adopted to analyze microstress field in the composite. The relationships between matrix cracking stress, interface ...
) with 60° braiding angle under quasi-static tensile load. The modified Von Mises strength criterion and 3D Hashin failure criterion are used to predict the damage initiation of the pure matrix and fiber tows ...