Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds

Synthesis, Characterization, and Osteoblastic Cell Culture of... Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds 105 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering."/> 105 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering."/> div.banner_title_bkg div.trangle { border-color: #C57B00 transparent transparent transparent; opacity:0.95; /*new styles start*/ -ms-filter:"progid:DXImageTransform.Microsoft.Alpha(Opacity=95)" ;filter: alpha(opacity=95); /*new styles end*/ } div.banner_title_bkg_if div.trangle { border-color: transparent transparent #C57B00 transparent ; opacity:0.95; /*new styles start*/ -ms-filter:"progid:DXImageTransform.Microsoft.Alpha(Opacity=95)" ;filter: alpha(opacity=95); /*new styles end*/ } div.banner_title_bkg div.trangle { width: 346px; } #banner { background-image: url('http://images.hindawi.com/journals/ijbm/ijbm.banner.jpg'); background-position: 50% 0;} Hindawi Publishing Corporation Home Journals About Us International Journal of Biomaterials About this Journal Submit a Manuscript Table of Contents Journal Menu About this Journal · Abstracting and Indexing · Aims and Scope · Article Processing Charges · Articles in Press · Author Guidelines · Bibliographic Information · Citations to this Journal · Contact Information · Editorial Board · Editorial Workflow · Free eTOC Alerts · Publication Ethics · Reviewers Acknowledgment · Submit a Manuscript · Subscription Information · Table of Contents Open Special Issues · Published Special Issues · Special Issue Guidelines Abstract Full-Text PDF Full-Text HTML Full-Text ePUB Linked References How to Cite this Article International Journal of Biomaterials Volume 2014 (2014), Article ID 501789, 7 pages http://dx.doi.org/10.1155/2014/501789 Research Article Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds André Dutra Messias , 1,2 Kelly Fernanda Martins , 2,3 Adriana Cristina Motta , 2 and Eliana Aparecida de Rezende Duek 1,2,3 1 Department of Materials Engineering, Faculty of Mechanical Engineering, State University of Campinas, Rua Mendeleyev 200, 13083-860 Campinas, SP, Brazil 2 Laboratory of Biomaterials, Faculty of Medical Sciences and Health, Pontifical Catholic University of São Paulo, Rua Joubert Wey 290, 18030-070 Sorocaba, SP, Brazil 3 Federal University of Sao Carlos, Rodovia João Leme dos Santos, Km 110, SP-264, Itinga, 18052-780 Sorocaba, SP, Brazil Received 23 October 2013; Revised 3 June 2014; Accepted 4 June 2014; Published 25 June 2014 Academic Editor: Feng Huei Lin Copyright © 2014 André Dutra Messias et al. This is an open access article distributed under the Creative Commons Attribution License , which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Abstract Lactide-based polymers have been widely investigated as materials for tissue engineering. However, characteristics such as low flexibility and elongation tend to limit particular applications, although these can be enhanced by adding plasticizers such as trimethylene carbonate (TMC) to the polymer chain of the copolymer poly(L-lactide-co-D,L-lactide) (PLDLA). The aim of this work was to synthesize and characterize a terpolymer of L-lactide, D,L-lactide, and TMC. The polymers were synthesized from 30% TMC by bulk polymerization and resulted in an average molar mass >10 5 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering. 1. Introduction Bone has a limited capacity for regeneration, especially in cases involving large losses as a result of complicated fractures caused by trauma, disease, birth defects, bone tumor removal, joint replacement, spinal fusion, or periodontal diseases. Bone loss is a major challenge for modern medicine, particularly since current techniques, such as metallic implants and autologous bone grafts, have significant drawbacks. There is therefore a need to develop novel therapeutic approaches such as bone tissue engineering [ 1 , 2 ]. Tissue engineering seeks to create an alternative means of repairing bone injuries by combining a scaffold, cells, and growth factors to produce tissue substitutes capable of restoring or replacing lost tissues and organs. The approaches used include cell therapies, induction of tissue/organ regeneration by biologically active molecules, and the transplantation of tissues grown in vitro [ 2 , 3 ]. An underlying principle in this approach is that biomaterial or cell-biomaterial constructs degrade concomitantly with tissue regeneration. Poly( α -hydroxyacids) are biodegradable, resorbable materials with good biocompatibility and these features make them preferred candidates for tissue engineering. The lactide monomers have different chiral molecules. Among lactide-derived polymers, only poly(L-lactide) and poly(D,L-lactide) have been extensively investigated as biomaterials. The biological properties of the copolymer poly(L-co-D,L lactide) (PLDLA) remain poorly known whereas poly(L-lactide) (PLLA) is a semicrystalline polymer with a high modulus and strength. PLLA is known for its increasing crystallinity during degradation which can generate an intense inflammatory response [ 4 ]. In contrast, poly(D,L-lactide) (PDLLA) is an amorphous polymer characterized by the random distribution of the two isomeric forms along the polymer chain [ 5 ]. PLDLA is also amorphous and has mechanical features similar to those of PLLA without the inconvenience of long degradation times and high crystallinity. The brittle nature of poly(lactides) requires modification in order to be useful as biomedical materials [ 6 ]. The need for biodegradable elastomeric polymers for medical implants and porous scaffolds in tissue engineering has been documented in recent years [ 7 – 9 ]. The suitability of poly trimethylene carbonate (TMC) for the preparation of biomedical implants has also been evaluated [ 10 ]. Poly(TMC) has a very low modulus and tensile strength and its poor mechanical properties have discouraged any practical application other than as a component of copolymers and blends. Poly(TMC) has been used as a softening unit in stiff and brittle polymers such as lactide [ 7 , 11 , 12 ] and glycolide [ 13 ]. Scaffolds are implants or injections that are used to deliver cells, drugs, and genes into the body. Different forms of polymeric scaffolds for cell/drug delivery are available, for example, typical three-dimensional porous matrices, nanofiber matrices, thermosensitive sol-gel transition hydrogels, and a porous microsphere. A scaffold provides a suitable substrate for cell attachment, cell proliferation, differentiated function, and cell migration [ 14 ]. Porous bioresorbable polymers have been widely used as scaffolds in tissue engineering. Macroporous structures are desirable in many cases to facilitate cell seeding, infiltration of fluids, vascularization, and tissue ingrowth. In this context, several techniques have been developed to create porous scaffolds, including solvent casting/particulate leaching, fiber bonding, gas foaming, phase inversion, and solvent removal by freeze-drying. The morphology and properties of the resulting scaffolds depend largely on the fabrication process used [ 15 ]. Polymeric scaffolds should be designed to facilitate cell distribution and guide tissue regeneration in three dimensions [ 16 ]. Among the different methods for producing scaffolds, solvent casting followed by precipitation or particulate leaching is one of the most straightforward methods [ 17 , 18 ]. Particulate leaching is a general procedure that is used to obtain porous scaffolds in solvent casting methods [ 19 , 20 ]. In this study, scaffolds of PLDLA and PLDLA-TMC were prepared by solvent casting/particulate leaching using saccharose crystals as the porogen. The copolymers synthesized were characterized by physical and chemical methods and the thermal properties of the scaffolds were investigated. The usefulness of the scaffolds for stimulating osteoblast adhesion and proliferation in vitro was also assessed. 2. Materials and Method 2.1. Poly(L-co-D,L-lactide-co-trimethylene carbonate) Synthesis Polymerization was carried out using L-lactide (Purasorb L, Purac, Netherlands), D,L-lactide (Purasorb DL, Purac), and trimethylene carbonate (TMC, 1,3-dioxane-2-one; Boehringer Ingelheim Pharma, Germany) in 70 : 30 : 0 and 50 : 20 : 30 monomer ratios catalyzed by Sn(Oct) 2 at 130°C for 48 h in a vacuum ampoule (INPI patent requisition, protocol number 020110049277). The polymers were subsequently purified by dissolution in chloroform and precipitation in methanol. 2.2. Physicochemical Characterization of the Synthesized Polymer 2.2.1. Nuclear Magnetic Resonance (NMR) Nuclear magnetic resonance (NMR) spectra were obtained with a Bruker 250 spectrometer operated at 300 MHz and 75 MHz for 1 H and 13 C, respectively, at room temperature. The polymer samples (10% w/v) were dissolved in deuterated chloroform (CDCl 3 ) and tetramethylsilane was used as the reference standard. 2.2.2. Fourier Transform Infrared (FTIR) Spectrometry Fourier transform infrared (FTIR) spectrometry was carried out using a Perkin Elmer FT-IR Spectrum One spectrometer in the range of 4000–650 cm −1 after casting the polymer from chloroform solution onto sodium chlorite pellets. 2.2.3. Gel Permeation Chromatography (GPC) Gel permeation chromatography (GPC) analyses were carried out using a Waters instrument (1525 binary HPLC pump and 2414 refractive index detector, Waters Corporation, USA) equipped with Waters Styragel columns (HR 4E and HR 5E). Tetrahydrofuran was used as the mobile phase at a flow rate of 1 mL/min. The columns and detector were maintained at 30°C and 40°C, respectively. 2.3. Scaffold Fabrication, Morphology, and Thermal Properties 2.3.1. Scaffold Fabrication The polymer scaffolds were prepared by the solvent casting/particulate leaching method. Initially, the polymer was dissolved in chloroform (10% w/v) for 4 h. After complete dissolution, a 70% (w/v) solution of ground, sieved sucrose crystals (>250 μ m) was added. The mixture was then cast in silicone molds with cylindrical cavities (7 mm in diameter and 10 mm high) and the solvent was allowed to evaporate overnight at room temperature. Sucrose particles were removed by immersion in a 1% (w/v) aqueous solution of polyvinyl alcohol in order to reduce the surface tension between the polymer and water. Finally, the scaffolds were dried in a vacuum and sliced to form disks ~4 mm high. 2.3.2. Scanning Electron Microscopy (SEM) Morphological analysis of the scaffolds was carried out by scanning electron microscopy (SEM) using a JEOL JXA-840A scanning electron microscope after gold coating (Balzer SCD 050) of the samples. Some samples were immersed in liquid nitrogen and fractured in order to examine the internal structure of the scaffold. 2.3.3. Scanning Differential Calorimetry (DSC) Scanning differential calorimetry (DSC) measurements were carried out on a DSC 2920 thermal analyzer (TA Instruments, USA). Polymeric samples were hermetically sealed in aluminum pans and heated at 200°C to destroy the thermal history of the polymers. Subsequently, the samples were exposed to temperatures ranging from −50°C to 200°C at increments of 10°C min −1 , in an inert nitrogen atmosphere flushed at 5 mL min −1 . 2.3.4. Thermogravimetric Analysis (TGA) The thermal stability of the scaffolds was tested in an STA 409C thermogravimetric analyzer (Netzsch) in which the samples were heated at 10°C min −1 up to 500°C, in an inert argon atmosphere. 2.4. Osteoblast Cell Culture on Scaffolds 2.4.1. Cell Culture Human osteoblast-like SaOS-2 cells were purchased from the Rio de Janeiro Cell Bank (Rio de Janeiro, RJ, Brazil) and cultured in McCoy’s 5A modified medium (CULTILAB, Brazil) containing L-glutamine, HEPES, 15% fetal bovine serum (FBS—CULTILAB, Brazil), 50 mg of getamicin/L (Invitrogen), and 2.5 mg of amphotericin B/L (Invitrogen) in a humidified 95% air/5% CO 2 incubator, at 37°C. The medium was changed every 3-4 days. Cells were detached by treatment with a trypsin/EDTA solution (CULTILAB, Brazil). The scaffolds were sterilized by immersion in 70% ethanol for 1 h and repeatedly washed with deionized water. Before cell culture, sterilized scaffolds were maintained in McCoy’s 5A medium for ~24 h. A cell suspension (1 × 10 4 cells/well in 200 μ L of growth medium) was seeded onto scaffolds of PLDLA-TMC and PLDLA in 96-well plates (TPP, Switzerland) and cultured for 1, 3, 7, and 14 days. Control cells were cultured in wells without scaffolds. The long-term culture clarifies how the scaffolds can sustain the cell proliferation and also allows the observation of the cell differentiation. 2.4.2. MTT Assay To evaluate the mitochondrial activity of the seeded cells, that is, cell viability on the scaffolds during culture, the samples and controls were washed 2-3 times with McCoy’ 5A medium without serum and then incubated with 200 μ L of 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT—Sigma-Aldrich) in McCoy’s medium (0.5 mg mL −1 ). The plates were incubated for 4 h in a cell incubator at 37°C, after which the MTT solution was replaced with 200 μ L of dimethylsulphoxide (DMSO—Sigma-Aldrich). After 10 min, 100 μ L aliquots were transferred to empty wells and the absorbances were measured in a microplate reader (Elx-800-UV, Bio-Tek Instruments) at 570 nm and 650 nm. 2.4.3. ALP Assay Alkaline phosphatase (ALP) produced by SaOS-2 was quantified as an osteoblast marker using an ALP kit (Labtest, Brazil). Briefly, 10 μ L aliquots of culture supernatant were collected and added to 100 μ L of p -nitrophenol phosphate solution (12 mM p -nitrophenol phosphate, 10 mM phenol, and 1.6 mM EDTA buffered to pH 10.4, 0.96 mM zinc sulfate, 2 mM magnesium acetate, and 6.4 mM sodium azide). The reagent was run for 2 min at 37°C and the changes in absorbance were measured in a microplate reader at 415 nm and 650 nm. 3. Results and Discussion 3.1. Physicochemical Characterization of the Synthesized Polymer Poly(L-co-D,L-lactide-co-trimethylene carbonate) was synthesized by bulk polymerization via ring-opening of cyclic dimer monomers at 130°C for 48 h in a vacuum atmosphere. Table 1 shows molar mass of terpolymer measured by GPC. The catalyst used was stannous octoate (Sn(Oct) 2 ) in a monomer/catalyst ratio of 5,000 (w/w). Previous studies demonstrated that this monomer/catalyst ratio produced higher yields and greater molar mass values [ 21 ]. Table 1: Molar mass of terpolymer. Figure 1 shows the 1 H-NMR spectra of PLDLA-TMC. The signals found in the terpolymer 1 H-NRM were practically the same as those for the poly(L-lactide-co-D,L lactide) copolymer and differed at only two points that are characteristic of TMC, that is, δ 2.05 ppm (CH 2 -TMC) and δ 4.24 ppm (OCH 2 -TMC) [ 22 ]. In the copolymer spectrum (data not shown), a multiplet at 5.12–5.24 ppm was assigned to the CH (b) proton, while the quartet at 1.55–1.59 ppm was assigned to the protons CH 3 (a) [ 23 ]. In the case of PLDLA-TMC, the triplet at 2.05 ppm was assigned to the protons CH 2 (c), while the triplet at 4.24 was assigned to OCH 2 (d). Figure 1: 1 H NMR spectra of PLDLA-TMC. The 13 C-NMR spectrum (Figure 2 ) showed lactide units at 16.6 (CH 3 ), 69.0 (CH), and 169.6 (C=O) ppm and TMC units at 27.8 (CH 2 –CH 2 –CH), 61.8–64.7 (CH 2 O), and 154.8 (C=O) ppm. These chemical shifts agreed with the findings of Matsumura et al. [ 24 ] who synthesized low molar mass (21,000 g mol −1 ) lactide/TMC copolymers using a lipase-catalyzed reaction. Figure 2: 13 C NMR spectrum of PLDLA-TMC. Figure 3 represents PLDLA and PLDLA-TMC infrared spectra and shows no difference when TMC is present. The strongest peaks are found at 1181 and 1746 cm −1 corresponding to C–C bonds and carbonyl axial deformation, respectively. Figure 3: FT-IR spectra of PLDLA and PLDLA-TMC. 3.2. Scaffold Construction, Morphology, and Thermal Properties SEM revealed the porous morphology of the scaffold surface (Figures 4(a) and 4(b) ) and interior (Figures 4(c) and 4(d) ). The pores were irregular in shape and consisted of a mixture of large pores (~250–500 μ m in diameter) and small pores (<100 μ m). Inner side of the scaffold is highly porous compared to the scaffold surface (Figures 4(c) and 4(d) ). Scaffold porosity and pore size are important features when evaluating biomaterial properties for tissue engineering [ 25 ]. An adequate pore size allows cell invasion and tissue ingrowth to surround the local implant while maintaining adequate nutrient transfer; however, there is some controversy regarding the best pore that favors new bone formation and growth [ 26 – 28 ]. The porosity and pore structure can be controlled by salt weight, particle size, and polymer fraction [ 25 ]. Figure 4: SEM of PLDLA-TMC scaffolds showing the external (a, b) and inner (c, d) surfaces. Inner views of the scaffolds were obtained after cryofracture. The results for the thermal characterization of the scaffolds are shown in Figures 5 (DSC) and 6 (TGA). None of the polymeric scaffolds showed evidence of crystallinity. PLDLA-TMC was amorphous and DSC thermograms showed a decrease in the glass transition temperature ( ) of PLDLA-TMC (51.7°C) compared to PLDLA (57.9°C) (Figure 5 ). Similar tendencies were observed for the values for poly(L-lactide-co-TMC) and poly(D,L lactide-co-TMC) [ 24 ]. Davachi et al. [ 29 ] showed that an increase in the TMC content of poly(lactide-TMC-glycolide) resulted in a decrease in the glass transition temperature. Since the crystalline phase is poorly accessible to water and other permeants, the presence of crystallinity reduces polymer permeability and the rate of biodegradation by chain scission because of a decrease in accessible hydrolysable bonds. With regard to the use of these polymers for biomedical applications, it is worth remembering that crystalline debris formed during degradation may cause an undesired late inflammatory response, thereby negatively influencing tissue growth and normal function [ 30 ]. Hence, little or no crystallinity is desirable [ 31 ]. Figure 5: DSC thermograms showing the glass transition temperature of PLDLA and PLDLA-TMC scaffolds. Figure 6: TGA thermograms of PLDLA and PLDLA-TMC scaffolds. The thermal stability of PLDLA-TMC was measured with a thermogravimetric analyzer (TGA). Figure 6 shows typical TGA traces of weight loss as a function of temperature. This analysis showed that both polymers decomposed in a single-stage degradation and that the addition of TMC reduced the polymer thermal stability; that is, the addition of TMC to L/D,L-lactide resulted in greater degradation of the polymer. The onset temperature of PLDLA decreased from 333.2°C to 322.6°C when TMC was present. The maximum decomposition temperature of PLDLA was 362.8°C, whereas that of PLDLA-TMC was 342.1°C. 3.3. Osteoblast Cell Culture on Scaffolds The MTT assay showed that the viability of SaOS-2 osteoblasts increased with time (Figure 7 ), an indication of cell proliferation on the porous scaffolds. The presence of TMC in PLDLA did not affect cell viability compared to scaffolds containing only PLDLA. After 1 and 7 days, cells grown on PLDLA and PLDLA-TMC scaffolds showed greater viability than those grown in control wells ( ). After 14 days, only cells grown on PLDLA-TMC scaffolds had greater viability than control cells ( ). SaOS-2 proliferation ceased at 7 days since the viability was similar at 7 and 14 days. Figure 7: Viability of SaOS-2 osteoblasts grown on scaffolds. The values are the mean ± SD ( ). Early osteoblastic differentiation was demonstrated by the ALP activity of SaOS-2 cells (Figure 8 ). There was no significant difference in the ALP activities of PLDLA and PLDLA-TMC scaffolds. The ALP activity increased from days 1 and 3 to days 7 and 14 ( ). Figure 8: Alkaline phosphatase activity of SaOS-2 on scaffolds. Values are expressed as means ± SD, . Stein and Lian [ 32 ] identified two stages of osteoblast differentiation, namely, proliferation during the first 7–14 days and the secretion of extracellular matrix proteins and production of early differentiation markers, such as ALP, from day 7 onwards. ALP belongs to a group of membrane-bound glycoproteins involved in the deposition of minerals on extracellular matrix molecules [ 33 ]. 4. Conclusion Poly(L-co-D,L-lactide-co-trimethylene carbonate) (PLDLA-TMC) was synthetized by ring-opening bulk polymerization of the monomers, using stannous octanoate as catalyst. Thermal analysis showed that the presence of TMC reduced the glass transition temperature and decreased the polymer thermal stability. The scaffolds had a porous morphology that was conducive to cell growth, as shown in the viability and proliferation of SaOS-2 osteoblasts. The detection of alkaline phosphatase activity demonstrated that the cells retained their osteoblast phenotype. Thus, PLDLA-based devices are potentially useful for bone tissue engineering. Conflict of Interests The authors declare that there is no conflict of interests regarding the publication of this paper. Acknowledgments The authors thank FAPESP (Fundação de Amparo à Pesquisa do Estado de São Paulo, Grant no. 2010/15065-7) for financial support and the Scanning Electron Microscopy Laboratory (LabMEV) of the State University of Campinas (UNICAMP) for providing access to their equipment. References J. A. Baddour, K. Sousounis, and P. A. Tsonis, “Organ repair and regeneration: an overview,” Birth Defects Research C: Embryo Today , vol. 96, no. 1, pp. 1–29, 2012. View at Publisher · View at Google Scholar · View at Scopus J. M. Holzwarth and P. X. Ma, “Biomimetic nanofibrous scaffolds for bone tissue engineering,” Biomaterials , vol. 32, no. 36, pp. 9622–9629, 2011. View at Publisher · View at Google Scholar · View at Scopus B. Demirbag, P. Y. Huri, G. T. Kose, A. Buyuksungur, and V. Hasirci, “Advanced cell therapies with and without scaffolds,” Biotechnology Journal , vol. 6, no. 12, pp. 1437–1453, 2011. View at Publisher · View at Google Scholar · View at Scopus A. C. Motta and E. A. R. Duek, “Synthesis, characterization and “in vitro” degradation of PLLA,” Polímeros , vol. 16, no. 1, pp. 26–32, 2006. View at Publisher · View at Google Scholar L. S. Nair and C. T. Laurencin, “Polymers as biomaterials for tissue engineering and controlled drug delivery,” Advances in Biochemical Engineering/Biotechnology , vol. 102, pp. 47–90, 2006. View at Publisher · View at Google Scholar D. J. Darensbourg, W. Choi, O. Karroonnirun, and N. Bhuvanesh, “Ring-opening polymerization of cyclic monomers by complexes derived from biocompatible metals. Production of poly(lactide), poly(trimethylene carbonate), and their copolymers,” Macromolecules , vol. 41, no. 10, pp. 3493–3502, 2008. View at Publisher · View at Google Scholar · View at Scopus B. Buchholz, “Analysis and characterization of resorbable DL-lactide-trimethylene carbonate copolyesters,” Journal of Materials Science: Materials in Medicine , vol. 4, no. 4, pp. 381–388, 1993. View at Publisher · View at Google Scholar · View at Scopus U. A. Stock and J. P. Vacanti, “Tissue engineering: current state and prospects,” Annual Review of Medicine , vol. 52, pp. 443–451, 2001. View at Publisher · View at Google Scholar · View at Scopus Y. Wang, G. A. Ameer, B. J. Sheppard, and R. Langer, “A tough biodegradable elastomer,” Nature Biotechnology , vol. 20, no. 6, pp. 602–606, 2002. View at Publisher · View at Google Scholar · View at Scopus I. Engelberg and J. Kohn, “Physico-mechanical properties of degradable polymers used in medical applications: a comparative study,” Biomaterials , vol. 12, no. 3, pp. 292–304, 1991. View at Publisher · View at Google Scholar · View at Scopus D. W. Grijpma, R. D. A. van Hofslot, H. Supèr, A. J. Nijenhuis, and A. J. Pennings, “Rubber toughening of poly(lactide) by blending and block copolymerization,” Polymer Engineering and Science , vol. 34, no. 22, pp. 1674–1684, 1994. View at Publisher · View at Google Scholar · View at Scopus E. Ruckenstein and Y. Yuan, “Molten ring-open copolymerization of L-lactide and cyclic trimethylene carbonate,” Journal of Applied Polymer Science , vol. 69, no. 7, pp. 1429–1434, 1998. View at Scopus A. R. Katz, D. P. Mukherjee, A. L. Kaganov, and S. Gordon, “A new synthetic monofilament absorbable suture made from polytrimethylene carbonate,” Surgery, Gynecology & Obstetrics , vol. 161, no. 3, pp. 213–222, 1985. View at Scopus T. Garg, O. Singh, S. Arora, and R. S. R. Murthy, “Scaffold: a novel carrier for cell and drug delivery,” Critical Reviews in Therapeutic Drug Carrier Systems , vol. 29, no. 1, pp. 1–63, 2012. View at Scopus J. D. Kretlow, L. Klouda, and A. G. Mikos, “Injectable matrices and scaffolds for drug delivery in tissue engineering,” Advanced Drug Delivery Reviews , vol. 59, no. 4-5, pp. 263–273, 2007. View at Publisher · View at Google Scholar · View at Scopus A. Yousefi, C. Gauvin, L. Sun, R. W. DiRaddo, and J. Fernandas, “Design and fabrication of 3D-plotted polymeric scaffolds in functional tissue engineering,” Polymer Engineering and Science , vol. 47, no. 5, pp. 608–618, 2007. View at Publisher · View at Google Scholar · View at Scopus E. Chevalier, D. Chulia, C. Pouget, and M. Viana, “Fabrication of porous substrates: a review of processes using pore forming agents in the biomaterial field,” Journal of Pharmaceutical Sciences , vol. 97, no. 3, pp. 1135–1154, 2008. View at Publisher · View at Google Scholar · View at Scopus P. K. D. V. Yarlagadda, M. Chandrasekharan, and J. Y. M. Shyan, “Recent advances and current developments in tissue scaffolding,” Bio-Medical Materials and Engineering , vol. 15, no. 3, pp. 159–177, 2005. View at Scopus S. H. Barbanti, A. R. Santos Jr., C. A. C. Zavaglia, and E. A. R. Duek, “Porous and dense poly(L-lactic acid) and poly(D,L-lactic acid-co-glycolic acid) scaffolds: in vitro degradation in culture medium and osteoblasts culture,” Journal of Materials Science: Materials in Medicine , vol. 15, no. 12, pp. 1315–1321, 2004. View at Publisher · View at Google Scholar · View at Scopus S. H. Barbanti, A. R. Santos Jr., C. A. C. Zavaglia, and E. A. R. Duek, “Poly( ε -caprolactone) and poly(D,L-lactic acid-co-glycolic acid) scaffolds used in bone tissue engineering prepared by melt compression-particulate leaching method,” Journal of Materials Science: Materials in Medicine , vol. 22, no. 10, pp. 2377–2385, 2011. View at Publisher · View at Google Scholar · View at Scopus A. C. Motta and E. A. R. Duek, “Synthesis and characterization of the copolymer poly (L-co-D,L lactic acid),” Polímero , vol. 17, no. 2, pp. 123–129, 2007. View at Publisher · View at Google Scholar D. Pospiech, H. Komber, D. Jehnichen et al., “Multiblock copolymers of L-lactide and trimethylene carbonate,” Biomacromolecules , vol. 6, no. 1, pp. 439–446, 2005. View at Publisher · View at Google Scholar · View at Scopus K. A. M. Thakur, R. T. Kean, E. S. Hall, M. A. Doscotch, and E. J. Munson, “A quantitative method for determination of lactide composition in poly(lactide) using 1 H NMR,” Analytical Chemistry , vol. 69, no. 21, pp. 4303–4309, 1997. View at Publisher · View at Google Scholar · View at Scopus S. Matsumura, K. Tsukada, and K. Toshima, “Novel lipase-catalyzed ring-opening copolymerization of lactide and trimethylene carbonate forming poly(ester carbonate)s,” International Journal of Biological Macromolecules , vol. 25, no. 1–3, pp. 161–167, 1999. View at Publisher · View at Google Scholar · View at Scopus X. Zhao, X. Li, Y. Kang, and Q. Yuan, “Improved biocompatibility of novel poly(L-lactic acid)/ β -tricalcium phosphate scaffolds prepared by an organic solvent-free method,” International Journal of Nanomedicine , vol. 6, pp. 1385–1390, 2011. View at Scopus O. Gauthier, J. Bouler, E. Aguado, P. Pilet, and G. Daculsi, “Macroporous biphasic calcium phosphate ceramics: influence of macropore diameter and macroporosity percentage on bone ingrowth,” Biomaterials , vol. 19, no. 1–3, pp. 133–139, 1998. View at Publisher · View at Google Scholar · View at Scopus K. A. Hing, S. M. Best, and W. Bonfield, “Characterization of porous hydroxyapatite,” Journal of Materials Science: Materials in Medicine , vol. 10, no. 3, pp. 135–145, 1999. View at Publisher · View at Google Scholar · View at Scopus A. G. Mikos, G. Sarakinos, M. D. Lyman, D. E. Ingber, J. P. Vacanti, and R. Langer, “Prevascularization of porous biodegradable polymers,” Biotechnology and Bioengineering , vol. 42, no. 6, pp. 716–723, 1993. View at Publisher · View at Google Scholar · View at Scopus S. M. Davachi, B. Kaffashi, J. M. Roushandeh, and B. Torabinejad, “Investigating thermal degradation, crystallization and surface behavior of l-lactide, glycolide and trimethylene carbonate terpolymers used for medical applications,” Materials Science and Engineering C , vol. 32, no. 2, pp. 98–104, 2012. View at Publisher · View at Google Scholar · View at Scopus R. R. M. Bos, F. B. Rozema, G. Boering et al., “Degradation of and tissue reaction to biodegradable poly(L-lactide) for use as internal fixation of fractures: a study in rats,” Biomaterials , vol. 12, no. 1, pp. 32–36, 1991. View at Publisher · View at Google Scholar · View at Scopus A. P. Pêgo, A. A. Poot, D. W. Grijpma, and J. Feijen, “Physical properties of high molecular weight 1,3-trimethylene carbonate and D,L-lactide copolymers,” Journal of Materials Science: Materials in Medicine , vol. 14, no. 9, pp. 767–773, 2003. View at Publisher · View at Google Scholar · View at Scopus G. S. Stein and J. B. Lian, “Molecular mechanisms mediating proliferation/differentiation interrelationships during progressive development of the osteoblast phenotype,” Endocrine Reviews , vol. 14, no. 4, pp. 424–442, 1993. View at Publisher · View at Google Scholar · View at Scopus A. Polini, D. Pisignano, M. Parodi, R. Quarto, and S. Scaglione, “Osteoinduction of human mesenchymal stem cells by bioactive composite scaffolds without supplemental osteogenic growth factors,” PLoS ONE , vol. 6, no. 10, Article ID e26211, 2011. View at Publisher · View at Google Scholar · View at Scopus var _gaq = _gaq || []; _gaq.push(['_setAccount', 'UA-8578054-2']); _gaq.push(['_trackPageview']); (function () { var ga = document.createElement('script'); ga.type = 'text/javascript'; ga.async = true; ga.src = ('https:' == document.location.protocol ? 'https://ssl' : 'http://www') + '.google-analytics.com/ga.js'; var s = document.getElementsByTagName('script')[0]; s.parentNode.insertBefore(ga, s); })(); http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png International Journal of Biomaterials Hindawi Publishing Corporation

Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds

Loading next page...
 
/lp/hindawi-publishing-corporation/synthesis-characterization-and-osteoblastic-cell-culture-of-poly-l-co-cFQ0ZvZAqq

References

References for this paper are not available at this time. We will be adding them shortly, thank you for your patience.

Publisher
Hindawi Publishing Corporation
Copyright
Copyright © 2014 André Dutra Messias et al.
ISSN
1687-8787
eISSN
1687-8795
Publisher site
See Article on Publisher Site

Abstract

Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds 105 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering."/> 105 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering."/> div.banner_title_bkg div.trangle { border-color: #C57B00 transparent transparent transparent; opacity:0.95; /*new styles start*/ -ms-filter:"progid:DXImageTransform.Microsoft.Alpha(Opacity=95)" ;filter: alpha(opacity=95); /*new styles end*/ } div.banner_title_bkg_if div.trangle { border-color: transparent transparent #C57B00 transparent ; opacity:0.95; /*new styles start*/ -ms-filter:"progid:DXImageTransform.Microsoft.Alpha(Opacity=95)" ;filter: alpha(opacity=95); /*new styles end*/ } div.banner_title_bkg div.trangle { width: 346px; } #banner { background-image: url('http://images.hindawi.com/journals/ijbm/ijbm.banner.jpg'); background-position: 50% 0;} Hindawi Publishing Corporation Home Journals About Us International Journal of Biomaterials About this Journal Submit a Manuscript Table of Contents Journal Menu About this Journal · Abstracting and Indexing · Aims and Scope · Article Processing Charges · Articles in Press · Author Guidelines · Bibliographic Information · Citations to this Journal · Contact Information · Editorial Board · Editorial Workflow · Free eTOC Alerts · Publication Ethics · Reviewers Acknowledgment · Submit a Manuscript · Subscription Information · Table of Contents Open Special Issues · Published Special Issues · Special Issue Guidelines Abstract Full-Text PDF Full-Text HTML Full-Text ePUB Linked References How to Cite this Article International Journal of Biomaterials Volume 2014 (2014), Article ID 501789, 7 pages http://dx.doi.org/10.1155/2014/501789 Research Article Synthesis, Characterization, and Osteoblastic Cell Culture of Poly(L-co-D,L-lactide-co-trimethylene carbonate) Scaffolds André Dutra Messias , 1,2 Kelly Fernanda Martins , 2,3 Adriana Cristina Motta , 2 and Eliana Aparecida de Rezende Duek 1,2,3 1 Department of Materials Engineering, Faculty of Mechanical Engineering, State University of Campinas, Rua Mendeleyev 200, 13083-860 Campinas, SP, Brazil 2 Laboratory of Biomaterials, Faculty of Medical Sciences and Health, Pontifical Catholic University of São Paulo, Rua Joubert Wey 290, 18030-070 Sorocaba, SP, Brazil 3 Federal University of Sao Carlos, Rodovia João Leme dos Santos, Km 110, SP-264, Itinga, 18052-780 Sorocaba, SP, Brazil Received 23 October 2013; Revised 3 June 2014; Accepted 4 June 2014; Published 25 June 2014 Academic Editor: Feng Huei Lin Copyright © 2014 André Dutra Messias et al. This is an open access article distributed under the Creative Commons Attribution License , which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Abstract Lactide-based polymers have been widely investigated as materials for tissue engineering. However, characteristics such as low flexibility and elongation tend to limit particular applications, although these can be enhanced by adding plasticizers such as trimethylene carbonate (TMC) to the polymer chain of the copolymer poly(L-lactide-co-D,L-lactide) (PLDLA). The aim of this work was to synthesize and characterize a terpolymer of L-lactide, D,L-lactide, and TMC. The polymers were synthesized from 30% TMC by bulk polymerization and resulted in an average molar mass >10 5 g/mol. Thermal investigation of PLDLA-TMC showed a decrease in the glass transition and onset temperatures compared to PLDLA. PLDLA-TMC scaffolds stimulated the proliferation and normal phenotypic manifestations of cultured osteoblasts. These results show that it was possible to produce a terpolymer from L-lactide, D,L-lactide, and TMC. Scaffolds of this terpolymer had important characteristics that could be useful for applications in bone tissue engineering. 1. Introduction Bone has a limited capacity for regeneration, especially in cases involving large losses as a result of complicated fractures caused by trauma, disease, birth defects, bone tumor removal, joint replacement, spinal fusion, or periodontal diseases. Bone loss is a major challenge for modern medicine, particularly since current techniques, such as metallic implants and autologous bone grafts, have significant drawbacks. There is therefore a need to develop novel therapeutic approaches such as bone tissue engineering [ 1 , 2 ]. Tissue engineering seeks to create an alternative means of repairing bone injuries by combining a scaffold, cells, and growth factors to produce tissue substitutes capable of restoring or replacing lost tissues and organs. The approaches used include cell therapies, induction of tissue/organ regeneration by biologically active molecules, and the transplantation of tissues grown in vitro [ 2 , 3 ]. An underlying principle in this approach is that biomaterial or cell-biomaterial constructs degrade concomitantly with tissue regeneration. Poly( α -hydroxyacids) are biodegradable, resorbable materials with good biocompatibility and these features make them preferred candidates for tissue engineering. The lactide monomers have different chiral molecules. Among lactide-derived polymers, only poly(L-lactide) and poly(D,L-lactide) have been extensively investigated as biomaterials. The biological properties of the copolymer poly(L-co-D,L lactide) (PLDLA) remain poorly known whereas poly(L-lactide) (PLLA) is a semicrystalline polymer with a high modulus and strength. PLLA is known for its increasing crystallinity during degradation which can generate an intense inflammatory response [ 4 ]. In contrast, poly(D,L-lactide) (PDLLA) is an amorphous polymer characterized by the random distribution of the two isomeric forms along the polymer chain [ 5 ]. PLDLA is also amorphous and has mechanical features similar to those of PLLA without the inconvenience of long degradation times and high crystallinity. The brittle nature of poly(lactides) requires modification in order to be useful as biomedical materials [ 6 ]. The need for biodegradable elastomeric polymers for medical implants and porous scaffolds in tissue engineering has been documented in recent years [ 7 – 9 ]. The suitability of poly trimethylene carbonate (TMC) for the preparation of biomedical implants has also been evaluated [ 10 ]. Poly(TMC) has a very low modulus and tensile strength and its poor mechanical properties have discouraged any practical application other than as a component of copolymers and blends. Poly(TMC) has been used as a softening unit in stiff and brittle polymers such as lactide [ 7 , 11 , 12 ] and glycolide [ 13 ]. Scaffolds are implants or injections that are used to deliver cells, drugs, and genes into the body. Different forms of polymeric scaffolds for cell/drug delivery are available, for example, typical three-dimensional porous matrices, nanofiber matrices, thermosensitive sol-gel transition hydrogels, and a porous microsphere. A scaffold provides a suitable substrate for cell attachment, cell proliferation, differentiated function, and cell migration [ 14 ]. Porous bioresorbable polymers have been widely used as scaffolds in tissue engineering. Macroporous structures are desirable in many cases to facilitate cell seeding, infiltration of fluids, vascularization, and tissue ingrowth. In this context, several techniques have been developed to create porous scaffolds, including solvent casting/particulate leaching, fiber bonding, gas foaming, phase inversion, and solvent removal by freeze-drying. The morphology and properties of the resulting scaffolds depend largely on the fabrication process used [ 15 ]. Polymeric scaffolds should be designed to facilitate cell distribution and guide tissue regeneration in three dimensions [ 16 ]. Among the different methods for producing scaffolds, solvent casting followed by precipitation or particulate leaching is one of the most straightforward methods [ 17 , 18 ]. Particulate leaching is a general procedure that is used to obtain porous scaffolds in solvent casting methods [ 19 , 20 ]. In this study, scaffolds of PLDLA and PLDLA-TMC were prepared by solvent casting/particulate leaching using saccharose crystals as the porogen. The copolymers synthesized were characterized by physical and chemical methods and the thermal properties of the scaffolds were investigated. The usefulness of the scaffolds for stimulating osteoblast adhesion and proliferation in vitro was also assessed. 2. Materials and Method 2.1. Poly(L-co-D,L-lactide-co-trimethylene carbonate) Synthesis Polymerization was carried out using L-lactide (Purasorb L, Purac, Netherlands), D,L-lactide (Purasorb DL, Purac), and trimethylene carbonate (TMC, 1,3-dioxane-2-one; Boehringer Ingelheim Pharma, Germany) in 70 : 30 : 0 and 50 : 20 : 30 monomer ratios catalyzed by Sn(Oct) 2 at 130°C for 48 h in a vacuum ampoule (INPI patent requisition, protocol number 020110049277). The polymers were subsequently purified by dissolution in chloroform and precipitation in methanol. 2.2. Physicochemical Characterization of the Synthesized Polymer 2.2.1. Nuclear Magnetic Resonance (NMR) Nuclear magnetic resonance (NMR) spectra were obtained with a Bruker 250 spectrometer operated at 300 MHz and 75 MHz for 1 H and 13 C, respectively, at room temperature. The polymer samples (10% w/v) were dissolved in deuterated chloroform (CDCl 3 ) and tetramethylsilane was used as the reference standard. 2.2.2. Fourier Transform Infrared (FTIR) Spectrometry Fourier transform infrared (FTIR) spectrometry was carried out using a Perkin Elmer FT-IR Spectrum One spectrometer in the range of 4000–650 cm −1 after casting the polymer from chloroform solution onto sodium chlorite pellets. 2.2.3. Gel Permeation Chromatography (GPC) Gel permeation chromatography (GPC) analyses were carried out using a Waters instrument (1525 binary HPLC pump and 2414 refractive index detector, Waters Corporation, USA) equipped with Waters Styragel columns (HR 4E and HR 5E). Tetrahydrofuran was used as the mobile phase at a flow rate of 1 mL/min. The columns and detector were maintained at 30°C and 40°C, respectively. 2.3. Scaffold Fabrication, Morphology, and Thermal Properties 2.3.1. Scaffold Fabrication The polymer scaffolds were prepared by the solvent casting/particulate leaching method. Initially, the polymer was dissolved in chloroform (10% w/v) for 4 h. After complete dissolution, a 70% (w/v) solution of ground, sieved sucrose crystals (>250 μ m) was added. The mixture was then cast in silicone molds with cylindrical cavities (7 mm in diameter and 10 mm high) and the solvent was allowed to evaporate overnight at room temperature. Sucrose particles were removed by immersion in a 1% (w/v) aqueous solution of polyvinyl alcohol in order to reduce the surface tension between the polymer and water. Finally, the scaffolds were dried in a vacuum and sliced to form disks ~4 mm high. 2.3.2. Scanning Electron Microscopy (SEM) Morphological analysis of the scaffolds was carried out by scanning electron microscopy (SEM) using a JEOL JXA-840A scanning electron microscope after gold coating (Balzer SCD 050) of the samples. Some samples were immersed in liquid nitrogen and fractured in order to examine the internal structure of the scaffold. 2.3.3. Scanning Differential Calorimetry (DSC) Scanning differential calorimetry (DSC) measurements were carried out on a DSC 2920 thermal analyzer (TA Instruments, USA). Polymeric samples were hermetically sealed in aluminum pans and heated at 200°C to destroy the thermal history of the polymers. Subsequently, the samples were exposed to temperatures ranging from −50°C to 200°C at increments of 10°C min −1 , in an inert nitrogen atmosphere flushed at 5 mL min −1 . 2.3.4. Thermogravimetric Analysis (TGA) The thermal stability of the scaffolds was tested in an STA 409C thermogravimetric analyzer (Netzsch) in which the samples were heated at 10°C min −1 up to 500°C, in an inert argon atmosphere. 2.4. Osteoblast Cell Culture on Scaffolds 2.4.1. Cell Culture Human osteoblast-like SaOS-2 cells were purchased from the Rio de Janeiro Cell Bank (Rio de Janeiro, RJ, Brazil) and cultured in McCoy’s 5A modified medium (CULTILAB, Brazil) containing L-glutamine, HEPES, 15% fetal bovine serum (FBS—CULTILAB, Brazil), 50 mg of getamicin/L (Invitrogen), and 2.5 mg of amphotericin B/L (Invitrogen) in a humidified 95% air/5% CO 2 incubator, at 37°C. The medium was changed every 3-4 days. Cells were detached by treatment with a trypsin/EDTA solution (CULTILAB, Brazil). The scaffolds were sterilized by immersion in 70% ethanol for 1 h and repeatedly washed with deionized water. Before cell culture, sterilized scaffolds were maintained in McCoy’s 5A medium for ~24 h. A cell suspension (1 × 10 4 cells/well in 200 μ L of growth medium) was seeded onto scaffolds of PLDLA-TMC and PLDLA in 96-well plates (TPP, Switzerland) and cultured for 1, 3, 7, and 14 days. Control cells were cultured in wells without scaffolds. The long-term culture clarifies how the scaffolds can sustain the cell proliferation and also allows the observation of the cell differentiation. 2.4.2. MTT Assay To evaluate the mitochondrial activity of the seeded cells, that is, cell viability on the scaffolds during culture, the samples and controls were washed 2-3 times with McCoy’ 5A medium without serum and then incubated with 200 μ L of 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT—Sigma-Aldrich) in McCoy’s medium (0.5 mg mL −1 ). The plates were incubated for 4 h in a cell incubator at 37°C, after which the MTT solution was replaced with 200 μ L of dimethylsulphoxide (DMSO—Sigma-Aldrich). After 10 min, 100 μ L aliquots were transferred to empty wells and the absorbances were measured in a microplate reader (Elx-800-UV, Bio-Tek Instruments) at 570 nm and 650 nm. 2.4.3. ALP Assay Alkaline phosphatase (ALP) produced by SaOS-2 was quantified as an osteoblast marker using an ALP kit (Labtest, Brazil). Briefly, 10 μ L aliquots of culture supernatant were collected and added to 100 μ L of p -nitrophenol phosphate solution (12 mM p -nitrophenol phosphate, 10 mM phenol, and 1.6 mM EDTA buffered to pH 10.4, 0.96 mM zinc sulfate, 2 mM magnesium acetate, and 6.4 mM sodium azide). The reagent was run for 2 min at 37°C and the changes in absorbance were measured in a microplate reader at 415 nm and 650 nm. 3. Results and Discussion 3.1. Physicochemical Characterization of the Synthesized Polymer Poly(L-co-D,L-lactide-co-trimethylene carbonate) was synthesized by bulk polymerization via ring-opening of cyclic dimer monomers at 130°C for 48 h in a vacuum atmosphere. Table 1 shows molar mass of terpolymer measured by GPC. The catalyst used was stannous octoate (Sn(Oct) 2 ) in a monomer/catalyst ratio of 5,000 (w/w). Previous studies demonstrated that this monomer/catalyst ratio produced higher yields and greater molar mass values [ 21 ]. Table 1: Molar mass of terpolymer. Figure 1 shows the 1 H-NMR spectra of PLDLA-TMC. The signals found in the terpolymer 1 H-NRM were practically the same as those for the poly(L-lactide-co-D,L lactide) copolymer and differed at only two points that are characteristic of TMC, that is, δ 2.05 ppm (CH 2 -TMC) and δ 4.24 ppm (OCH 2 -TMC) [ 22 ]. In the copolymer spectrum (data not shown), a multiplet at 5.12–5.24 ppm was assigned to the CH (b) proton, while the quartet at 1.55–1.59 ppm was assigned to the protons CH 3 (a) [ 23 ]. In the case of PLDLA-TMC, the triplet at 2.05 ppm was assigned to the protons CH 2 (c), while the triplet at 4.24 was assigned to OCH 2 (d). Figure 1: 1 H NMR spectra of PLDLA-TMC. The 13 C-NMR spectrum (Figure 2 ) showed lactide units at 16.6 (CH 3 ), 69.0 (CH), and 169.6 (C=O) ppm and TMC units at 27.8 (CH 2 –CH 2 –CH), 61.8–64.7 (CH 2 O), and 154.8 (C=O) ppm. These chemical shifts agreed with the findings of Matsumura et al. [ 24 ] who synthesized low molar mass (21,000 g mol −1 ) lactide/TMC copolymers using a lipase-catalyzed reaction. Figure 2: 13 C NMR spectrum of PLDLA-TMC. Figure 3 represents PLDLA and PLDLA-TMC infrared spectra and shows no difference when TMC is present. The strongest peaks are found at 1181 and 1746 cm −1 corresponding to C–C bonds and carbonyl axial deformation, respectively. Figure 3: FT-IR spectra of PLDLA and PLDLA-TMC. 3.2. Scaffold Construction, Morphology, and Thermal Properties SEM revealed the porous morphology of the scaffold surface (Figures 4(a) and 4(b) ) and interior (Figures 4(c) and 4(d) ). The pores were irregular in shape and consisted of a mixture of large pores (~250–500 μ m in diameter) and small pores (<100 μ m). Inner side of the scaffold is highly porous compared to the scaffold surface (Figures 4(c) and 4(d) ). Scaffold porosity and pore size are important features when evaluating biomaterial properties for tissue engineering [ 25 ]. An adequate pore size allows cell invasion and tissue ingrowth to surround the local implant while maintaining adequate nutrient transfer; however, there is some controversy regarding the best pore that favors new bone formation and growth [ 26 – 28 ]. The porosity and pore structure can be controlled by salt weight, particle size, and polymer fraction [ 25 ]. Figure 4: SEM of PLDLA-TMC scaffolds showing the external (a, b) and inner (c, d) surfaces. Inner views of the scaffolds were obtained after cryofracture. The results for the thermal characterization of the scaffolds are shown in Figures 5 (DSC) and 6 (TGA). None of the polymeric scaffolds showed evidence of crystallinity. PLDLA-TMC was amorphous and DSC thermograms showed a decrease in the glass transition temperature ( ) of PLDLA-TMC (51.7°C) compared to PLDLA (57.9°C) (Figure 5 ). Similar tendencies were observed for the values for poly(L-lactide-co-TMC) and poly(D,L lactide-co-TMC) [ 24 ]. Davachi et al. [ 29 ] showed that an increase in the TMC content of poly(lactide-TMC-glycolide) resulted in a decrease in the glass transition temperature. Since the crystalline phase is poorly accessible to water and other permeants, the presence of crystallinity reduces polymer permeability and the rate of biodegradation by chain scission because of a decrease in accessible hydrolysable bonds. With regard to the use of these polymers for biomedical applications, it is worth remembering that crystalline debris formed during degradation may cause an undesired late inflammatory response, thereby negatively influencing tissue growth and normal function [ 30 ]. Hence, little or no crystallinity is desirable [ 31 ]. Figure 5: DSC thermograms showing the glass transition temperature of PLDLA and PLDLA-TMC scaffolds. Figure 6: TGA thermograms of PLDLA and PLDLA-TMC scaffolds. The thermal stability of PLDLA-TMC was measured with a thermogravimetric analyzer (TGA). Figure 6 shows typical TGA traces of weight loss as a function of temperature. This analysis showed that both polymers decomposed in a single-stage degradation and that the addition of TMC reduced the polymer thermal stability; that is, the addition of TMC to L/D,L-lactide resulted in greater degradation of the polymer. The onset temperature of PLDLA decreased from 333.2°C to 322.6°C when TMC was present. The maximum decomposition temperature of PLDLA was 362.8°C, whereas that of PLDLA-TMC was 342.1°C. 3.3. Osteoblast Cell Culture on Scaffolds The MTT assay showed that the viability of SaOS-2 osteoblasts increased with time (Figure 7 ), an indication of cell proliferation on the porous scaffolds. The presence of TMC in PLDLA did not affect cell viability compared to scaffolds containing only PLDLA. After 1 and 7 days, cells grown on PLDLA and PLDLA-TMC scaffolds showed greater viability than those grown in control wells ( ). After 14 days, only cells grown on PLDLA-TMC scaffolds had greater viability than control cells ( ). SaOS-2 proliferation ceased at 7 days since the viability was similar at 7 and 14 days. Figure 7: Viability of SaOS-2 osteoblasts grown on scaffolds. The values are the mean ± SD ( ). Early osteoblastic differentiation was demonstrated by the ALP activity of SaOS-2 cells (Figure 8 ). There was no significant difference in the ALP activities of PLDLA and PLDLA-TMC scaffolds. The ALP activity increased from days 1 and 3 to days 7 and 14 ( ). Figure 8: Alkaline phosphatase activity of SaOS-2 on scaffolds. Values are expressed as means ± SD, . Stein and Lian [ 32 ] identified two stages of osteoblast differentiation, namely, proliferation during the first 7–14 days and the secretion of extracellular matrix proteins and production of early differentiation markers, such as ALP, from day 7 onwards. ALP belongs to a group of membrane-bound glycoproteins involved in the deposition of minerals on extracellular matrix molecules [ 33 ]. 4. Conclusion Poly(L-co-D,L-lactide-co-trimethylene carbonate) (PLDLA-TMC) was synthetized by ring-opening bulk polymerization of the monomers, using stannous octanoate as catalyst. Thermal analysis showed that the presence of TMC reduced the glass transition temperature and decreased the polymer thermal stability. The scaffolds had a porous morphology that was conducive to cell growth, as shown in the viability and proliferation of SaOS-2 osteoblasts. The detection of alkaline phosphatase activity demonstrated that the cells retained their osteoblast phenotype. Thus, PLDLA-based devices are potentially useful for bone tissue engineering. Conflict of Interests The authors declare that there is no conflict of interests regarding the publication of this paper. Acknowledgments The authors thank FAPESP (Fundação de Amparo à Pesquisa do Estado de São Paulo, Grant no. 2010/15065-7) for financial support and the Scanning Electron Microscopy Laboratory (LabMEV) of the State University of Campinas (UNICAMP) for providing access to their equipment. References J. A. Baddour, K. Sousounis, and P. A. Tsonis, “Organ repair and regeneration: an overview,” Birth Defects Research C: Embryo Today , vol. 96, no. 1, pp. 1–29, 2012. View at Publisher · View at Google Scholar · View at Scopus J. M. Holzwarth and P. X. Ma, “Biomimetic nanofibrous scaffolds for bone tissue engineering,” Biomaterials , vol. 32, no. 36, pp. 9622–9629, 2011. View at Publisher · View at Google Scholar · View at Scopus B. Demirbag, P. Y. Huri, G. T. Kose, A. Buyuksungur, and V. Hasirci, “Advanced cell therapies with and without scaffolds,” Biotechnology Journal , vol. 6, no. 12, pp. 1437–1453, 2011. View at Publisher · View at Google Scholar · View at Scopus A. C. Motta and E. A. R. Duek, “Synthesis, characterization and “in vitro” degradation of PLLA,” Polímeros , vol. 16, no. 1, pp. 26–32, 2006. View at Publisher · View at Google Scholar L. S. Nair and C. T. Laurencin, “Polymers as biomaterials for tissue engineering and controlled drug delivery,” Advances in Biochemical Engineering/Biotechnology , vol. 102, pp. 47–90, 2006. View at Publisher · View at Google Scholar D. J. Darensbourg, W. Choi, O. Karroonnirun, and N. Bhuvanesh, “Ring-opening polymerization of cyclic monomers by complexes derived from biocompatible metals. Production of poly(lactide), poly(trimethylene carbonate), and their copolymers,” Macromolecules , vol. 41, no. 10, pp. 3493–3502, 2008. View at Publisher · View at Google Scholar · View at Scopus B. Buchholz, “Analysis and characterization of resorbable DL-lactide-trimethylene carbonate copolyesters,” Journal of Materials Science: Materials in Medicine , vol. 4, no. 4, pp. 381–388, 1993. View at Publisher · View at Google Scholar · View at Scopus U. A. Stock and J. P. Vacanti, “Tissue engineering: current state and prospects,” Annual Review of Medicine , vol. 52, pp. 443–451, 2001. View at Publisher · View at Google Scholar · View at Scopus Y. Wang, G. A. Ameer, B. J. Sheppard, and R. Langer, “A tough biodegradable elastomer,” Nature Biotechnology , vol. 20, no. 6, pp. 602–606, 2002. View at Publisher · View at Google Scholar · View at Scopus I. Engelberg and J. Kohn, “Physico-mechanical properties of degradable polymers used in medical applications: a comparative study,” Biomaterials , vol. 12, no. 3, pp. 292–304, 1991. View at Publisher · View at Google Scholar · View at Scopus D. W. Grijpma, R. D. A. van Hofslot, H. Supèr, A. J. Nijenhuis, and A. J. Pennings, “Rubber toughening of poly(lactide) by blending and block copolymerization,” Polymer Engineering and Science , vol. 34, no. 22, pp. 1674–1684, 1994. View at Publisher · View at Google Scholar · View at Scopus E. Ruckenstein and Y. Yuan, “Molten ring-open copolymerization of L-lactide and cyclic trimethylene carbonate,” Journal of Applied Polymer Science , vol. 69, no. 7, pp. 1429–1434, 1998. View at Scopus A. R. Katz, D. P. Mukherjee, A. L. Kaganov, and S. Gordon, “A new synthetic monofilament absorbable suture made from polytrimethylene carbonate,” Surgery, Gynecology & Obstetrics , vol. 161, no. 3, pp. 213–222, 1985. View at Scopus T. Garg, O. Singh, S. Arora, and R. S. R. Murthy, “Scaffold: a novel carrier for cell and drug delivery,” Critical Reviews in Therapeutic Drug Carrier Systems , vol. 29, no. 1, pp. 1–63, 2012. View at Scopus J. D. Kretlow, L. Klouda, and A. G. Mikos, “Injectable matrices and scaffolds for drug delivery in tissue engineering,” Advanced Drug Delivery Reviews , vol. 59, no. 4-5, pp. 263–273, 2007. View at Publisher · View at Google Scholar · View at Scopus A. Yousefi, C. Gauvin, L. Sun, R. W. DiRaddo, and J. Fernandas, “Design and fabrication of 3D-plotted polymeric scaffolds in functional tissue engineering,” Polymer Engineering and Science , vol. 47, no. 5, pp. 608–618, 2007. View at Publisher · View at Google Scholar · View at Scopus E. Chevalier, D. Chulia, C. Pouget, and M. Viana, “Fabrication of porous substrates: a review of processes using pore forming agents in the biomaterial field,” Journal of Pharmaceutical Sciences , vol. 97, no. 3, pp. 1135–1154, 2008. View at Publisher · View at Google Scholar · View at Scopus P. K. D. V. Yarlagadda, M. Chandrasekharan, and J. Y. M. Shyan, “Recent advances and current developments in tissue scaffolding,” Bio-Medical Materials and Engineering , vol. 15, no. 3, pp. 159–177, 2005. View at Scopus S. H. Barbanti, A. R. Santos Jr., C. A. C. Zavaglia, and E. A. R. Duek, “Porous and dense poly(L-lactic acid) and poly(D,L-lactic acid-co-glycolic acid) scaffolds: in vitro degradation in culture medium and osteoblasts culture,” Journal of Materials Science: Materials in Medicine , vol. 15, no. 12, pp. 1315–1321, 2004. View at Publisher · View at Google Scholar · View at Scopus S. H. Barbanti, A. R. Santos Jr., C. A. C. Zavaglia, and E. A. R. Duek, “Poly( ε -caprolactone) and poly(D,L-lactic acid-co-glycolic acid) scaffolds used in bone tissue engineering prepared by melt compression-particulate leaching method,” Journal of Materials Science: Materials in Medicine , vol. 22, no. 10, pp. 2377–2385, 2011. View at Publisher · View at Google Scholar · View at Scopus A. C. Motta and E. A. R. Duek, “Synthesis and characterization of the copolymer poly (L-co-D,L lactic acid),” Polímero , vol. 17, no. 2, pp. 123–129, 2007. View at Publisher · View at Google Scholar D. Pospiech, H. Komber, D. Jehnichen et al., “Multiblock copolymers of L-lactide and trimethylene carbonate,” Biomacromolecules , vol. 6, no. 1, pp. 439–446, 2005. View at Publisher · View at Google Scholar · View at Scopus K. A. M. Thakur, R. T. Kean, E. S. Hall, M. A. Doscotch, and E. J. Munson, “A quantitative method for determination of lactide composition in poly(lactide) using 1 H NMR,” Analytical Chemistry , vol. 69, no. 21, pp. 4303–4309, 1997. View at Publisher · View at Google Scholar · View at Scopus S. Matsumura, K. Tsukada, and K. Toshima, “Novel lipase-catalyzed ring-opening copolymerization of lactide and trimethylene carbonate forming poly(ester carbonate)s,” International Journal of Biological Macromolecules , vol. 25, no. 1–3, pp. 161–167, 1999. View at Publisher · View at Google Scholar · View at Scopus X. Zhao, X. Li, Y. Kang, and Q. Yuan, “Improved biocompatibility of novel poly(L-lactic acid)/ β -tricalcium phosphate scaffolds prepared by an organic solvent-free method,” International Journal of Nanomedicine , vol. 6, pp. 1385–1390, 2011. View at Scopus O. Gauthier, J. Bouler, E. Aguado, P. Pilet, and G. Daculsi, “Macroporous biphasic calcium phosphate ceramics: influence of macropore diameter and macroporosity percentage on bone ingrowth,” Biomaterials , vol. 19, no. 1–3, pp. 133–139, 1998. View at Publisher · View at Google Scholar · View at Scopus K. A. Hing, S. M. Best, and W. Bonfield, “Characterization of porous hydroxyapatite,” Journal of Materials Science: Materials in Medicine , vol. 10, no. 3, pp. 135–145, 1999. View at Publisher · View at Google Scholar · View at Scopus A. G. Mikos, G. Sarakinos, M. D. Lyman, D. E. Ingber, J. P. Vacanti, and R. Langer, “Prevascularization of porous biodegradable polymers,” Biotechnology and Bioengineering , vol. 42, no. 6, pp. 716–723, 1993. View at Publisher · View at Google Scholar · View at Scopus S. M. Davachi, B. Kaffashi, J. M. Roushandeh, and B. Torabinejad, “Investigating thermal degradation, crystallization and surface behavior of l-lactide, glycolide and trimethylene carbonate terpolymers used for medical applications,” Materials Science and Engineering C , vol. 32, no. 2, pp. 98–104, 2012. View at Publisher · View at Google Scholar · View at Scopus R. R. M. Bos, F. B. Rozema, G. Boering et al., “Degradation of and tissue reaction to biodegradable poly(L-lactide) for use as internal fixation of fractures: a study in rats,” Biomaterials , vol. 12, no. 1, pp. 32–36, 1991. View at Publisher · View at Google Scholar · View at Scopus A. P. Pêgo, A. A. Poot, D. W. Grijpma, and J. Feijen, “Physical properties of high molecular weight 1,3-trimethylene carbonate and D,L-lactide copolymers,” Journal of Materials Science: Materials in Medicine , vol. 14, no. 9, pp. 767–773, 2003. View at Publisher · View at Google Scholar · View at Scopus G. S. Stein and J. B. Lian, “Molecular mechanisms mediating proliferation/differentiation interrelationships during progressive development of the osteoblast phenotype,” Endocrine Reviews , vol. 14, no. 4, pp. 424–442, 1993. View at Publisher · View at Google Scholar · View at Scopus A. Polini, D. Pisignano, M. Parodi, R. Quarto, and S. Scaglione, “Osteoinduction of human mesenchymal stem cells by bioactive composite scaffolds without supplemental osteogenic growth factors,” PLoS ONE , vol. 6, no. 10, Article ID e26211, 2011. View at Publisher · View at Google Scholar · View at Scopus var _gaq = _gaq || []; _gaq.push(['_setAccount', 'UA-8578054-2']); _gaq.push(['_trackPageview']); (function () { var ga = document.createElement('script'); ga.type = 'text/javascript'; ga.async = true; ga.src = ('https:' == document.location.protocol ? 'https://ssl' : 'http://www') + '.google-analytics.com/ga.js'; var s = document.getElementsByTagName('script')[0]; s.parentNode.insertBefore(ga, s); })();

Journal

International Journal of BiomaterialsHindawi Publishing Corporation

Published: Jun 25, 2014

There are no references for this article.